Abstract:Calcium looping cycle for post-combustion CO2 capture has gained increasing attention worldwide. However, CaO-based sorbents derived from natural sources for calcium looping cycle experience rapid loss of capacity during high-temperature cyclic carbonation/calcination reactions. Synthesizing sintering-resistant CaO-based sorbents by adding a support material has been extensively studied as an effective method of combating the problem. The support material in the synthetic sorbents plays an important role in retaining the capacity, and various support materials have been tested in the literature. In practical reactors, sulfur is present and it has been reported that sulfation of sorbents will also reduce the CO2 capture capacity. However, thus far, it is not clear whether/how support material would affect sulfation of sorbents and, thus, CO2 capture. In this paper, four different support materials, such as Ca2MnO4, La2O3, Ca12Al14O33, and MgO, were studied. The cyclic CO2 capture performance of the synthetic sorbents made from CaO and the support materials were investigated in detail, in the presence of SO2 and steam. The results showed that a mass ratio of 20-25% support material would be optimum for synthesizing sorbents with high cyclic CO2 capture capacity, and Ca12Al14O33 and MgO seem to be more effective than Ca2MnO4 and La2O3. The 80:20 wt % CaO/MgO synthetic sorbent achieved the highest CO2 capture capacity under ideal conditions over 100 cycles. However, the CaO/MgO sorbent had a strong affinity to SO2 capture during cyclic reactions, especially in the presence of steam. Under realistic conditions (i.e., both SO2 and steam are present during carbonation), the CaO/MgO sorbent showed the highest cumulative SO2 capture capacity, whereas the CaO/Ca12Al14O33 sorbent obtained the highest CO2 capture capacity after 10 cycles. The smaller average crystallite size of MgO in the sorbent was responsible for the strong SO2 affinity of the CaO/MgO sorbent as well as its stable cyclic CO2 capture abilities under ideal conditions.

Calcium Looping Technology Using Improved Stability Nanostructured Sorbent For Cyclic Co2 Capture

Mechanism for self-reactivation of nano-CaO-based CO 2 sorbent in calcium looping

Synthesis of a Porous Nano‐CaO/MgO‐Based CO2 Adsorbent

Different Sorbents in Calcium Looping Cycle for CO2 Capture

Development and performance of CaO/La2O3 sorbents during calcium looping cycles for CO2 capture

Review on the development of sorbents for calcium looping

Morphological Changes of Pure Micro‐ and Nano‐Sized CaCO3 during a Calcium Looping Cycle for CO2 Capture

Synthesis and Performance of a Nano Synthetic Ca-based Sorbent for High Temperature CO2 Capture

Effect of Doped Lanthanum and Aluminum Salts on Calcium Looping Cycle for CO2 Capture

Reactivation of calcium-based sorbent by water hydration for CO2 capture

A green and scalable synthesis of highly stable Ca-based sorbents for CO2 capture

Cyclic Performance Of Waste-Derived Sio2 Stabilized, Cao-Based Sorbents For Fast Co2 Capture

Degradation Study of a Novel Polymorphic Sorbent under Realistic Post-Combustion Conditions

Comparative investigation on CO2 uptake performance of limestone-derived sorbents with different supports synthesized by impregnated layer solution combustion method

Effect of Support Material on Carbonation and Sulfation of Synthetic Cao-Based Sorbents in Calcium Looping Cycle

Improved performance of modified CaO-Al2O3 based pellets for CO2 capture under realistic Ca-looping conditions

Studies on CO2 uptake by CaO/Ca3Al2O6 sorbent in calcium looping cycles

New insights into stabilizing mechanism of Ca9Al6O18 stabilizing Ca-based sorbents for CO2 cyclic capture under mild conditions

Application of the sol-gel technique to develop synthetic calcium-based sorbents with excellent carbon dioxide capture characteristics.

Progress in reducing calcination reaction temperature of Calcium-Looping CO2 capture technology: A critical review

Enhanced cyclic stability of CO 2 adsorption capacity of CaO-based sorbents using La 2 O 3 or Ca 12 Al 14 O 33 as additives