Abstract:While the addition of WC increases the hardness and wear resistance of coatings, an excessive WC content can also induce crack initiation and propagation, increasing brittleness and leading to premature failure. Therefore, in this study, WC particles were incorporated into nickel-based coatings by plasma-arc surfacing to optimize their content and distribution, balancing their tensile properties and wear resistance. The coatings were comprehensively evaluated through microstructural analysis, hardness testing, wear resistance assessment, and tensile testing. The results show that as the mass fraction of WC increased from 45% to 65%, the increase in carbon significantly promoted the formation of M7C3, M6C, and M23C6 carbides and suppressed the formation of the γ-phase. The microstructural analysis showed that the content of massive carbides increased significantly with the increasing WC content, and the XPS analysis further confirmed that the changes in the WC and Cr7C3 phases were particularly pronounced in the high-WC coating. The 65% WC coating showed higher hardness (a 232 increase in HV1.0), a lower and more stable coefficient of friction (0.42), and better wear resistance than the 45% WC coating, with a wear rate of 3.329 × 10−6 mm3/(N·m)−1, which was 3.709 × 10−6 mm3/(N·m)−1 lower than that of the 45% WC coating. The conventional tensile test results show that the maximum stress and strain of the 45% WC coating were 71% and 36% higher than those of the 65% WC coating, respectively. In addition, the 45% WC coating exhibited better ductility and quasi-cleavage characteristics, whereas the 65% WC coating showed typical brittle cracking behavior. The results of the field tensile tests also showed that the fracture time of the 65% WC coating was 27 s shorter than that of the 45% WC coating. Overall, the 45% WC coating had a good combination of strength and toughness.

Wear Behavior of Plasma Sprayed Ni-WC Composite Coatings

Residual stress and wear resistance of WC particle reinforced Ni-based coating

Microstructure and Wear Performance of WC Reinforced Ni-based Composite Coating

Influence of WC content on the wear resistance of plasma sprayed WC/Ni60 coatings

ABRASIVE WEAR BEHAVIOR OF WC REINFORCED Ni-BASED COMPOSITE COATING SPRAYED AND FUSED BY OXY-ACETYLENE FLAME

Wear performance of the plasma sprayed fine WC-Co composite powders coatings

Effect of WC–Co Content on the Microstructure and Properties of NiCrBSi Composite Coatings Fabricated by Supersonic Plasma Spraying

Effect of WC Content on Hardness and Fracture Toughness of WC-Ni60A Wear-Resistant Coatings

Optimizing Wear Resistance and Tensile Strength of Nickel-Based Coatings through Tungsten Carbide Reinforcement

Microstructure and wear-resistance performance of WC / Cu-Ni-Mn composite coatings

WC-Co Reinforced NiCoCrAlYTa Composite Coating: Effect of the Proportion on Microstructure and Tribological Properties

Study on the friction and wear properties of nickel-based-WC-10Ni composite coatings prepared on the surface of TC4 titanium alloy

A Study On Abrasive Resistance Of Ni-Based Coatings With A Wc Hard Phase

Influence of WC particle behavior on the wear resistance properties of Ni–WC composite coatings

Wear Behavior of Ni/WC Surface-Infiltrated Composite Coating on Copper Substrate

Dissolution Behaviour of WC Particles and Evolution of Precipitated Phases in the Plasma Transfer Arc Ni-based Composite Coating Reinforced by 30 Wt.% WC Particles

Microstructure and Wear Resistance of Composite Coatings Ni-Co/WC+G

Microstructure and Wear Behavior of Arc Sprayed Wc-Co/Fecrb and Wc-Ni/Fecrb Composite Coatings

Study on the abrasive resistance of Ni-based coatings containing WC hard phase

Microstructure and Wear Behavior of Hard Ni60 and Soft WC-12Co/N125 Coatings Prepared by Laser Cladding on W1813N Non-magnetic Stainless Steel