Abstract:With excellent specific strength, specific modulus and service performance at high temperature, TiAl-based alloys have become the key material for the update of aerospace engineering. However, the coarse as-cast grain size, low room temperature plasticity and strength limit their further engineering application. In this paper, the Ti-48Al-2Cr-2Nb ingot alloyed with TiB2 and Ni was prepared by the induction melting, and the effects of TiB2 and Ni on the solidification microstructure and mechanical properties were studied. The results show that the addition of TiB2 and Ni exhibits little influence on the solidification path and primary phase. The grain size is refined from 700 mu m to 100 mu m, and the flake TiB2 and Ni-riched tau(3) phase is determined. The nanohardness of tau(3) phase is detected as 8.3 GPa, which is significantly higher than that of lamellar colony and bulk gamma phase. Tensile strength of T4822-(Ni,TiB2) alloy is similar to that of the matrix alloy, and the fracture elongation is increased by 30% at room temperature. At 700 similar to 900 degrees C, T4822-(Ni,TiB2) alloy shows the preferable tensile strength, and the tensile strength at 900. reaches 365 MPa, 9% higher than that of the matrix alloy. At 800 and 900 degrees C, the breaking elongation reaches 25.3% and 36.1%, respectively, much higher than that of the matrix alloy. The refinement of grain size and the massive gamma phase at grain boundary are the main reasons for the plasticity improvement of T4822-(Ni,TiB2) alloy. And the good high temperature strength can be attributed to the hard borides and Ni-rich tau(3) phase inside and at the interface of lamellar masses.

Structure of TiAl Based Alloy by Suction Casting

Permanent Mold Suction Casting for Tial Based Alloys

Permanent Mold bottom pouring suction casting for γ-TiAl based alloys

Effect of Ti on Microstructure and Mechanical Properties of Die-Cast Al-Mg-Zn-Si Alloy

Effect of Heat Treatment on Microstructure of TiAl Based Alloy Casting by Suction Casting Process

Study on Vacuum Suction Casting for TiAl-Based Alloys

Simultaneously Improved the Strength and Ductility of Cast Al-3Li-2Cu Alloy by Ti Addition and Heat Treatment

Effect of Al Contents on the As-cast Microstructure Evolution of TiAl Binary Alloys

Novel Casting TiAl Alloy with Fine Microstructure and Excellent Performance Assisted by Ultrasonic Melt Treatment

Optimization of the Microstructure and Mechanical Properties of a Laves Phase-Strengthened Hypoeutectic NiAl/Cr(Mo,W) Alloy by Suction Casting

Microstructure Evolution and Mechanical Properties' Improvement of NiAl–Cr(Mo)–Hf Eutectic Alloy During Suction Casting and Subsequent HIP Treatment

Promoting Strengthening and Grain Refinement of Aluminum Alloy During Wire and Arc Additive Manufacturing by Adding TiB2 Particles

Study on the Fabrication of Porous TiAl Alloy Via Non-Aqueous Gel Casting of a TiH2 and Al Powder Mixture

Effect of Ti content on microstructures and mechanical properties of cast Al-2Li-2Cu-0.5Mg alloy

As-cast Structure Refinement of Ti-46Al Alloy by Hafnium and Boron Additions

A Preliminary Research on the Mechanical Properties of TiAl+Ti5Si3 Dual Phase Alloys

Solidification Microstructure Evolution and Mechanical Properties of Casting Ti-48Al-2Cr-2Nb-(Ni,TiB2)Alloy

Relationship Between Microstructures and Mechanical Properties of Ti-6Al-4V Alloy in Centrifugal Casting

Effect of Al Addition on Phase Purity of Ti3Si(Al)C2 Synthesized by Mechanical Alloying

Microstructures and Properties of Porous TiAl-based Intermetallics Prepared by Freeze-Casting

Synthesis and Properties of an Ultrafine Grained Ti-45al-2cr-2nb-1b-0.5ta Alloy Prepared by Double Mechanical Milling and Spark Plasma Sintering