Abstract:In this paper, phenolic resin (PF) and dicyclopentadiene (DCPD) monomers were mixed in different proportions. Under the action of a new generation of ruthenium carbene catalysts, DCPD was polymerised in situ. Polydicyclopentadiene (PDCPD)/PF interpenetrating polymer networks (IPNs) were prepared using the casting curing moulding process. The structure and properties of the prepared IPNs were characterised using Fourier infrared spectroscopy (FT-IR), apparent crosslinking degree, thermal weight loss, mechanical properties, impact resistance and scanning electron microscopy (SEM). The study results showed that the conversion of DCPD did not change with the addition of PF. But when its content exceeds 10%, the crosslinking degree of PDCPD decreases. When the PF content is 10%, the maximum bending strength of PDCPD/PF IPNs is (104.5 ± 1.3) MPa, maximum tensile strength is (74.5 ± 1.4) MPa, and maximum-notched impact strength is (4.2 ± 0.2) kJ/m 2 . Compared with PDCPD, the bending strength is increased by 22.7%, tensile strength is increased by 32.6%, and notched impact strength is increased by 31.3%, but the thermal stability has no major impact at this time. PF has good dispersibility and compatibility in DCPD. Due to the interpenetrating network structure of PF and PDCPD, the interpenetrating interlocking of the PF molecular chain and PDCPD crosslinked network restricts its movement. Its performance reached the optimum, and the PDCPD/PF IPNs with excellent performance was successfully prepared.

A Novel Approach to Interpenetrating Networks of Epoxy Resin and Polydimethylsiloxane

Cure of Neat Resins and Properties of Composites for Interpenetrating Polymer Networks from the Novel Bismaleimide and Cyanate Containing Naphthalene

Interpenetrating polymer networks from the novel bismaleimide and cyanate containing naphthalene: Cure and thermal characteristics

Simultaneous Interpenetrating Polymer Networks of Polyurethane from Pentaerythritol–Modified Castor Oil and Polystyrene: Structure–Property Relationships

Synthesis and characterization of epoxy resin‐polydicyclopentadiene interpenetrating polymer networks by UV‐initiated simultaneously frontal polymerization

Interpenetrating polymer networks templated on bicontinuous microemulsions containing silicone oil, methacrylic acid, and hydroxyethyl methacrylate

Synthesis and characterization of crosslinkable latex with interpenetrating network structure based on polystyrene and polyacrylate

Enhanced mechanical and adhesive properties of PDMS based on novel PDMS-epoxy IPN structure

On the synergism of interpenetrating polymer networks of PU/EP

Preparation and properties of an interpenetrating network polymer based on polydicyclopentadiene and phenolic resin

Preparation and characterization of a semi-interpenetrating network gel polymer electrolyte

Synthesis and Characterization of Nanocomposites of Silicon Dioxide and Polyurethane and Epoxy Resin Interpenetrating Network

Synthesis and Characterization of Ph‐ and Temperature‐sensitive Silk Sericin/poly(n‐isopropylacrylamide) Interpenetrating Polymer Networks

Interpenetrating Thermophobic and Thermophilic Dual Responsive Networks

Interpenetrating polymer networks hydrogels

Reactive blend of epoxy-novolac resin and epoxide-terminated low-molecular-weight poly(phenylene oxide)

Interpenetrating Polymer Network Hydrogels Composed of Chitosan and Photocrosslinkable Gelatin with Enhanced Mechanical Properties for Tissue Engineering

Thermal, Mechanical, and Morphological Properties of Soybean Oil-Based Polyurethane/epoxy Resin Interpenetrating Polymer Networks (Ipns)

Interpenetrating Polymer Networks with Controllable Intermolecular Hydrogen Bonding

Evaluation of Effective Crosslinking Density for Pseudo-Semi Interpenetrating Polymer Networks Based on Polyether Glycols Mixture by Dynamic Mechanical Analysis

Simultaneous One-Pot Interpenetrating Network Formation to Expand 3D Processing Capabilities