Synthesis of Novel Sulfonated Polybenzimidazole and Preparation of Cross-Linked Membranes for Fuel Cell Application
Hongjie Xu,Kangcheng Chen,Xiaoxia Guo,Jianhua Fang,Jie Yin
DOI: https://doi.org/10.1016/j.polymer.2007.07.029
IF: 4.6
2007-01-01
Polymer
Abstract:A novel sulfonated polybenzimidazole, sulfonated poly[2,2′-(p-oxydiphenylene)-5,5′-bibenzimidazole] (SOPBI), was successfully prepared by post-sulfonation reaction of the parent polymer, poly[2,2′-(p-oxydiphenylene)-5,5′-bibenzimidazole] (OPBI), using concentrated and fuming sulfuric acid as the sulfonating reagent at 80°C, and the degree of sulfonation (DS) could be regulated by controlling the reaction conditions. No significant polymer degradation was observed in the post-sulfonation processes. Direct polymerization of 4,4′-dicarboxydiphenyl ether-2,2′-disulfonic acid disodium salt (DCDPEDS) and 3,3′-diaminobenzidine (DABz), however, resulted in insoluble gels either in polyphosphoric acid (PPA) or in phosphorus pentoxide/methanesulfonic acid (PPMA) in a ratio of 1:10 by weight reaction medium. The SOPBIs prepared by the post-sulfonation method showed good solubility in dimethyl sulfoxide (DMSO), high thermal stability, good film forming ability and excellent mechanical properties. Cross-linked SOPBI membranes were successfully prepared by thermal treatment of phosphoric acid-doped SOPBI membranes at 180°C in vacuo for 20h and the resulting cross-linked membranes showed much improved water stability and radical oxidative stability in comparison with the corresponding uncross-linked ones, while the proton conductivity did not change largely. Highly proton conductive (150mScm−1, 120°C in water) and water stable SOPBI membrane was developed.