Abstract:ZnO nanorods were grown on ITO substrates with different concentration of electrolyte by electrodeposition method. Microstructure, surface topography, photoluminescence Spectra, Raman spectra and water contact angle of the thin films were measured. The XRD results show all samples are hexagonal wurtzite and the intensity of diffraction peaks at (002) preferred orientation are strengthen as electrolyte concentration increase from 0.005 to 0.03 M. As the concentration increases, the average diameter, density and inclination of the ZnO nanorods increased. Room temperature photoluminescence spectras of the ZnO nanorods show a narrow UV band centering at about 377 nm and broad visible emissions around 600 nm and the UV peak intensity revealed a remarkable decreased. Raman spectras exhibit three peaks which are located at 439 cm(-1), 562 cm(-1) and 1095 cm(-1). All samples change from hydrophobicity to hydrophilic after one hour ultraviolet (UV) irradiation. (C) The Author(s) 2015. Published by ECS. This is an open access article distributed under the terms of the Creative Commons Attribution Non-Commercial No Derivatives 4.0 License (CC BY-NC-ND, http://creativecommons.org/licenses/by-nc-nd/4.0/), which permits non-commercial reuse, distribution, and reproduction in any medium, provided the original work is not changed in any way and is properly cited. For permission for commercial reuse, please email: oa@electrochem.org. All rights reserved.

Electrochemical synthesis of orientation-ordered ZnO nanorod bundles

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Preparation of Large-Scale Highly Oriented Zno Noodle Arrays and Study on the Photoconductivity

Facile synthesis of Zn 1−x Cu x O nanorods with a very broad visible band

Effects of Electrodeposition Electrolyte Concentration on Microstructure, Optical Properties and Wettability of ZnO Nanorods

Effect of Electrodeposition Time on Microstructure, Wettability and Optical Properties of ZnO Nanorod Arrays

A large-scale-oriented ZnO rod array grown on a glass substrate via an in situ deposition method and its photoconductivity

A Versatile Approach for the Synthesis of ZnO Nanorod-Based Hybrid Nanomaterials Via Layer-by-Layer Assembly

Controlled Synthesis of Oriented Single-Crystal Zno Nanotube Arrays on Transparent Conductive Substrates

Preparation and Photoluminescence of ZnO with Nanostructure by Hollow-Cathode Discharge

Fabrication of oriented ZnO nanorod arrays and their optical performances

Morphological control of ZnO nanostructures by electrodeposition.

Controlled one-step fabrication of highly oriented ZnO nanoneedle/nanorods arrays at near room temperature.

Electrochemical Route to the Synthesis of Ultrathin ZnO Nanorod/nanobelt Arrays on Zinc Substrate

Nanostructured ZnO: from Monodisperse Nanoparticles to Nanorods

Straight and Thin ZnO Nanorods: Hectogram-Scale Synthesis at Low Temperature and Cathodoluminescence.

Synthesis of Monodispersed Zno Nanorod Array Films by Chemical Solution Deposition.

Substrate effect on Electrodeposition of ZnO nanorod Arrays

Complex and oriented ZnO nanostructures

Controllable Synthesis of Highly Dispersed Zno Nanoparticles and Nanorods

A simple and novel route for the preparation of ZnO nanorods