Photoelectrical and Charge Transfer Properties of Hydrogen-Evolving TiO2 Nanotube Arrays Electrodes Annealed in Different Gases
L. X. Sang,Z. Y. Zhang,C. F. Ma
DOI: https://doi.org/10.1016/j.ijhydene.2011.01.071
IF: 7.2
2011-01-01
International Journal of Hydrogen Energy
Abstract:TiO2 nanotube arrays were fabricated by sonoelectrochemical anodic oxidation and calcined in nitrogen, air, or 5% hydrogen/nitrogen which was denoted as TNT-A, TNT-N, and TNT-H, respectively. All annealed TiO2 nanotube arrays samples exhibited similar surface morphology. With UV illumination (365 +/- 15 nm), the photocurrent density of the TNT-A, TNT-N and TNT-H was about 0.27 mA/cm(2), 0.45 mA/cm(2) and 0.60 mA/cm(2), respectively. The trapped electron at the Ti4+ center of TiO2 nanotube arrays shows absorption at around 500-700 nm. From the XPS measurement, it was found that annealing in 5% hydrogen/nitrogen helped the sample obtain a greater defect density. Because of the reduction of Ti4+ and the formation of oxygen vacancies, the charge transfer resistance appeared in this order: TNT-A > TNT-N > TNT-H. Thus TNT-H harvested the greatest charge carrier density of 9.86 x 10(20) cm(-3), TNT-N and TNT-A obtained a charge carrier density of 1.38 x 10(20) cm(-3) and 1.06 x 10(20) cm(-3), respectively. Accordingly, the hydrogen production rate by water splitting over TNT-A, TNT-N and TNT-H (320-780 nm irradiation, 3 h) was about 120 mu L/h cm(2), 159 mu L/h cm(2) and 231 mu L/h cm(2), respectively. Copyright (C) 2011, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.