The effect of temperature and dynamic loading on quartz fiber posts conglutinate with root dentin

Wen-hao QIAN,Pei-cheng XU,Jian-sheng SU
DOI: https://doi.org/10.3969/j.issn1008-0392.2010.06.007
2010-01-01
Abstract:Objective To compare the effect of surface treatments on the push-out shear bond strength of quartz fiber posts to three root regions under dynamic loading and Thermocycling.Methods Fifty-four extracted human maxillary central incisors were decapitated and treated with complete root canal therapy.Then prepare the path of post.54 quartz fiber posts were randomly assigned into three groups according to the chemical surface treatments:treat with silane agent(Group A),treat with 24% Hydrogen peroxide(Group B),treat with 24%Hydrogen peroxide,then with silane agent(Group C), Posts were inserted using the resin adhesive system.Each group quartz fiber posts were treated according to dynamic loading(n = 6),Thermocycling(n=6) and contrast(n=6).The dynamic loading group samples were applied to 30 N load with 1.25 Hz at 135 degrees angle with tooth long axis,and treated for 10 000 cycling on fatigue test machine.Thermocycling group samples were subject to thermal cycling for 10000 times(treated temperature:5℃/55℃,dwell time:30 s,transfer time:20 s).Control group samples were saved in Sodium Chloride for one week at 37℃.After treatment each root was sectioned into three sections with 2 mm thick.A push-out test was performed to measure bond strengths.Data were analyzed with ANOVA.Results In the cervical of the root,the push-out bond strength was significant weak after dynamic loading treatment when compared with control(P<0.01).However,in the middle of the root,the push-out bond strength only A group was significant infirmness after dynamic loading treatment when compared with control(P<0.05).In comparison of Thermocycling treatment with control samples,the cervical third of the root,the push-out bond strength was significant lower in A and B group after Thermocycling treatment(P<0.05).In the middle of the root,the push-out bond strength from A group of Thermocycling treatment was markered lower than control(P<0.05). However,in the apical of the root,there were no significant different in the push-out bond strength among any group(P>0.05).Conclusion Dynamic loading and Thermocycling treatment could reduce the push-out shear bond strength of quartz fiber posts on tooth root,especially in the cervical third of the root.But there is no significant effect on C group.
What problem does this paper attempt to address?