Abstract:To achieve the high dispersion of SiO2 nanoparticles in polyurethane acrylate resin, the titanate coupling agent, PN-102, was used as the surface modifier to prepare the modified SiO2 nanoparticles (Si-PN102-5) with small particle size and good dispersion ability in PUA-6 resin. Accordingly, hydrophilic SiO2 (Si-380) and hydrophobic SiO2 (Si-115) were introduced into PUA-6 resin to prepare the corresponding composite coatings, so as to investigate the effects of SiO2 nanoparticles modified with different surface modifiers on the properties of PUA / SiO2 composite coatings. The properties of PUA / SiO2 composite coatings were characterized by the tests of FTIR, AFM, SEM, DMA, TG and so on. The FT-IR and XPS results show that PN-102 had functionalized the SiPN102-5 particle surface successfully. The TEM test displays that the particle size of SiO2 was almost unchanged before and after modification, maintaining at about 20-30 nm. The SEM, DMA and tensile test reveal that Si-PN102-5 not only blocks the interaction and accumulation of nanoparticles, but also enhances the interface interaction with polymer chains through chain entanglement, which endows Si-PN102-5-5% composite coatings with highest mechanical strength among the other prepared coatings, reaching to 11.0 +/- 0.1 MPa in tensile strength and 9.4 +/- 3.0% in elongation at break. The pencil hardness of the prepared Si-PN102-5-5% composite coating could reach to 5H which is higher than the commercial PUA-6 based coating, and it also displayed good adhesion (4B) and flexibility (3 mm). The TG results show that all of prepared composite coatings display good thermal stability with a decomposition temperature of higher than 250 degrees C.

Effect of Antimony Doped Tin Oxide on Behaviors of Waterborne Polyurethane Acrylate Nanocomposite Coatings

The Coating Properties of Waterborne UV-Curable Polyurethane Acrylate and Influencing Factors

Preparation of Environmentally Friendly Anticorrosive Coatings with Aniline Trimer-Modified Waterborne Polyurethane

Preparation of functional ZnO nanoparticles and their application as UV photosensitizer and reinforcing agent for waterborne polyurethane acrylate composite coating

Synthesis and Application of Hydroxyethyl Methacrylate Modified Waterborne Polyurethane

Preparation, mechanical properties of waterborne polyurethane and crosslinked polyurethane‐acrylate composite

Effects of aminopropyl-terminated polydimethylsiloxane on structure and properties of waterborne polyurethane-acrylate

UV-curable waterborne polyurethane acrylate modified with octavinyl POSS for weatherable coating applications

Synthesis and UV-curing of Waterborne Acrylated Polyurethanes

Preparation, Characterization, and Property Analysis of Environmentally Friendly Waterborne Polyurethane-Acrylate

The Synergistic Effects of Sio2 Nanoparticles and Organic Photostabilizers for Enhanced Weathering Resistance of Acrylic Polyurethane Coating

Preparation and Properties of UV-curable Polyurethane Acrylate/sio2 Composite Hard Coatings

Research on the Performance of Series Waterborne Polyurethane Acrylate Modified Epoxy Acrylates

Effect of Water Content on the Aggregation and Adhesion Properties of Waterborne Polyurethane

Realization of customizable performance castor oil-based waterborne polyurethane antiseptic coatings via arbutin

Preparation and Characterization of Fluorinated Acrylate and Epoxy Co-Modified Waterborne Polyurethane

Preparation and Properties of UV-Curable Waterborne Polyurethane Acrylate/MXene Nanocomposite Films

Eliminating the oxygen inhibition in the redox free radical polymerization of alicyclic polyurethane acrylate coatings: A study of the beneficial effect of paraffin wax

Effects of Isosorbide on the Microphase Separation and Properties of Waterborne Polyurethane Coatings

Study on the Synthesis and Properties of Waterborne Polyurea Modified by Epoxy Resin

Preparation, properties and application of waterborne hydroxyl-functional polyurethane/acrylic emulsions in two-component coatings