Abstract:This article reports the successful synthesis of mesoporous hydroxyapatite, Ca-10(PO4)(6)(OH)(2) (denoted HA) using cationic surfactant as the template. The wide-angle (2theta > 10degrees) diffraction data revealed characteristic peaks of HA, where a hexagonal lattice structure can be deduced. The lattice structure is found in space group P6(3)/m, the parameters of which are in excellent agreement with reference data; i.e. a = b = 0.9418 nm, c = 0.6884 nm. For small angle diffraction (2theta < 10&DEG;), the characteristic peaks occur at 2θ values of 3.30, 5.75, 7.25 and 8.30&DEG;, indicating the presence of atomic planes with a periodical spacing of 2.677 nm. Nitrogen adsorption indicated a pore size distribution of approximately 3 nm, and a corresponding pore volume of 0.0113 cm(3) g(-1), hence the volume ratio of the mesopores was found to be &SIM;0.036. SEM micrographs reveal a rod-like structure of HA, possessing a thickness of about 50-100 nm and length ranging from 500 to 1000 nm, while TEM micrographs revealed that nano-channels are formed within the rod-like structure. These nano-channels align in a lengthwise direction within the rods, consistent with the cavities being generated by the removal of "organic" CTAB templating structure during calcination. The channels have dimensions of around 3.5 nm and the spaces between the nano-channels are filled with an ordered crystalline HA structure. Comparing the pore size and the spacing between neighboring channels, the pore volume ratio of each rod was calculated to be &SIM;0.029, which is in agreement with the result from gas adsorption. A probable mechanism is that CTAB-PO43- mixtures form rod-like micelles, which contain many PO43- groups on the surface, and in the presence of Ca2+, Ca-9(PO4)(6) clusters are preferentially condensed on the rod-shaped micellar surface due to the conformation compatibility between the identical hexagonal shapes of the micelles and Ca-9(PO4)(6) clusters. The micelles act as nucleating points for the growth of HA crystals. During the thermal incubation stage, CTAB-HA complexes are produced and they coalesce to form a stable three-dimensional rod-like structure. The morphology of the final product shows about 10 layers of HA crystal grows on one micelle during the reaction in water.

Biomineralizing Synthesis of Mesoporous Hydroxyapatite–calcium Pyrophosphate Polycrystal Using Ovalbumin As Biosurfactant

Biomineralization of large hydroxyapatite particles using ovalbumin as biosurfactant

Synthesis of Hydroxyapatite Mediated by Amphiphilic Block Copolymer PS112-b-PAA38

Synthesis of Hydroxyapatite Mediated by Amphiphilic Block Copolymer PS<sub>112</sub>-b-PAA<sub>38</sub>

Triblock Co-Polymer Templating Synthesis of Mesostructured Hydroxyapatite

Crystallization of smooth amorphous calcium phosphate microspheres to core-shell hydroxyapatite microspheres

“Reservoir” and “barrier” effects of ABC block copolymer micelle in hydroxyapatite mineralization control

Hydroxyapatite nanostructure material derived using cationic surfactant as a template

Preparation of Mesoporous Nano-Hydroxyapatite Using a Surfactant Template Method for Protein Delivery

Microwave Hydrothermal Transformation of Amorphous Calcium Carbonate Nanospheres and Application in Protein Adsorption

Fabrication of Hydroxyapatite Hierarchical Hollow Microspheres and Potential Application in Water Treatment

Controlled Synthesis of Hydroxyapatite Crystals Templated by Novel Surfactants and Their Enhanced Bioactivity

Synthesis of Mesoporous Hydroxyapatite Using a Modified Hard-Templating Route

Hydroxyapatite hierarchically nanostructured porous hollow microspheres: rapid, sustainable microwave-hydrothermal synthesis by using creatine phosphate as an organic phosphorus source and application in drug delivery and protein adsorption

Biomimetic Hydroxyapatite Porous Microspheres with Co-Substituted Essential Trace Elements: Surfactant-Free Hydrothermal Synthesis, Enhanced Degradation and Drug Release

Mineralization of Calcium Phosphate Controlled by Biomimetic Self-Assembled Peptide Monolayers Via Surface Electrostatic Potentials

Biomimetic mineralization of a hydroxyapatite crystal in the presence of a zwitterionic polymer

Biomimetic Synthesis and Characterization of Hydroxyapatite Crystal with Low Phase Transformation Temperature

Synthesis of Polymerized Calcium Silicate Hydrate Nanostructures As Drug Carriers

Apatite-binding Peptide Induced Self-assembly of Calcium Phosphate Particles in an In Vitro Biomimetic Mineralization System

Synthesis of Mesoporous Structured Hydroxyapatite Particles Using Yeast Cells As the Template