Magnetic and impedance properties of nanocomposite CoFe2 O 4/ Co0.7 Fe0.3 and single-phase CoFe 2 O4 prepared via a one-step hydrothermal synthesis
Fenlian Zan,Yongqing Ma,Qian Ma,Yuanfeng Xu,Zhenxiang Dai,Ganhong Zheng,Mingzai Wu,Guang Li
DOI: https://doi.org/10.1111/jace.12437
IF: 4.186
2013-01-01
Journal of the American Ceramic Society
Abstract:Using a one-step hydrothermal method and at different stirring speeds (V-s), we have synthesized different types of CoFe2O4-based magnetic nanocrystalline samples. With increasing V-s, the sample changes from a nanocomposite of CoFe2O4/Co0.7Fe0.3 (CFO/CF) to single-phase CoFe2O4 (CFO). The maximum magnetization, 88.9emu/g, and coercivity, 3010Oe, were obtained when V-s=0. As V-s increases, the saturation magnetization M-s decreases, because the amount of soft magnetic CF phase decreases. A clear enhancement in the remanence, M-r, was observed, with the maximum M-r/M-s=0.67; the coercivity H-c also exhibits a local maximum for the sample with V-s=200r/min. These trends can be explained well by the interplay between dipolar interaction, magnetocrystalline anisotropy, and shape anisotropy. The stirring speed also influences the impedance of the materials; the related mechanism is discussed.