Synthesis of SnO2 Nanorods and Hollow Spheres and Their Electrochemical Properties As Anode Materials for Lithium Ion Batteries

L. Tan,M. S. Wang,Y. J. Liu,X. C. Xiao,L. -Z. Fan,Y. D. Wang

DOI: https://doi.org/10.1179/1753555712y.0000000001

2012-01-01

Materials Technology

Abstract:SnO2 nanorods and hollow spheres were conducted via a surfactant assisted hydrothermal reaction with the hydrothermal temperature. The crystalline structure and morphologies of the as prepared samples were characterised by X-ray diffraction, scanning electron microscopy, and transmission electron microscopy. The results indicate that the products are hollow spheres with diameters of approximately 400-800 nm and shell thicknesses of 60-70 nm via hydrothermal treating at 160 degrees C for 42 h and rod-like nanostructures with diameters of similar to 30 nm and lengths of 100-300 nm via hydrothermal treating at 200 degrees C for 42 h respectively. The as prepared samples were used as anode materials for lithium ion battery, whose charge-discharge properties and cycle performance were examined. The results show that the initial discharge capacities of SnO2 hollow spheres and SnO2 nanorods samples are 1303 and 1426 mA h g(-1) at 0.2C rate, and still retain charge capacities of 518 and 578 mA h g(-1) respectively. Its good cycling behaviour and charge capacities make it a promising cathode material for advanced electrochemical devices for lithium ion batteries.