Abstract:Ceramic-reinforced metal matrix composites are known for their high wear resistance. A coating based on these materials would be helpful to improve the wear behavior of aluminum alloys. Laser cladding has been used to deposit a coating consisting of an aluminum alloy reinforced with SiC particles on an AA6082 aluminum alloy. Laser cladding is a very energetic technique that causes the SiC particles to react with the molten aluminum to form Al4C3, which degrades the particles and reduces the properties of the coating. The formation of this detrimental compound was successfully achieved with the addition of Silicon and Titanium to the composite matrix. The microstructures of the newly developed material were characterized and the wear behavior was studied under dry sliding conditions on a pin-on-disc tribometer. The relationship between the microstructure and wear behavior was identified. The absence of Al4C3 in the Al40Si/SiC and Al12Si20Ti/SiC coatings’ microstructures resulted in an abrasion mechanism instead of a delamination mechanism. The wear behavior changed along the sliding distances. During the first 200 m of sliding distances, the wear rate of all coatings was lower than the uncoated one due to their higher microhardness. For longer sliding distances, the wear resistance of the uncoated AA6082 was higher than the coated ones due to the formation of a lubricant oxide layer on the AA6082 worn surface. For 1000 m of wear distances, the wear behavior was different for each coating. The wear rate of the Al12Si/SiC coating continued growing due to the delamination mechanism and the presence of Al4C3 that acted as starting crack points. The wear rate of the Al40Si/SiC coating decreased due to the formation of a thin, superficial oxide layer. The wear rate of the Al12SiTi/SiC progressively decreased along the sliding distance to below the substrate wear rate.

Effects of Surface Coating on Wear Properties of A356-20vol.%Sicp Composites

Effect of Submicron SiC Particles on the Properties of Alcocrfeni High Entropy Alloy Coatings

Wear Behaviour and Microstructural Changes of SiCw-Al Composite under Unlubricated Sliding Friction

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

Study of fabrication and wear properties of Ni–SiC composite coatings on A356 aluminum alloy

Effects of nanoceramic particle size and content on the wear resistance of micro-arc oxidation coatings for 2A12 aluminum alloy

Effects of Surface Coating Preparation and Sliding Modes on Titanium Oxide Coated Titanium Alloy for Aerospace Applications

Wear Behaviour of Friction Surfaced Al-Ni and Al-SiC Coatings over Mild Steel

Improved wear and corrosion resistance of alumina alloy by MAO and PECVD

Effect of SiC Weight Percentage on Tribological Characteristics of Al7075/SiC Composites

Sliding wear of spark plasma sintered CrFeCoNiCu high entropy alloy coatings with MoS2 and WC additions

A Comparison of the Tribological Properties of SiC Coatings Prepared via Atmospheric Plasma Spraying and Chemical Vapor Deposition for Carbon/Carbon Composites

Microstructure, Friction, And Wear Properties Of Ni-Al2o3-Mos2 Composite Coatings

Dry Sliding Behavior and Particulate Emissions of a SiC-graphite Composite Friction Material Paired with HVOF-Coated Counterface

Appraisal of tribological properties of A356 with 20% SiC composites under dry sliding condition

Wear Resistance of Aluminum Matrix Composites’ Coatings Added on AA6082 Aluminum Alloy by Laser Cladding

Enhanced Mechanical and Tribological Capabilities of a Silicon Aluminum Alloy with an Electroplated Ni–Co–P/Si3N4 Composite Coating

Effect of B4C and SiC nanoparticle reinforcement on the wear behavior and surface structure of aluminum (Al6063-T6) matrix composite

Final surface modification for better wear resistance of ceramic coating on cast AlSi10Mg alloy

Processing and Analysis of Micro-Arc Oxidation Coating on 319S Aluminum Alloy

Influence of Al2O3 reinforcement on the abrasive wear characteristic of Al2O3/PA1010 composite coatings