The facile and effective approach for fabricating polyurethane gradient materials with significant damping properties
Fangling Wang,Yuewang Zhu,Liuye Wang,Kai Ren,Juan Li,Chengzhong Wang,Shengling Jiang
DOI: https://doi.org/10.1002/app.54708
IF: 3
2023-10-05
Journal of Applied Polymer Science
Abstract:Polyurethane materials with gradient structure are prepared using reaction injection method, achieving continuous changes in hard segment content along the length direction. The gradient material extends the effective damping temperature range (TR) from 40.7°C (−32.3 ~ 8.4°C) for component A and 66.6°C (59.5 ~ 126.1°C) for component B to 139.5°C (−20.6 ~ 118.9°C). Furthermore, due to the elimination of interface effects, the tensile strength of the material do not significantly decrease. Polyurethane is the main matrix material of polymer damping materials, but the damping temperature range is narrow, the effective damping temperature range does not match the working temperature of the material, and the elastic modulus is sensitive to temperature during glass transition, which is not conducive to safe use in a wide temperature range. In this paper, the polyurethane gradient material with the hard segment content continuously changing along the length direction was designed and prepared by the reaction injection method. Dynamic mechanical analysis (DMA) shows that the gradient structure greatly influences the comprehensive damping performance of polyurethane. While maintaining no significant decrease in mechanical properties, the gradient material extends the effective damping temperature range (TR) from 40.7°C (−32.3 ~ 8.4°C) for component A and 66.6°C (59.5 ~ 126.1°C) for component B to 139.5°C (−20.6 ~ 118.9°C). At the same time, the damping peak remains high (0.48), which is close to the higher damping peak of the B component of 0.56. The elastic modulus (E′) decreases slowly with the increase in temperature, which can better ensure the safety of the material.
polymer science