Hard Magnetic Properties and Microstructure of Melt-Spun Sm2Fe15−xCuxGa2C (x=0 and 0.5) Ribbons
SY Zhang,HW Zhang,BG Shen,WS Zhan,TS Chin,FR de Boer,KHJ Buschow
DOI: https://doi.org/10.1063/1.369629
IF: 2.877
1999-01-01
Journal of Applied Physics
Abstract:The structure, magnetic properties and microstructure of Sm2Fe15−xCuxGa2C (x=0 and 0.5) ribbons prepared by melt spinning and subsequent heat treatment were studied. A significant increase in coercivity has been found for ribbons prepared with the addition of a small amount of Cu. The maximum coercivity μ0Hc is 1.4 and 2.0 T at room temperature for ribbons with x=0 and 0.5, respectively, after annealing in vacuum at 1043 K for 15 min. A small amount of Cu addition has little effect on the lattice parameters, Curie temperature TC, and magnetocrystalline anisotropy field HA at room temperature, while it decreases the saturation magnetization Ms. The magnetocrystalline anisotropy constants K1 and K2 for the x=0 and 0.5 samples were determined in the temperature range between 50 and 293 K, using magnetically aligned samples. The variations of coercivity, magnetization, and remanence as functions of applied field and temperature are consistent with the view that the magnetization of Sm2Fe15−xCuxGa2C ribbons with x=0 as well as 0.5 are mainly controlled by pinning of domain walls. High-resolution transmission electron microscopy and energy-dispersive x-ray analysis demonstrate that Cu atoms dissolve partially into the 2:17-type matrix phase in Sm2Fe14.5Cu0.5Ga2C ribbons, which is effective in pinning the domain walls and enhancing the coercivity.