Abstract:Novel phosphorus-containing liquid crystalline copolyesters based on biphenyl mesogenic monomer (PDEBP) were synthesized by polycondensation of dimethyl biphenyl-4,4'-dicarboxylate (DBD), diethylene glycol (DEG) and a phosphorus-containing diol, 2-(6-oxido-6H-dibenz < c, e > < 1, 2 > oxaphosphorin-6-yl)-1,4-phenylenebis(oxy) diethanol (DOPO-HQ-HE). Chemical structure of the PDEBP was characterized by H-1-NMR spectroscopy, and the thermal and liquid crystalline behaviors of the copolyesters were investigated by thermogravimetric analysis (TGA), differential scanning calorimetry (DSC) and hot-stage polarizing optical microscope (POM) TGA results suggested that char formation of the copolyesters was improved with the introduction of DOPO-HQ-HE without destroying the initial thermal stability of the polymer, and the residue at 700 degrees C in N-2(W-tR(700)) of PDEBP7.5 (7.5 mol% of DOPO-HQ-HE in copolyester) reached 31. 9 wt%, having a positive influence on flame retardance of the copolyesters. DSC tests suggested that the crystallinity of the copolyesters was destroyed by incorporating DOPO-HQ-HE into the main chain due to the bulky pendent group. The isotropic temperature (T-i) and endothermic heat (Delta H-i) were decreased by increasing the amount of DOPO-HQ-HE, and the T-i, and Delta H-i, of PDEBP7. 5 reached 129 degrees C and 1. 61 J/g, respectively. POM observations showed that a typical birefringence phenomenon of nematic schlieren structure could be found in the processes of both heating and cooling, in accord with the results of DSC tests except these of PDEBP7. 5, for which it was hard to find the birefringence phenomenon during heating and cooling by POM, indicating the further introduction of the phosphorus-containing diol could destroy the liquid crystalline behavior of the resulting copolyester.

Synthesis,Characterization and Thermal Properties of a Novel Phosphorus-Containing Copolyesters Based on 2-carboxyethyl (phenylphosphinic) Acid

A phosphorus-, nitrogen- and carbon-containing polyelectrolyte complex: preparation, characterization and its flame retardant performance on polypropylene

Synthesis and Properties of Copolyesters Containing Phosphorus in Main Chains

Thermal Stability and Flame Retardancy of Phosphorus-containing Copolyester Nanocomposites

A novel phosphorus-containing poly(1,4-cyclohexylenedimethylene terephthalate) copolyester: Synthesis, thermal stability, flammability and pyrolysis behavior

Synthesis and Thermal Behavior of Phosphorus-Containing Thermotropic Wholly Aromatic Copolyesters

Synthesis and Characterization of Phosphorus-Containing Liquid Crystalline Copolyesters Based on Biphenyl-4, 4 '-Dicarboxylic Acid

Phosphorus-containing copolyesters: The effect of ionic group and its analogous phosphorus heterocycles on their flame-retardant and anti-dripping performances

Synthesis and Thermal Degradation Behaviours of Novel Phosphorus-Containing Polyurethane Elastomers

Phosphorus-containing Poly(trimethylene Terephthalate) Derived from 2-(6-oxido-6h-dibenz〈c,e〉〈1,2〉oxaphosphorin-6-yl)-1,4-hydroxyethoxy Phenylene: Synthesis, Thermal Degradation, Combustion and Pyrolysis Behavior

Novel Inherently Flame-Retardant Poly(trimethylene Terephthalate) Copolyester with the Phosphorus-Containing Linking Pendent Group

Aggregation State and Thermal Properties of Copolyesters Containing Phosphaphenathrene

A Novel Phosphorus‐containing Copolyester with Low Melting Temperature and High Flame Retardancy

Preparation of Phosphorus-Containing Poly-Acrylate Resins and their Flame Resistant Properties

Synthesis and Curing Kinetics of Phosphorus-Containing Unsaturated Polyester with Reactive Flame Retardant

A novel biodegradable phosphorus-containing copolyester with preferable flame retardancy and mechanical properties

Synthesis and thermal behavior of a novel UV-curable transparent flame retardant film and phosphorus-nitrogen synergism of flame retardancy

Synthesis and Property Testing of a Novel Copolymerizable Flame Retardant

Unsaturated Polyester Resins Modified with Phosphorus-Containing Groups: Effects on Thermal Properties and Flammability

A Novel Branched Phosphorus-Containing Flame Retardant: Synthesis and Its Application into Poly(Butylene Terephthalate)

Synthesis and Flame-Retardant Properties of Phosphorus-Containing Polymers Based on Poly(4-Hydroxystyrene)