Abstract:A simple ultrasonic method was developed to synthesize rod-like SnS nanocrystals, using tin chloride and thioacetamide as starting materials, ethanolamine and water as solvents. The as-obtained nanostructures were characterized by X-ray diffraction (XRD) study, energy-dispersive X-ray spectroscopy (EDS), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS) and Ultraviolet-visible spectrophotometry (UV). From the XRD pattern, the reflection peaks of the as-obtained samples can be indexed to the orthorhombic structure with lattice constants a = 3.99, b = 4.34, c = 11.20 angstrom, which are very consistent with the values in the standard card of SnS phase (JCPDS No. 39-0354). No characteristic peak was observed for other impurities such as SnO2 and SnS2, implying the formation of single-phase tin monosulfide. The quantification calculation shows the ratio of Sn/S to be 51.30/48.70 via the EDS analysis. These data clearly indicate that the as-prepared rod-like nanostructures are exactly SnS. TEM results show that, the SnS nanorods have length about 100nm and width less than 30nm. The direct and indirect band gaps of the SnS nanorods are determined to be 1.53 eV and 1.34 eV, respectively. The band gaps of the as-obtained SnS nanorods showed blue shifts due to the quantum size effects. The ultrasonic condition is believed to be critical for the formation of SnS with pure phase. For it provides the energy to form rod-like nanostructures and helps preventing the hydrolysis of Sn2+ to form tin oxides and hydrates. Also, it prevents oxidation of the final products.

Room temperature growth of nanocrystalline tin (II) selenide from aqueous solution

A Hydrothermal Method for Low-Temperature Growth of Nanocrystalline Pyrite Nickel Diselenide

Synthesis of nanocrystalline lead chalcogenides PbE (E = S, Se, or Te) from alkaline aqueous solutions

A Redox Reaction to Synthesize Nanocrystalline Cu2-xSe in Aqueous Solution

Two-dimensional SnS nanosheets fabricated by a novel hydrothermal method

Solvothermal Synthesis to Cu2snse4 Nanocrystals at Low Temperature

Solvothermal Route to Tin Monoselenide Bulk Single Crystal with Different Morphologies

Room Temperature Synthesis of Cubic Nanocrystalline CdSe in Aqueous Solution

Solution-phase synthesis of monodispersed SnTe nanocrystallites at room temperature

A hydrothermal synthesis of orthorhombic nanocrystalline cobalt diselenide CoSe2

A convenient, low temperature route to nanocrystalline SnSe

A Novel Room Temperature Method to Nanocrystalline Ag2se

Organic solution method for crystal growth of tin chalcogenides with special morphologies

Solvent–thermal preparation of nanocrystalline tin chalcogenide

Ultrasonically Assisted Synthesis of Tin Sulfide Nanorods at Room Temperature

Hydrothermal synthesis, characterization and properties of SnS nanoflowers

Surfactant-Controlled Growth of Selenium Nanowires at Room Temperature

A direct solvothermal route to nanocrystalline selenides at low temperature

An Aqueous Approach to ZnSe and CdSe Semiconductor Nanocrystals

Tin Selenide (SnSe): Growth, Properties, and Applications

Synthesis of SnS2 nanocrystals via a solvothermal process