Abstract:Carbon supported platinum nanowires (Pt NWs/C), acting as cathode catalyst for proton exchange membrane fuel cell (PEMFC), were synthesized by reducing H2PtCl6 with HCOOH at room temperature without assistance of template. The catalyst microstructure and morphology were characterized by transmission electron microscopy (TEM) and X-ray diffraction (XRD). The Pt NWs/C had an average cross-sectional diameter of (4.0±0.2) nm and a length of 15-25 nm. Good electrocatalytic performance and oxygen reduction reaction (ORR) of the as-prepared catalyst was characterized by cyclic voltammetry (CV) and linear sweep voltammetry (LSV). Two membrane electrode assemblies (MEAs) were fabricated, with Pt NWs/C and Pt/C as cathode catalyst respectively, and tested for comparison. The maximum power densities of Pt NWs/C and Pt/C, respectively were 705.6 mW·cm-2 and 674.4 mW·cm-2. Afterwards, an 18-cell stack with Pt NWs/C as cathode catalyst and a 20-cell stack with Pt/C as cathode catalyst were built for testing. Maximum power densities were 409.2 mW·cm-2 and 702.7 mW·cm-2, and coefficients of variation (Cv) of individual cell were 16.1% and 4.36% at the maximum power density, respectively. Data analysis indicated that Pt NWs/C for the cathode in a MEA exhibited good catalytic activity at a scale-up level, however, as compared with the commercial Pt/C catalyst, CV performance and uniformity should be improved. This work not only sheds light on the scale-up possibility of Pt NWs/C catalyst, but also provides a possibility for further durability test before its application in a fuel cell vehicle.

A Study on Novel Pulse Preparation and Electrocatalytic Activities of Pt/C-Nafion Electrodes for Proton Exchange Membrane Fuel Cell

Preparation of Membrane Electrode Assemblies for Proton Exchange Membrane Fuel Cells

Carbon‐supported Pt‐Co Nanowires As a Novel Cathode Catalyst for Proton Exchange Membrane Fuel Cells

Carbon-supported Pt nanowire as novel cathode catalysts for proton exchange membrane fuel cells

Preparation of Pt nanowires as cathode catalyst for PEMFC and its application in stack

Highly Active Carbon-Supported Pt Nanoparticles Modified and Dealloyed with Co for the Oxygen Reduction Reaction

Pt Nanowire Electrocatalysts for Proton Exchange Membrane Fuel Cells

An Effective Method of Applying Octahedral Pt-Ni/C to Membrane Electrode Assembly and Related In-Situ X-ray Absorption Fine Structures Study

Efficient Synthesis of Pt–Co Nanowires As Cathode Catalysts for Proton Exchange Membrane Fuel Cells

Preparation of Oxygen Reduction Catalyst Electrodes by Electrochemical Acidification and Synergistic Electrodeposition

Patchy Fe-N-C Supported Low-Loading Pt Nanoparticles As a Highly Active Cathode for Proton Exchange Membrane Fuel Cells

Preparation and Application of Pt-Ni Catalysts Supported on Cobalt-Polypyrrole-Carbon for Fuel Cells

Performance of Proton Exchange Membrane Fuel Cell Electrodes Prepared by Direct Deposition of Ultrathin Platinum on the Membrane Surface

Electrodepositing Pt by Modulated Pulse Current on A Nafion-Bonded Carbon Substrate As an Electrode for Pemfc

A New Method for the Preparation of the Electrodes with Very Low Platinum Loading Used in Proton Exchange Membrane Fuel Cell

In situ grown nanoscale platinum on carbon powder as catalyst layer in proton exchange membrane fuel cells (PEMFCs)

Research on Electrocatalysts of Proton Exchange Membrane Fuel Cells

Highly dispersed ultrafine PtCo alloy nanoparticles on unique composite carbon supports for proton exchange membrane fuel cells

Manipulation of Electronic States of Pt Sites Via D-Band Center Tuning for Enhanced Oxygen Reduction Reaction in Proton Exchange Membrane Fuel Cells.

High-performance anode for Polymer Electrolyte Membrane Fuel Cells by multiple-layer Pt sputter deposition

Enhanced Catalytic Properties from Platinum Nanodots Covered Carbon Nanotubes for Proton-Exchange Membrane Fuel Cells