Ni Ion Release, Osteoblast-Material Interactions, and Hemocompatibility of Hafnium-Implanted Niti Alloy

Tingting Zhao,Yan Li,Xinqing Zhao,Hong Chen,Tao Zhang

DOI: https://doi.org/10.1002/jbm.b.31989

2011-01-01

Abstract:Hafnium ion implantation was applied to NiTi alloy to suppress Ni ion release and enhance osteoblastmaterial interactions and hemocompatibility. The auger electron spectroscopy, x-ray photoelectron spectroscopy, and atomic force microscope results showed that a composite TiO2/HfO2 nanofilm with increased surface roughness was formed on the surface of NiTi, and Ni concentration was reduced in the superficial surface layer. Potentiodynamic polarization tests displayed that 4 mA NiTi sample possessed the highest Ebr - Ecorr, 470 mV higher than that of untreated NiTi, suggesting a significant improvement on pitting corrosion resistance. Inductively coupled plasma mass spectrometry tests during 60 days immersion demonstrated that Ni ion release rate was remarkably decreased, for example, a reduction of 67% in the first day. The water contact angle increased and surface energy decreased after Hf implantation. Cell culture and methyl-thiazol-tetrazolium indicated that Hf-implanted NiTi expressed enhanced osteoblasts adhesion and proliferation, especially after 7 days culture. Hf implantation decreased fibrinogen adsorption, but had almost no effect on albumin adsorption. Platelets adhesion and activation were suppressed significantly (97% for 4 mA NiTi) and hemolysis rate was decreased by at least 57% after Hf implantation. Modified surface composition and morphology and decreased surface energy should be responsible for the improvement of cytocompatibility and hemocompatibility. (c) 2011 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 2012.