Abstract:At present stage, the transmittance improvement is still a thorny problem in SiAlON ceramics due to their complex composition and processing. In the present research, Dy–α-SiAlON ceramics were selected to be translucent in the medium infrared range. The samples had a higher densification value by using hot-pressing (HP) sintering method at 1650–1700 °C with or without LiF additive. The as-sintered specimens experienced the post-hot-isostatic-pressing (PHIP) treatment at 1650–1700 °C for 30–90 min in either N 2 or Ar environment to increase the optical transmittance. A significant optical transparency improvement has been found in Dy–α-SiAlON, with or without LiF co-doping, undergone a PHIP at 1700 °C for 30 min under an Argon gas pressure of 180 MPa. The improved transmittance attributes to a fully developed α-Sialon crystalline phase, a uniform grain size, a denser grain arrangement, and a clean grain boundary, based on the X-ray diffraction analysis, SEM and TEM microstructure observation, and optical transmittance measurement. Keywords Dy–α-SiAlON Hot pressing sintering Post hot-isostatic-pressing treatment Transmittance Infrared range 1 Introduction SiAlONs, as the solid solution of Si 3 N 4 with the substitution of Al and O for Si and N, are well-developed advanced engineering ceramic materials for their excellent combination of mechanical strength, toughness, hardness and thermal shock resistance. And it has also been interesting in the controllable properties of SiAlON's by chemical composition design and processing adjusting. In recent twenty years, the translucent SiAlONs attracted considerable attention for their potential applications as optical window or dome materials in a wide range from visible to medium infrared wavelengths, facing an increased requirement for some applications in the extreme harsh environment, for example, under higher temperature or supersonic working conditions. Many material scientists have successfully prepared different translucent SiAlONs with varied element doping or substitution of Al and O for Si and N. In 1981, Mitomo with his colleagues reported a translucent β-SiAlON using the hot-pressing sintering technique, with a composition of z = 2–4, but the transmittance was not very high in the infrared region. 1 Later, Karunaratne reported that Y 3+ -doped SiAlON could be optical translucent ceramics, just using a pressureless sintering method. 2 In the following years, a serial colorful and translucent SiAlONs were obtained by a wider selection of elements doping from alkali earth cations Ca 2+ , Mg 2+ to many rear earth cations, where most of the prepared ceramics were α-SiAlONs. In 1997, Shen's group designed and sintered a series of Nd3 + , Tb 3+ , Er 3+ , Sm 3+ , and Y 3+ -doped translucent SiAlONs by hot-pressing method. 3 Then, Mandal's group reported the single-phase α-SiAlONs with a wider optical transmission range by hot-isostatic-pressing sintering. 4 Jones with his colleagues prepared Lu–α-SiAlONs with a higher transmission of 70% in the visible region and a dual phase mixture of α/β-SiAlONs having a higher toughness, in 2003 and 2004 respectively. 5,6 Su and Chen shown us some good results of higher transmission in the infrared range of 3–5 μm obtained in Dy–SiAlON by spark plasma sintering and Gd–SiAlON by hot pressing method in 2004 and 2005. 7,8 Recently, Xiong's group published their research work on the translucent Mg–SiAlON using spark plasma sintering. 9 In the same year, Xue of our group reported the lower temperature sintering of translucent Dy–SiAlON with LiF as additive. 10 Furthermore, Ye with his group published their new results about Y 3+ /Yb 3+ dual-doped α-SiAlONs having a higher infrared transmission and toughened Sc 3+ /Lu 3+ doped α-SiAlONs by an in situ growth of elongated grains in 2008 and 2009 respectively. 11,12 Now it is clear that a higher optical transmission, without a bigger victim of mechanical properties, is the aim that all SiAlONs researchers pursued for. Therefore many efforts have been made to reach the aim by accurately adjusting of chemical composition and purity, and using post-heat-treatment. While the post-heat-treatment after sintering process was considered to be effective to increase transmission by increasing the uniformity of grain size, minimizing the pores in the bulks, and reducing the amounts of residual glassy phase or grain boundary phase. It is the microstructural inhomogeneity (pores, grain boundary, anisotropy of grains, etc.) in the polycrystalline ceramics that causes the internal light scattering with a resultant of optical opaque. Among the post-heat treatment techniques, the hot-isostatic-pressing (HIP) or post-hot-isostatic pressing (PHIP) were proved to be an important way to further densify the powder compacts, then to provide the improvement of mechanical and optical properties. Ekstrom et al. reported the Yttrium-doped α-SiAlON HIP-ed and PHIP-ed with less residual grain boundary glass phases. 13 It was the reduced residual grain boundary glass phases that played a positive role in raising the optical transmittance of materials. Motivated by the research activities mentioned above, in the present study, hot-pressing sintering (HP) and post-hot-isostatic-pressing technique were combined to fabricate and enhance the Dy–α-SiAlONs with a higher transmission in medium infrared region of 3–5 μm, because Dy–α-SiAlONs are excellent candidates for optical window materials, not only for their stability of crystal phase but also for the economical consideration. 2 Experimental According to the phase equilibrium relationship of the complex SiAlONs and the formula of M m / v Si 12−( m + n ) Al m + n O n N 16− n , the α-SiAlON ceramics reported here has a nominal composition Dy 0.66 Si 9.0 Al 3.0 O 1.0 N 15.0 (noted as Dy–SiAlON, where M = Dy, m = 2 n = 2.0, v = 3). High-purity powders of α-Si 3 N 4 (SN-E10, Ube, Japan), AlN (Grade A, Starck, Germany), Dy 2 O 3 (Yaolong Chemical Plant, Shanghai, China), Al 2 O 3 (Yaolong Chemical Plant, Shanghai, China), and LiF (Sinopharm Chemical Reagent Co., Ltd, Beijing, China) were mixed in ethanol, milled using Si 3 N 4 balls in a Si 3 N 4 jar. After milling, the powder slurry was dried at 80 °C and sieved. And then a charge of 6.0 g each was loaded directly into a graphite die of 25 mm in diameter. The samples were hot pressed at 1650–1700 °C under a 30 MPa pressure for 60 min in a flowing nitrogen atmosphere of 0.1 MPa. After HP sintering, the compacted samples were put into the HIP furnace for a further PHIP heat treatment at 1650–1700 °C for 30–90 min under a 120 MPa pressure of N 2 or a 180 MPa pressure of Ar atmosphere. The HP-sintered and PHIP-treated samples were sliced with the surface perpendicular to the hot-pressing direction, and then polished or thinned to different thickness for the microstructure observation and optical transmission measurement. Bulk density of specimens was measured by Archimedes principle. The phase analysis was performed using the X-ray diffractionmeter (D8, Advance X-ray Diffractionmeter, Bruker, Germany). Microstructure observation was carried out under an electron probe microanalyzer (JXA-8100, JEOL, Japan) and transmission electron microscope (JEM-2010/200CX/2100F, JEOL, Japan). Optical transmission of the translucent samples in wavelength of 2.5–6.5 μm was measured using a Fourier Transform Infrared Spectrometer (EQUINOX55, Bruker, USA). 3 Results and discussion Table 1 lists the results obtained from all samples HP-sintered and PHIP-treated, in which it clearly shows the effects of temperature, soaking time, or atmosphere of PHIP treatment on phase purity and optical transmittance of the resultant bulks. Based on the previous researches by other scientists and ourselves, 10,14–16 additional and optimal 0.1 wt% LiF was added to reduce the HP-sintering temperature, decrease the grain size, and then increase the optical transmittance to some extent. LiF was considered to be an important sintering additive for preparing ceramics at lower temperatures by causing the formation of intermediate phase. Presumably, LiF “film”, or a film of complex composition formed by reaction with SiO 2 on Si 3 N 4 powders, or Al 2 O 3 on AlN powders, or grain boundary phases, could act as an “eutectic activated layer” or “pathway” through which an enhanced grain boundary sliding, or particle rearrangement, or interface diffusivity could occur, with an increasing sintering rate and grain growth. Comparatively, Dy–SiAlON without 0.1 wt% LiF additive should be sintered at a higher temperature level (1700 °C) to reach a full density. Therefore, there were no significant differences in grain size, morphology, grain boundary phases, and even density between LiF-doped and undoped Dy–SiAlON. Fig. 1 shows a HRTEM micrograph and EDAX analysis of the triple junction by three grains in the 0.1 wt%LiF–Dy–SiAlON HP-sintered at 1650 °C for 60 min in N 2 gas. The elemental analysis of the grain boundary phase indicates the complex composition of Dy–Si–Al–O–N with a trace of F existence. The XRD data for the series samples either HP-sintered or PHIP-treated ones showed that the crystalline phase in the HP-sintered bulks was primarily α-SiAlON with minor Dy–melilite solid solution Dy–melilite solid solution (Dy 2 Si 3− x Al x O 3+ x N 4− x , abbreviated as M′) or as main grain boundary phase, but the samples undergone a PHIP-treatment in N 2 atmosphere contained more Dy–mellilite solid solution phase. It is reasonable to consider the co-existence of α-SiAlON with Dy 2 Si 3− x Al x O 3+ x N 4− x phase, according to the subsolidus phase relationships in the systems R–Si–Al–O–N (R = Nd, Sm, Dy) and also the calculation results of multicomponent systems, 17,18 where R-melilite solid solution was thought to be the only stable compound which is compatible with α- or β-SiAlON in the complex system of R 2 O 3 –Si 3 N 4 –AlN–Al 2 O 3 . It should emphasize that the percentages of Dy–melilite solid solution increase gradually with the increase of temperature and Al substitute in a following N 2 atmosphere. In our present experiment, when PHIP-treated in N 2 atmosphere, the Dy–SiAlON experienced the second run of heating and soaking at higher temperature in a N 2 atmosphere. As a consequence, the solution–precipitation–recrystallization process might occur during the longer PHIP stage at the interface between Dy 2 Si 3− x Al x O 3+ x N 4− x and α-SiAlON phase. And more Dy 2 Si 3− x Al x O 3+ x N 4− x phase too could develop because its lower viscosity and higher mobility of reaction than those of Dy–SiAlON. The most striking feature in the experimental result was the big difference in optical transmittance between the HP-sintered and PHIP-treated samples. The HP-sintered ones, with or without LiF addition, were all translucent in a wide range from visible to medium infrared wavelength, seen in Fig. 2 , showing a translucent LiF–Dy–α-SiAlON sample after HP-sintered. Contrarily, the samples PHIP-treated in the N 2 atmosphere were all opaque, with more grain boundary phase contents contained, as mentioned above. The increased grain boundary phase was thought to be formed at the interface or triple junctions of grains under a higher PHIP temperature, a longer soaking time, but a rather lower N 2 pressure (120 MPa) condition. That might be related to a solution–precipitation–recrystallization process of SiAlON grains, reacted with grain boundary phase Dy–melilite solid solution during the PHIP step under a rather lower pressure of N 2 gas, since the PHIP-treatment was generally carried out under a much higher gas pressure than 180 MPa to restrict the “solution” of crystalline grains. Fig. 3 gives a strong evidence to support the explanation, which illustrates the surface micrograph of the sample Dy–SiAlON PHIP-treated at 1650 °C/90 min/N 2 (120 MPa), where it can be seen that the round α′ grains are surrounded by grain boundary phases, that is indentified to be the chemical composition rich in N and Si contents according to EDAX elemental analysis. And a heavier C contamination (about 5 wt%) was also detected in the same sample. Comparatively, the samples, that were PHIP-treated at much higher temperature of 1700 °C but in an inert Ar environment, showed a higher transmittance than that of the original HP-sintered ones. There was only a minor M′ phase existence in the PHIP-treated sample around an inert Ar gas, since a much higher inert gas pressure was very effective to restrict the “solution” of crystalline grains. The highest value of transmittance was obtained in the sample 0.1LiF-doped Dy–α-SiAlON experienced a PHIP history at 1700 °C/30 min/Ar (180 MPa) after HP-sintering at 1650 °C/60 min/N 2 . Fig. 3 shows the optical transmittance spectrum and a TEM micrograph of the investigated PHIP-ed (in Ar gas) sample, 0.1LiF-doped Dy–α-SiAlON with a thickness of 0.5 mm for transmittance measurement. The sample has a higher optical transmittance in the medium infrared region and the transmittance value is over 70%, possessing a maximum value of 73%. As a comparison, the maximum transmittance value of the original HP-ed 0.1LiF-doped Dy–α-SiAlON sample was only 62%. The specimen PHIP-treated at 1700 °C/30 min/Ar (180 MPa) was chosen for electron microscope observation to find some answers about the transparency improvement in the view of microstructure. The micrograph in Fig. 4 reveals a denser grains arrangement, an equiaxed grain morphology, and less grain boundary phases remaining at the interface or triple junctions in the PHIP-treated specimen. As expected, the PHIP treatment provided an important role in enhancing plastic yielding, creep, and diffusion of grains during the heating under a higher gas pressure applied. It is the denser grain arrangement and less grain boundary phases that attribute the transmittance improvement by reducing the light scattering from the inhomogeneous microstructure feature in the polycrystalline ceramics. As the parallel or reference experimental, the samples without additive of LiF were also investigated on their optical property and microstructure feature. The sample Dy–α-SiAlON needed to be HP-sintered at a higher temperature of 1700 °C owning less M′ grain boundary phase at interface or triple conjunctions of grain boundary. Therefore, the sample was also translucent in the visible and medium infrared region as well. The highest value of transmittance was obtained in the sample Dy–α-SiAlON experienced a post-HIP history at 1700 °C/30 min/Ar (180 MPa) after HP-sintering at 1700 °C/60 min/N 2 . Fig. 5 shows the optical transmittance spectrum and a micrograph of the investigated Dy–α-SiAlON sample, with a thickness of 1.0 mm for transmittance measurement. The sample has a higher optical transmittance in the medium infrared region and the transmittance value is over 60%, having a maximum value of 64%. As a comparison, the maximum transmittance value of the original HP-ed Dy–α-SiAlON sample was only 58%. Electron microscope observation shows no significant grain growth after experienced a PHIP step. Fig. 4 reveals a uniform grains size distribution in the PHIP-ed sample. Similarly, it is the well-grown grain size, denser grain arrangement, and less residual intergranular phases that result in the transmittance improvement in PHIP-ed Dy–α-SiAlON by weakening the light scattering from the inhomogeneous microstructure feature in the ceramics. 4 Conclusion Post-hot-isostatic-pressing (PHIP) treatment at a higher temperature (1700 °C) and under a higher inert Ar environment pressure (180 MPa) was an effective method for promoting the optical transparency of Dy–α-SiAlON with or without LiF additive, by supplying an extra driving force for sintering. The higher inert Ar gas pressure was very effective to restrict the “solution” of crystalline grains and the formation of grain boundary phase. Microstructure observation reveals that the uniform grain size with an equiaxed grain morphology, denser grain arrangement, and less grain boundary phases attribute the transmittance improvement of the Dy–α-SiAlON or LiF-doped Dy–α-SiAlON ceramics that experienced a PHIP processing in Ar environment. But the PHIP treatment under a rather lower N 2 pressure (120 MPa) showed a negative effect on the transparency increasing, by inducing a higher Dy–mellilite solid solution (M′) grain boundary phase content, resulting in a stronger light scattering. So, the further investigation on the gas pressure, gas type, and temperature of PHIP has to be considered to further promote the transparency of the SiAlONs ceramics. References 1 M. Mitomo T. Moriyoshi T. Sakai Y. Ohsaka M. Kobayasgi Translucent β-SiAlON Ceramics J Mater Sci Lett 1 1981 25 26 2 B.S.B. Karunaratne R.J. Lumby M.H. Lewis Rear-earth-doped α-SiAlON ceramics with novel optical properties J Mater Res 11 1996 2790 2794 3 Z.J. Shen M. Nygren U. Hslenius Absorption spectra of rare-earth-doped α-SiAlON ceramics J Mater Sci Lett 16 1997 263 266 4 H. Mandal New developments in α-SiAlON ceramics J Eur Ceram Soc 19 1999 2349 2357 5 M.I. Jones H. Hyuga K. Hirao Optical and mechanical properties of α/β-SiAlON composites J Am Ceram Soc 86 2003 520 522 6 M.I. Jones H. Hyuga K. Hyuga Y. Yamauch Highly translucent Lu–α-SiAlON J Am Ceram Soc 87 2004 714 716 7 X.L. Su P.L. Wang W.W. Chen Z.J. Shen M. Nygren Y.B. Cheng Effects of composition and thermal treatment on infrared transmission of Dy–α-SiAlON J Eur Ceram Soc 24 2004 2869 2877 8 W.W. Chen X.L. Su P.L. Wang D.S. Yan Optical properties of Gd–α-SiAlON ceramics: effect of carbon contamination J Am Ceram Soc 88 2005 2304 2306 9 Y. Xiong Z.Y. Fu H. Wang W.M. Wang J.Y. Zhang Q.J. Zhang Translucent Mg–α-SiAlON ceramics prepated by spark plasma sintering J Am Ceram Soc 90 2007 1647 1649 10 J.M. Xue Q. Liu L.H. Gui Lower-temperature hot-pressed Dy–α-SiAlON ceramics with LiF additive J Am Ceram Soc 90 2007 1623 1625 11 F. Ye L.M. Liu C.F. Liu H.J. Zhang Y. Zhou J. Yu High infrared transmission of Y 3+ –Yb 3+ -doped-α-SiAlON Mater Lett 62 2008 4535 4538 12 F. Ye C.F. Liu L.M. Liu Y. Zhou Optical properties on in-situ toughened ScLu–α-SiAlON Scipta Mater 61 2009 982 984 13 A. Bartek T. Ekstrom H. Herbertsson T. Johansson Yttrium α-SiAlON ceramics by hot isostatic pressing and post-hot isostatic pressing J Am Ceram Soc 75 1992 432 439 14 M.W. Benscke N.E. Olson J.A. Pask Effect of LiF on hot-pressing of MgO J Am Ceram Soc 50 1967 365 368 15 J.P. Guha H.U. Anderson Reaction during sintering of barium titanate with lithium fluoride J Am Ceram Soc 69 1986 C-193 C-194 16 K.W. White G.P. Kelkar Fracture mechanisms of a coarse-grained, transparent MgAl 2 O 4 at elevated temperatures J Am Ceram Soc 75 1992 3440 3444 17 W. Chen P. Wang D.S. Yan Study on the formation behavior and crystallography of N-containing melilite solid solutions Dy 2 Si 3− x Al x O 3+ x N 4− x (R = Nd, Sm, Dy, Y, Yb) Eur J Solid State Inorg Chem 34 1997 871 880 18 P. Dorner L.J. Gauckler H. Krieg H.L. Lucas G. Petzow J. Weiss On the calculation and representation of multicomponent systems Mater Today 3 1979 241 257

High Infrared Transmission of Y3+–Yb3+-doped Α-Sialon

Microstructure and Luminescence of Yb3+-doped Fluorosilicate Glass Ceramics

Sintering Behavior, Microstructure and Mechanical Properties of Various Fluorine-Containing Y-SiAlON Glass-Ceramics

Optical properties of in situ toughened ScLu–α-SiAlON

Spectroscopic Properties Of Er3+/Yb3+ Co-Doped 50sio(2)-20al(2)O(3)-30caf(2) Glass And Glass Ceramics

Mechanical Properties And Thermal Shock Resistance Of Refractory Self-Reinforced Alpha-Sialons Using Barium Aluminosilicate As An Additive

Spectroscopic Properties Of Er3+ And Yb3+ Co-Doped Glass Ceramics Containing Srf2 Nanocrystals

Refractory self-reinforced Y-α-SiAlON with barium aluminosilicate glass ceramic addition

Spectroscopic Properties of Er3+/Yb3+ Co-Doped 50sio2–20al2o3–30caf2 Glass and Glass Ceramics

A First Principles Study on Optical Transparency Mechanism in Dy Doped Α-Sialon Ceramics

Microstructure Characteristics And High-Temperature Performance Of In-Situ Reinforced Alpha-Sialon Ceramics

Spectroscopic properties of Er<sup>3+</sup>and Yb<sup>3+</sup>co-doped glass ceramics containing SrF<sub>2</sub>nanocrystals

Transmittance improvement of Dy–α-SiAlON in infrared range by post hot-isostatic-pressing

Sensitized Yb3+ Luminescence of Eu3+/Yb3+‐Codoped Fluorosilicate Glass Ceramics

Yb0.5Ca0.75Si7.5Al4.5O1 .5N14.5 Α-Sialon Ceramics: A Hard Material with Low Thermal Conductivity

Hot-pressing of Translucent Y-α-SiAlON Ceramics Using Ultrafine Mixed Powders Prepared by Planetary Ball Mill

Enhanced thermal insulation and mechanical properties of Y-α-SiAlON porous ceramics with Sr doping

Rapid Densification and Reaction Sequences in Self-Reinforced Y-α-SiAlON Ceramics with Barium Aluminosilicate As an Additive

Preparation and Spectroscopic Properties of Yb-doped and Yb–Al-codoped High Silica Glasses

Evolution of core–rim structures and phase transformations in infra-red transmitting Y-α-SiAlON ceramics

Effect of Different Rare-Earth on Microstructure and Properties of alpha-Sialon Ceramics