Abstract:Polyethylene glycol 4000 (PEG-4000), PEG-20000, and polyvinyl pyrrolidone (PVP) at various concentrations were used as dispersants for the preparation of iron nanoparticles with a liquid-phase reducing method. The effects of these non-ionic surfactants as dispersants were investigated to improve product dispersibility and reactivity. Scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), double-beam UV-visible spectrophotometry (UV), and atomic absorption spectrophotometry (AAS) were used to characterize and investigate the product and its effectiveness in removing lead(II). SEM analysis showed that all three surfactants improved the dispersibility of iron nanoparticles. Fine, fibrous iron nanoparticles were attained after adding PEG-4000 and PEG-20000, whereas fluffy particulate iron nanoparticles were obtained after adding PVP. The FT-IR results indicated that the three surfactants did not undergo chemical reactions during iron nanoparticle formation. Instead, they attached to or coated the surface of the nanoparticles through electrostatic interaction or van der Waals forces. The results of XRD demonstrated that the surfactants had no influence on the crystal phase of iron nanoparticles, and the UV results indicated the dispersion effects of PEG-20000 and PVP were superior to that of PEG-4000. The AAS results showed that the maximum adsorption capacity of lead(II) reached 229 mg/g when iron nanoparticles were prepared by adding 3% PEG-20000. ©, 2015, South China University of Technology. All right reserved.

Preparation of FePt nanoparticles via polyol-reduction process

Preparation of FePt nanoparticles with flower-like assembly

Surfactants induced morphology control of FePt nanoparticles

Preparation and Characterization of Monodisperse FePd Nanoparticles

Preparation and characterization of FePt nanoparticles

Facile synthesis and surfactant regulated high coercivity of FePt nanoparticles

Polyol Synthesis of Superparamagnetic Fe_3O_4 Nanoparticles for Magnetic Resonance Imaging

Preparation of Monodisperse and Highly Coercive L10-FePt Nanoparticles Dispersible in Nonpolar Organic Solvents

Direct Synthesis and Size Selection of Ferromagnetic FePt Nanoparticles

Formation of monodisperse FePt alloy nanocrystals using air-stable precursors: fatty acids as alloying mediator and reductant for Fe3+ precursors

Synthesis of Silica Oxide-Coated FePt Magnetic Nanoparticle and Its Magnetic Properties

Shape-Selective Preparation and Properties of Oxalate-Stabilized Pt Colloid

Synthesis and Magnetic Studies of Core-Shell FePt@Fe3O4 Nanowires and Nanoparticles

FePt3 nanosuspension synthesized from different precursors – a morphological comparison by SAXS, DLS and TEM

Preparation and characterization of Fe3O4 nanoparticles via a hydrothermal process with propanediol as the solvent

Preparation and Surface Modification of Monodisperse Fe3O4 Nanoparticles

Preparation of Langmuir-Blodgett Monolayer Film of Fept Nanoparticles on Different Substrates Using Cycling Compression Method

Size-controlled Synthesis and Magnetic Studies of Monodisperse FePd Nanoparticles.

Characterization of Iron Nanoparticles Prepared with Non-ionic Surfactants

Magnetic Monodisperse Fe3o4 Nanoparticles