Abstract:A hydrophilic N,S-codoped hierarchically porous carbon (NSHPC) was fabricated successfully through a green route, which is through activation of bagasse with thiourea using calcium chloride as activation agent by a one-step process. The as-prepared N,S-codoped carbon with hierarchically porosities can offer merits for ion buffering and storage, and moreover, the doped nitrogen and sulfur in this sample can significantly enhance the hydrophilicity/wettability and pseudocapacitance. Thus, the as-prepared NSHPC material with a moderated specific surface area (SSA, 835.9 m(2) g(-1)) and pore volume (0.68 cm(3) CI), achieving from calcination the raw sources of bagasse, CaCl2, and thiourea in a mass ratio of 1:2:2 at 800 degrees C for 2 h under an inert flow, can exhibit a high mass specific capacitance and areal-normalized capacitance (349.0/41.6, 282.5/33.8, and 203.8/24.3 F g(-1)/mu F cm(-2) at 1.0 A g(-1) in 6.0 M KOH, 1.0 M H2SO4, and Li2SO4, respectively), superior rate performance (222.0, 152.0, and 98.8 F g(-1) at 100 A g(-1) in 6.0 M KOH, 1.0 M H2SO4 and Li2SO4, respectively), and outstanding cycle stability. Moreover, a symmetric capacitor fabricated by the NSHPC material shows high energy and good power densities (with respective 21.7 and 14.4 Wh kg(-1) at 0.4 and 4.0 kW kg(-1)) in 1.0 M Li2SO4 electrolyte. Also, this as-assembled device displays excellent cycle performance (with no capacitance fading after 10 000 cycles at 10.0 A g(-1)). Compared with the electrochemical performance of the as-prepared NSHPC sample and the previously synthesized N-doped porous carbon and activation carbon with similar SSA and pore volume, it is suggested that the S-doping in the NSHPC sample plays a positive role in enhancing its rate performance for supercapacitors originated from its incremental hydrophilicity and rich heteroatom content.

N, S co-doped porous carbon with high capacitive performance derived from heteroatom doped phenolic resin

Capacitance performance of N/O co-doped hierarchical porous carbon nanosheets synthesized via "one stone for three birds" strategy

Understanding of the effect of nitrogen-doping level and micropore volume ratio on the capacitive performance of N,S-codoped hierarchically porous carbon

Cooking Carbon with Protic Salt: Nitrogen and Sulfur Self-Doped Porous Carbon Nanosheets for Supercapacitors

Polymerization-Pyrolysis-Derived Hierarchical Nitrogen-Doped Porous Carbon for Energetic Capacitive Energy Storage

Boosting supercapacitor performance through the facile synthesis of boron and nitrogen co-doped resin-derived carbon electrode material

Boron and Nitrogen Co‐Doped Trimodal‐Porous Wood‐Derived Carbon for Boosting Capacitive Performance

One pot synthesis of nitrogen-doped hierarchical porous carbon derived from phenolic formaldehyde resin with sodium citrate as activation agent for supercapacitors

One-step Carbonization of Poly(styrene/divinylbenzene) to Fabricate N-doped Porous Carbon for High-Performance Supercapacitor Electrode

N, O co-doped porous carbon with rich pseudocapacitive groups exhibiting superior energy density in an acidic 2.4 V Li2SO4 electrolyte

Rational construction of hierarchical porous carbon with ultrahigh specific surface area and rich heteroatoms toward high-performance supercapacitors

Capacitive Performance of Nitrogen-Doped Hierarchical Porous Carbon Easily Synthesized with Double Metal Organic Salt

Design and Synthesis of Highly N, S Co-Doped 3D Carbon Materials with Tunable Porosity for Supercapacitors

Heteroatom-Doped Porous Carbon Materials with Unprecedented High Volumetric Capacitive Performance.

Boosting the capacitive performance by constructing O, N co-doped hierarchical porous structure in carbon for supercapacitor

Pseudocapacitive porous hard carbon anode with controllable pyridinic nitrogen and thiophene sulfur co-doping for high-power dual-carbon sodium ion hybrid capacitors

N/O co-doped porous carbon synthesized by lewis acid salt activation for high rate performance supercapacitor

Thiocyanogen-modulated N, S Co-doped lignin hierarchical porous carbons for high-performance aqueous supercapacitors

Preparation of Porous Doped Carbons and the High Performance in Electrochemical Capacitors

Understanding the Roles of Sulfur Doping for Enhancing of Hydrophilicity and Electrochemical Performance of N,S-Codoped Hierarchically Porous Carbon

Facile Synthesis of Nitrogen-Doped Carbon Materials with Hierarchical Porous Structures for High-Performance Supercapacitors in Both Acid and Alkaline Electrolytes