Abstract:Polydimethylsiloxane (PDMS) is usually used to obtain favorable performances of waterborne polyurethane (WPU) such as higher hardness, exceptional thermal stability and lower interfacial tension. However, there is always a problem that waterborne polyurethane (WPU) often performs weak tensile strength, lower tenacity and brittle property at room temperature when polydimethylsiloxane (PDMS) is embedded into the backbone of polyurethane. The study aims to address the problem by constructing dual crosslinking structure, namely introducing trimethylolpropane as an intramolecular crosslinking agent into prepolymers and then adding waterborne polycarbodiimide (SK-400) as a post-crosslinking agent in order to further enlarge the degree of crosslinking and mainly make up for the shortcoming that mechanical property decreases when polydimethylsiloxane (PDMS) was inserted into molecule chains. Initially a novel inner-crosslinking prepolymer (SiWPU) comprising polydimethylsiloxane need to be synthesized successfully by inserting trimethylolpropane into prepolymers. Then the sample SiWPU-3 was picked out as a matrix resin and dropwise added polycarbodiimide (SK-400) as a post-crosslinking agent into the matrix resin (C–SiWPU). As pH was gradually lowering following the evaporation of triethylamine in the emulsion (C–SiWPU), carboxyl groups (COOH) in prepolymers started to react with SK-400 (NCN) to form twofold crosslinking structure. When 0%, 2%, 4%, 6%, and 8 wt% of waterborne polycarbodiimide (SK-400) was incorporated into the solution, the tensile strengths are 47.8 MPa, 57.7 MPa, 65 MPa, 57.6 MPa and 54.5 MPa and the elongation at break 732%, 756%, 798%, 707% and 700%. The crosslinking density of SiWPU-3 without the addition of waterborne polycarbodiimide (SK-400) is 3.86 × 10−3 mol/cm3. As 6 wt% of waterborne polycarbodiimide (SK-400) was added into the emulsion of SiWPU-3, the crosslinking density of C–SiWPU-6 (6 wt% SK-400) is 6.19 × 10−3 mol/cm3. The films show excellent extensibility and exceptional tenacity. Hence, the emulsion is able to be applied in leather industry.

Synthesis and Characterization of a New UV Cross‐linkable Waterborne Siloxane‐polyurethane Dispersion

Synthesis of UV crosslinkable waterborne siloxane–polyurethane dispersion PDMS-PEDA-PU and the properties of the films

Synthesis and Characterization of Eugenol‐based Silicone Modified Waterborne Polyurethane with Excellent Properties

Synthesis of CO2-Derived, Siloxane-Functionalized Poly(ether Carbonate)s and Waterborne Polyurethanes

Synthesis and Characterization of PDMS Modified UV-curable Waterborne Polyurethane Dispersions for Soft Tact Layers

Synthesis of a Novel UV Crosslinking Waterborne Siloxane–polyurethane

Synthesis of UV Curable Waterborne Polyurethane Based on Dimer-Fatty-Acid Polyester Diol and Properties of Cured Film

Sturcture and Properties of New Aqueous Dispersion Polysiloxane-Polyuretane Copolymers

Synthesis and properties of self-crosslinkable polyurethane-urea with silsesquioxane formation

Preparation of an Ultraviolet‐curable Water‐borne Poly(urethane Acrylate)/silica Dispersion and Properties of Its Hybrid Film

Synthesis of waterborne polyurethane by inserting polydimethylsiloxane and constructing dual crosslinking for obtaining the superior performance of waterborne coatings

Synthesis and Properties of PDMS Modified Waterborne Polyurethane–acrylic Hybrid Emulsion by Solvent-Free Method

Synthesis of A Novel Core-Shell Type Acrylic-Polyurethane Hybrid Emulsion Containing Siloxane and Fluorine As Well As Water and the Oil Resistances of Cured Film

Characterization and Properties of UV-Curable Hyperbranched Polyurethane Acrylate-Polyurethane Diacrylate/SiO2 Hybrid Coatings

Investigation of Ultraviolet Curable Waterborne Polyurethane Acrylate Dispersion Based on Hydroxyl-Terminated Polybutadiene

Synthesis and Properties of Triethoxysilane-Terminated Anionic Polyurethane and Its Waterborne Dispersions

UV-curing of Hyperbranched Polyurethane Acrylate-Polyurethane Diacrylate/sio 2 Dispersion and TGA/FTIR Study of Cured Films

The synthesis and properties of siloxane-urethane copolymers aqueous nanodispersion using hydroxyalkyl and hydrohxypolyester terminated polydimethylsiloxane

Synthesis And Surface Property Of Siloxane-Modified Aqueous Polyurethane

Preparation and characterization of cationic waterborne polyurethanes containing a star-branched polydimethylsiloxane

Preparation and characteristics of polydimethylsiloxane (PDMS)-based waterborne polyurethane coatings with cold resistance