Abstract:Polyurethane materials with gradient structure are prepared using reaction injection method, achieving continuous changes in hard segment content along the length direction. The gradient material extends the effective damping temperature range (TR) from 40.7°C (−32.3 ~ 8.4°C) for component A and 66.6°C (59.5 ~ 126.1°C) for component B to 139.5°C (−20.6 ~ 118.9°C). Furthermore, due to the elimination of interface effects, the tensile strength of the material do not significantly decrease. Polyurethane is the main matrix material of polymer damping materials, but the damping temperature range is narrow, the effective damping temperature range does not match the working temperature of the material, and the elastic modulus is sensitive to temperature during glass transition, which is not conducive to safe use in a wide temperature range. In this paper, the polyurethane gradient material with the hard segment content continuously changing along the length direction was designed and prepared by the reaction injection method. Dynamic mechanical analysis (DMA) shows that the gradient structure greatly influences the comprehensive damping performance of polyurethane. While maintaining no significant decrease in mechanical properties, the gradient material extends the effective damping temperature range (TR) from 40.7°C (−32.3 ~ 8.4°C) for component A and 66.6°C (59.5 ~ 126.1°C) for component B to 139.5°C (−20.6 ~ 118.9°C). At the same time, the damping peak remains high (0.48), which is close to the higher damping peak of the B component of 0.56. The elastic modulus (E′) decreases slowly with the increase in temperature, which can better ensure the safety of the material.

A Novel Approach to Prepare a Gradient Polymer with a Wide Damping Temperature Range by In‐Situ Chemical Modification of Rubber During Vulcanization

Preparation of Gradient Polymer with Wide Damping Temperature Range by In-situ Sulfur Modification

Polybutadiene Vitrimers with Tunable Epoxy Ratios: Preparation and Properties

Sulfur Diffusion Studies Imitating Recycled Ground-Rubber-Containing Compounds

Vulcanization Kinetics of Natural Rubber and Strain Softening Behaviors of Gum Vulcanizates Tailored by Deep Eutectic Solvents

The facile and effective approach for fabricating polyurethane gradient materials with significant damping properties

Co-vulcanization of natural rubber and Eucommia ulmoides gum for mediation of the nonlinear rheology behaviors

Rubber Compounds from Devulcanized Ground Tire Rubber: Recipe Formulation and Characterization

On the Fundamental Polymer Chemistry of Inverse Vulcanization for Statistical and Segmented Copolymers from Elemental Sulfur.

Regulating Vulcanization Kinetics with Deep Eutectic Solvents for Developing Greener Processing Technology of Thermoplastic Vulcanizates

Dual functions of inverse vulcanized copolymers as both vulcanizator and interfacial modifier for improving the mechanical properties of silica reinforced rubber composites

Stretchable and Durable Inverse Vulcanized Polymers with Chemical and Thermal Recycling

Preparation and Damping Mechanism of Polymer Blends with Broad Damping Temperature Range Damping Elastomer Based on Inter-Phase Cross-Linkages

A Facile One-Pot Route to Elastomeric Vitrimers with Tunable Mechanical Performance and Superior Creep Resistance

Vulcanization of polypropylene

Preparation of an Elastomer with Broad Damping Temperature Range Based on EPDM/ENR Blend

Use of Gradient Laminating to Prepare NR/ENR Composites with Excellent Damping Performance

Mechanochemical synthesis of inverse vulcanized polymers

Effect of Deep Eutectic Solvents on Vulcanization Kinetics and Strain-Softening Behavior of Natural Rubber/styrene-Butadiene Rubber

Skeletal Network Enabling New-Generation Thermoplastic Vulcanizates

A Study on the Preparation of a Vulcanizing Mixture and Its Application in Natural Rubber Latex