Abstract:Monocore powder-in-tube MgB2 strands were cold-drawn and heat-treated at 600C and 700C for times of up to 71 hours and structure-property relationships examined. Drawing-induced elongation of the Mg particles led, after HT, to a textured macrostructure consisting of elongated polycrystalline MgB2 fibers separated by elongated pores. The superconducting Tc, Jc and Fp were correlated with the macrostructure and grain size. Grain size increased with HT time at both 600C and 700C. Jc and hence Fp decreased monotonically but not linearly with grain size. Overall, it was observed that at 700C, the MgB2 reaction was more or less complete after as little as 30 min; at 600C, full reaction completion did not occur until 71 h. into the HT. Transport, Jct(B) was measured in a perpendicular applied field, and the magnetic critical current densities, Jcm\bot(B) and Jcm{\phi}(B), were measured in perpendicular and parallel (axial) applied fields, respectively. Particularly noticeable was the premature dropoff of Jcm\bot(B) at fields well below the irreversibility field of Jct(B). This effect is attributed to the fibrous macrostructure and its accompanying anisotropic connectivity. Magnetic measurements with the field directed along the strand axis yielded a critical density, Jcm\bot(B), for current flowing transversely to the strand axis that was less than and dropped off more rapidly than Jct(B). In the conventional magnetic measurement, the loop currents that support the magnetization are restricted by the lower of Jct(B) and Jcm{\phi} (B). In the present case the latter, leading to the premature dropoff of the measured Jcm(B) compared to Jct(B) with increasing field. This result is supported by Kramer plots of the Jcm{\phi} (B) and Jct(B) data which lead to an irreversibility field for transverse current that is very much less than the usual transport-measured longitudinal one, Birr,t.

Temperature dependence of magnetic torque for a single crystal MgB2 in 10 kG

Superconducting anisotropy and evidence for intrinsic pinning in single crystalline MgB$_2$

Magnetic torque study of the temperature dependent anisotropy parameter in overdoped superconducting single-crystal YBa_2Cu_3O_7

Unusual effects of anisotropy on the specific heat of ceramic and single crystal MgB2

Two-bandgap magneto-thermal conductivity of polycrystalline MgB<sub>2</sub>

Superconducting Diamagnetic Fluctuations in MgB2

Magnetic field induced orientation of superconducting MgB$_2$ crystallites determined by X-ray diffraction

Thermal Conductivity of Ferrimagnet GdBaMn2O5.0 Single Crystals

STUDIES ON ANISOTROPY FOR SINGLE-CRYSTAL GdBa2Cu3O7-δ

Torque magnetometry on single-crystal high temperature superconductors near the critical temperature: a scaling approach

Research on anisotropy for single crystal GdBa2Cu3O7−y

High magnetic anisotropy and magnetocaloric effects in single crystal Cr$_2$Te$_3$

Large Anisotropic Normal-State Magnetoresistance in Clean MgB2 Thin Films.

Angular Dependent Torque Measurements on CeCoIn$_5$ Single Crystals

Anisotropy of superconductivity of as-grown MgB$_2$ thin films by molecular beam epitaxy

Study of high temperature resistivity and thermal stability of superconductor MgB2

Evidence for A Temperature Dependent Anisotropy of the Superconducting State Parameters in Underdoped Smba2cu3ox

Review of superconducting properties of MgB2

Large Anisotropic Thermal Expansion Anomaly near the Superconducting Transition Temperature in MgB2

Drawing induced texture and the evolution of superconductive properties with heat treatment time in powder-in-tube in-situ processed MgB2 strands

Transport and magnetic Jc of MgB2 strands and small helical coils