The Crystallization Behavior of Isotactic Polypropylene in Mixed Diluents

LIN Ya-Kai,CHEN Gang,YANG Jian,WANG Xiao-Lin

2007-01-01

Abstract:The non-isothermal crystallization behavior of isotactic polypropylene(iPP) in mixed diluents was investigated by polarizing microscopy, and the structure of iPP microporous materials prepared via thermally induced phase separation was studied by scanning electron microscopy(SEM). The mixtures of DBP and soybean oil were used as the diluents, and the mass fraction of iPP in the solution was fixed at 30%. Both the growth rate of iPP spherulite and the structure of iPP microporous materials are significantly influenced by the composition of mixed diluents, which result from the changes of the viscosity of the system and the compatibility between iPP and diluents. At a cooling rate of 2 K/min, the radius and growth rate of iPP spherulites both increase exponentially with time. The growth rate of iPP spherulites decreases with the increase of the mass fraction of DBP in mixed diluents. When the mass fraction of DBP in mixed diluents increases from 0 to 60%, the growth rate.of iPP spherulites decreases from 41.9 μm/min to 10.3 μm/min. Cellular structure is obtained at the cooling rate of 2 K/min, while the pore size increases significantly with the decrease of soybean oil in the mixed diluents.