Abstract:A precursor CuO/ZnO/Al2O3 catalyst for methanol synthesis has been prepared at room temperature by introducing a ternary salt solution into the excess of sodium carbonate solution following the reverse co-precipitation method. The catalyst was tested for the synthesis of methanol from synthesis gas. The composition (vol. %) has been presented: CO, 22; CO2, 5.8; N2, 5.5; H2, balance. The methanol productivity was recorded to be 2.7 kg kgcat–1 h–1 at a temperature of 260 °С, a pressure of 3 MPa, and a space velocity of 61,700 l (kgcat)–1 h–1. The possibility of regenerating the activity of a catalyst subjected to conditions of artificial aging (overheating in a syngas environment) has been tested: approximately 92% of the initial activity could be restored. Physicochemical studies were conducted using the thermogravimetric analysis (TGA), Fourier-transform infrared spectroscopy (FTIR), the scanning electron microscopy (SEM), and the X-ray diffraction (XRD) techniques using the Cu, Zn, and Al oxides obtained following the co-precipitation method. X-ray studies revealed that an amorphous phase was obtained from the Al oxide that was synthesized following both the direct and reverse co-precipitation methods. The calcination temperature was 300 °C. Individual oxides of Cu and Zn obtained following the reverse co-precipitation method form crystalline phases when calcined at 300 °C. When all three ingredients are present, calcination of the sample at 300 °C helps obtain an X-ray amorphous structure of the catalyst characterized by a high specific surface area. High-temperature carbonates are formed from samples prepared using a ternary mixture of nitrate salts when these are calcined at 300 °C.

Preparation of Supported Noble Metal Catalyst for Methanol Catalytic Combustion at Room Temperature

Methanol Synthesis from CO 2 and H 2 over Pd/ZnO/Al 2 O 3 : Catalyst Structure Dependence of Methanol Selectivity

Preparation and Properties of Supported Platinum Catalyst for Methanol Catalytic Combustion at Room Temperature

Preparation of Pt/Al2O3 catalyst and its performance on methanol catalytic combustion at low temperature

In Situ Growth of Tungsten Oxide on Alumina to Boost the Catalytic Performance of Platinum for Glycerol Hydrogenolysis

Impact of Preparation Methods on the Performance of Cu/Ni/Zr Catalysts for Methanol Decomposition

Effective Cu/ZnO/Al2O3 Catalyst for Methanol Production: Synthesis, Activation, Catalytic Performance, and Regeneration

Hydrogen-Ignited-Methanol Catalytic Co-Combustion of Aromatic Volatile Organic Compounds over PdPt/Al2O3 Bimetallic Catalyst

A New Supported Catalyst for Methanol Oxidation Prepared by a Reverse Micelles Method

Combustion of Methane and Carbon Monoxide over Alumina-Supported Catalysts for the Purpose of the Synthesis Gas Combustion

Preparation of Ordered Mesoporous Tio2 Thin Film and Its Application in Methanol Catalytic Combustion

Methanol Decomposition to Synthesis Gas over Supported Platinum-Containing Catalysts

Methane Combustion over the Porous Oxides and Supported Noble Metal Catalysts

Short Communication: Pt Thin Film Catalyst Preparation for Methanol Combustion at Room Temperature

A Photo-Reduction Method for Enhancing Catalytic Activity of Pt-Loaded Ordered Mesoporous TiO2 Film Catalyst in Methanol Combustion at Low Temperature

Supported platinum–zinc oxide core–shell nanoparticle catalysts for methanol steam reforming

Alcohol Solvent Assisted Synthesis of Metallic and Metal Oxide Catalysts: As-Prepared Cu/ZnO/Al 2 O 3 Catalysts for Low-Temperature Methanol Synthesis with an Ultrahigh Yield

Preparation of Highly Dispersed Supported Ni-Based Catalysts and Their Catalytic Performance in Low Temperature for CO Methanation

Mn-promoted Ag Supported on Pure Siliceous Beta Zeolite (Ag/beta-Si) for Catalytic Combustion of Formaldehyde

A High Activity Cu/ZnO/Al2O3 Catalyst for Methanol Synthesis: Preparation and Catalytic Properties

Carbon-Supported Pt and Ptru Nanoparticles As Catalysts for A Direct Methanol Fuel Cell