The relationship between (Mg,Zn)3RE phase and 14H-LPSO phase in Mg–Gd–Y–Zn–Zr alloys solidified at different cooling rates
shengdong zhang,G.Y. Yuan,canzhong lu,W.J. Ding
DOI: https://doi.org/10.1016/j.jallcom.2010.12.136
IF: 6.2
2011-01-01
Journal of Alloys and Compounds
Abstract:Mg–10Gd–3Y–1.8Zn–0.5Zr (wt.%) (GWZ1032K) alloys are prepared by permanent mold casting at cooling rate of 5 K/s, or further prepared by melt spinning at cooling rate of 10 4 K/s, or by slow solidification at different cooling rates (0.5 K/s, 0.1 K/s, 0.01 K/s and 0.005 K/s). (Mg,Zn) 3 RE phase and 14H-LPSO structure in alloys under different conditions are measured by XRD and observed under electron microscope. It shows there is no LPSO structure in the alloy prepared by melt spinning at cooling rate of 10 4 K/s. In the alloy prepared by permanent mold casting at cooling rate of 5 K/s, fine lamellar 14H-LPSO structure appears in the matrix nearby grain boundaries. With the cooling rates slowing down from 0.5 K/s to 0.005 K/s, (Mg,Zn) 3 RE phase is gradually replaced by 14H-LPSO phase at grain boundaries, and lamellar 14H-LPSO structure also propagates in α-Mg matrix. Both (Mg,Zn) 3 RE phase and 14H-LPSO phase are present at grain boundaries in the alloys solidified at cooling rates of 0.5 K/s and 0.1 K/s. When the cooling rate is very slow (0.005 K/s), lamellar 14H-LPSO structure penetrates throughout the matrix grain. It suggests the cooling rate is an important factor for the formation of 14H-LPSO structure in as-cast GWZ1032K alloys. The orientation relationship between (Mg,Zn) 3 RE phase and 14H-LPSO phase is determined by the composite SAED patterns, which is expressed as (1 1 0) (Mg,Zn)3RE //(0 0 1 4) 14H-LPSO phase , [ 3 ¯ 3 2 ] ( Mg , Zn ) 3 RE / / [ 1 1 0 ] 14 H-LPSO phase and [ 1 ¯ 1 2 ] ( Mg , Zn ) 3 RE / / [ 2 1 0 ] 14 H-LPSO phase . Keywords Mg–Gd–Y–Zn alloys Long period stacking ordered structure Cooling rate Orientation relationship 1 Introduction Recently, there has been increasing interest in the use of Mg alloys for applications in automobiles and aircrafts, due to their light weight and good mechanical properties. As new light structural materials, it is projected that the age-hardenable Mg–Gd–Y–Zr alloys represent super high strength and excellent creep resistance at both ambient and elevated temperatures [1–4] . However, their plasticity is very poor and thus limits their application, because the high content of rare earth (RE) is up to 10 wt.% or so. A number of cast Mg alloys containing small amount of Zn have been investigated recently [5–17] . These investigations have shown that Zn can be used to improve mechanical properties due to the formation of long period stacking ordered (LPSO) structure. A previous study reported the rapidly solidified powder metallurgy Mg 97 Zn 1 Y 2 alloys [5] , with LPSO structure, performed remarkable high strength (>600 MPa) and high ductility. The main reason for the excellent mechanical properties of these alloys is that the existence of LPSO structure improves the hardness and strength of Mg alloys [6,7] . In Mg–Gd–Zn and Mg–Gd–Y–Zn alloys prepared by permanent mold casting, LPSO structure is precipitated as 14H from the matrix upon annealing [8–10] . Yamasaki et al. [9] found that the microstructure of as-cast Mg–Gd–Zn alloy was composed of α-Mg matrix and eutectic compounds at grain boundaries, acknowledged as DO 3 -type (Mg,Zn) 3 Gd phase and α-Mg. Wu et al. [11,12] observed preciously little 14H-LPSO structured lamellae in α-Mg matrix close to grain boundaries in as-cast Mg–Gd–Zn alloy. This work also pointed out that in Mg–Gd–Zn alloy heat-treated at 773 K, 14H-LPSO phase was transformed from eutectic phase and the transformation mechanism is considered as spinodal decomposition. With respect to the fact that LPSO structure has been observed in Mg–Gd–Y–Zn alloys [13–17] , the nature of LPSO structure is further investigated in this study. We observed the characteristic morphologies of 14H-LPSO structure in Mg–Gd–Y–Zn alloys solidified at different cooling rates. The orientation relationship between (Mg,Zn) 3 RE phase and 14H-LPSO phase has been demonstrated. 2 Experimental procedure For the present investigation, Mg–10Gd–3Y–1.8Zn–0.4Zr (wt.%, refer to GWZ1032K hereafter) was prepared in an electric resistance furnace under a mixed atmosphere of CO 2 and SF 6 with 100:1 ratio. The raw materials were pure Mg and Zn (>99.95%), and Mg–25 wt.% Gd, Mg–25 wt.% Y and Mg–30 wt.% Zr. The alloy ingots were cast in a permanent mold and cooled in air. Six GWZ1032K specimens are arranged in Table 1 according to the cooling rates from high to low. Alloy B was prepared with permanent mold casting at the cooling rate of 5 K/s and used as the master alloy. Alloys A, C, D, E and F were obtained from the master alloy with the specific treatment. Alloy A was produced from the master alloy, re-melted using induction melting and then prepared by melt spinning method at the roller surface velocity of 10 m/s in purified melt atmosphere. The cooling rate of the as-spun ribbons for Alloy A was calculated 10 4 K/s according to the method published in previous study [18] . The four specimens of slow solidification were fabricated as follows. The master alloys were protected by cover agents and placed in the graphite crucible of the heat treatment furnace with sulfurous iron ore. Alloys were heated at 923 K for 30 min for complete melt and solute homogenization. After that, the temperature dropped off from 923 K to 723 K at four different cooling rates. After reaching 723 K, the specimens were taken out and quenched in cold water. The cooling rates for Alloys C, D, E and F were calculated in accordance with the cooling curves and expressed as 0.5 K/s, 0.1 K/s, 0.01 K/s and 0.005 K/s, respectively. At the same time, the temperature within the furnace was controlled by the temperature controller. In order to measure the actual cooling rates of the alloys, a thermocouple was inserted into the graphite crucible to achieve the temperature of the melting alloys. The cooling curves of the alloys were acquired by using data collection module and are presented in Fig. 1 . To investigate the microstructure, all materials were grinded, polished and etched. Microstructures were investigated using a LEO1450 scanning electron microscope (SEM) including an energy-dispersive X-ray analysis (EDS) to determine the local chemical compositions. Transmission electron microscopy (TEM) investigations were employed on thin foil samples of the different GWZ1032K alloys. The foils were prepared by electropolishing in a twin jet system using a solution of 4% HClO 4 and 96% methanol at 253 K and a voltage of 50 V. The TEM examinations were carried out using a JEOL-2010 instrument operating at 200 kV. For the phase analysis, X-ray diffraction (XRD) measurements were also performed using a Bruker D8 Advance (Bruker AXS, Karlsruhe, Germany). 3 Results The XRD measurements shown in Fig. 2 could prove the presence of α-Mg phase, (Mg,Zn) 3 RE phase or 14H-LPSO phase in the diffraction patterns for six alloys. The typical α-Mg peaks are present in all alloys. Only α-Mg phase (marked with hollow triangles) is recognized from the pattern of Alloy A. Both α-Mg and (Mg,Zn) 3 RE phase (marked with hollow circles) are observed in Alloy B, this finding is also in agreement with the investigations of Yamasaki et al. [9] . Apart from α-Mg and (Mg,Zn) 3 RE phase, an additional peaks of 14H-LPSO phase (marked with hollow rhombuses) are identified from the patterns of Alloys C and D. However, only α-Mg and 14H-LPSO phase are recognized from the patterns of Alloys E and F. The microstructure revealed by TEM is shown for Alloy A in Fig. 3 . Fig. 3 a shows a typical TEM bright-field (BF) image of the microstructure of Alloy A. The dendrite within area A in Fig. 3 a is α-Mg phase, confirmed by using selected area electron diffraction (SAED) patterns with the electron beam parallel to the [ 0 1 1 ¯ 1 ] and [ 1 2 ¯ 1 3 ¯ ] zones respectively ( Fig. 3 b and c). A dark-field electron micrograph and SAED pattern of area B note that the matrix is composed of α-Mg nanoscale particles ( Fig. 3 d and e). α-Mg nanoscale particle has a size smaller than 10 nm and appears an ellipsoidal shape. There is no LPSO structure found in Alloy A. The comparison of the EDS spectrums between the dendrite ( Fig. 3 f) and nanoscale particles ( Fig. 3 g) illustrates that the content of Gd, Y and Zn atoms in the dendrite is significantly more than that in nanoscale particles. This result suggests the dendrite within area A is α-Mg supersaturated solid solution. Fig. 4 shows the microstructure of Alloy B casted by permanent metal mold. As shown in Fig. 4 a, eutectic compounds are discontinuously located at grain boundaries. Fine lamellae formed on specific habit plane of α-Mg grains are close to grain boundaries. Typical TEM BF images and corresponding SAED patterns for eutectic phase and fine lamellae are shown in Fig. 4 b and c respectively. The SAED pattern of eutectic phase (B = [0 0 1] and [0 1 1] respectively) indicates that it has a cubic structure ( a = 0.7283 nm) ( Fig. 4 b). The EDS spectrum indicates eutectic phase has an average composition of 65 ± 3Mg–21.5 ± 2Gd–3.5 ± 1Y–6 ± 10Zn (at.%), i.e. (Mg,Zn) 3 (Gd,Y) 1 . The XRD measurement of eutectic phase ( Fig. 2 ) is also coincident with Mg 3 Gd phase (DO 3 , a = 0.7324 nm [19] ). In this study, eutectic phase is formulated as DO 3 -type (Mg,Zn) 3 RE phase, whereas the second phase in as-cast GW103K alloy without Zn content is identified as Mg 24 (Gd,Y) by our previous work [4] . In Fig. 4 c, the SAED pattern of fine lamellae in the matrix (B = [1 1 0] α-Mg ) shows it has a 14H-type LPSO structure ( a = 0.3370 nm, c = 3.5789 nm), with the evidence of 13 extra spots spacing equally between the central spot and the (0 0 2) Mg spot. Fig. 5 presents the microstructure of Alloys C and D solidified slowly at the cooling rates of 0.5 K/s and 0.1 K/s, respectively. Besides (Mg,Zn) 3 RE phase, 14H-LPSO phase appears at the grain boundaries both in Alloy C ( Fig. 5 a) and Alloy D ( Fig. 5 b). Typical TEM BF image and SAED pattern (B = [1 1 0] 14H-LPSO phase ) of 14H-LPSO phase are shown in Fig. 5 c and d. The SAED pattern indicates that there is it also has a 14H-LPSO structure ( a = 0.3375 nm, c = 3.5810 nm). The EDS spectrum indicates 14H-LPSO phase has an average composition of 88 ± 3Mg–4.5 ± 2Gd–1.5 ± 1Y–6 ± 2Zn (at.%), i.e. Mg 12 (Gd,Y) 1 Zn 1 . The XRD pattern of 14H-LPSO phase ( Fig. 2 ) is also in agreement with Mg 12 YZn phase in Mg–Y–Zn alloys [20] . Fig. 6 shows a magnified SEM image of (Mg,Zn) 3 RE phase, 14H-LPSO phase and fine lamellae in Alloy D. (Mg,Zn) 3 RE phase and 14H-LPSO phase are connective with each other at grain boundaries. The needle-shaped (Mg,Zn) 3 RE phase is identified in 14H-LPSO phase and the eutectic (Mg,Zn) 3 RE phase connects tightly with 14H-LPSO phase. Both the needle-shaped and eutectic (Mg,Zn) 3 RE phases have a specific habit plane with 14H-LPSO phase. Fig. 7 shows TEM BF images and corresponding SAED patterns of (Mg,Zn) 3 RE phase and 14H-LPSO phase at grain boundaries. The needle-shaped (Mg,Zn) 3 RE phase is surrounded by 14H-LPSO phase ( Fig. 7 a). The corresponding composite SAED pattern of (Mg,Zn) 3 RE phase and 14H-LPSO phase obtained from their interface ( Fig. 7 b) indicates (1 1 0) (Mg,Zn)3RE //(0 0 1 4) 14H-LPSO phase and [ 3 ¯ 3 2 ] ( Mg , Zn ) 3 RE / / [ 1 1 0 ] 14 H-LPSO phase . Fig. 7 c shows the eutectic (Mg,Zn) 3 RE phase links with 14H-LPSO phase. The corresponding (Mg,Zn) 3 RE phase/14H-LPSO phase SAED pattern ( Fig. 7 d) indicates (1 1 0) (Mg,Zn)3RE //(0 0 1 4) 14H-LPSO phase and [ 1 ¯ 1 2 ] ( Mg , Zn ) 3 RE / / [ 2 1 0 ] 14 H-LPSO phase . In Fig. 7 b, parallel weak streaks arise along the direction of g(0 0 1) 14H-LPSO phase and through the ± 1/2 { 1 ¯ 1 0 } 14 H - LPSO phase positions. In Fig. 7 d, parallel weak streaks arise along the direction of g(0 0 1) 14H-LPSO phase and through the ± 1 / 6 { 1 ¯ 2 0 } 14 H - LPSO phase , ± 2 / 6 { 1 ¯ 2 0 } 14 H - LPSO phase , ± 3 / 6 { 1 ¯ 2 0 } 14 H - LPSO phase 14H-LPSO phase , ± 4 / 6 { 1 ¯ 2 0 } 14 H - LPSO phase or ± 5 / 6 { 1 ¯ 2 0 } 14 H - LPSO phase positions. Two kinds of 14H-LPSO structures were observed in Alloys E and F, they are 14H-LPSO phase and lamellar 14H-LPSO structure ( Fig. 8 ). 14H-LPSO phase is observed at grain boundaries. Lamellar 14H-LPSO structure is formed on specific habit plane of α-Mg grains. In contrast to fine lamellae in Alloy B, lamellar 14H-LPSO structure in Alloys E and F is more prominent. In Alloy E, lamellar 14H-LPSO structure arranges nearby grain boundaries but does not penetrate throughout the grains ( Fig. 8 b). In Alloy F, the volume fraction of lamellar 14H-LPSO structure is much higher and every grain is penetrated by these lamellae ( Fig. 8 d). 4 Discussion There are two categories of 14H-LPSO structures emerging in as-cast GWZ1032K alloys during solidification, known as 14H-LPSO phase and lamellar 14H-LPSO structure. 14H-LPSO phase is as a second phase formed at grain boundaries. Lamellar 14H-LPSO structure is located in the α-Mg matrix, it is close to grain boundaries. The morphologies of two 14H-LPSO structures are changing dynamically under different solidification conditions. In Alloy B casted by permanent metal mold, the solute segregation is prominent due to a relatively high cooling rate (5 K/s). RE and Zn atoms in Alloy B are segregated at grain boundaries to form (Mg,Zn) 3 RE phase by eutectic reaction, which is followed with the nucleation of α-Mg matrix. The degree of solute segregation declines with the cooling rate slowing down, thus the volume fraction of (Mg,Zn) 3 RE phase decreases and 14H-LPSO phase begins to form at grain boundaries. Ultimately, only 14H-LPSO phase exists at grain boundaries and (Mg,Zn) 3 RE phase disappears. In addition, the volume fraction of lamellar 14H-LPSO structure in the matrix increases with the cooling rate slowing down. The alloy cools down slowly so that RE and Zn atoms diffuse into the matrix, thus lamellar 14H-LPSO structure has enough time to nucleate and propagate. When the cooling rate is very slow, lamellar 14H-LPSO structure cross over the matrix grain as shown in Alloy F. Datta et al. [21] reported that the energy of 14H-LPSO structure is fairly close to that of the hcp structure, indicating 14H-LPSO structure is a very stable structure. In this study, a stable 14H-LPSO structure tends to form in GWZ1032K alloy during solidification with the cooling rate slowing down. Take Alloy E (0.005 K/s) as an example, 14H-LPSO phase appears at grain boundaries and lamellar 14H-LPSO structure is significant in the matrix. The stacking sequence of 14H-LPSO structure in GWZ1032K alloy is identified as ABABCACACACBABA, which consists of two ABCA stacking sequence structural units [22–24] . It is well known that RE and Zn atoms are enriched in B and C layers in the ABCA structural unit [24] . The formation mechanism of 14H-LPSO structure is known as spinodal decomposition in Mg–Gd–Zn alloys [11,12] . The ordered arrangement of RE and Zn atoms in 14H-LPSO structure needs a driving force. But in Alloy A prepared by melt spinning, there was no enough driving force for the ordered arrangement of solute atoms (Gd, Y and Zn) because of a very high cooling rate. As a result, 14H-LPSO structure failed to form in Alloy A although the density of solute atoms kept a high level. Ding et al. [25] reported the detailed microstructure evolution of Mg–Gd–Zn–Zr alloy heat-treated at high temperature was similar to that of GWZ1032K alloy treated at different cooling rates. They found that in the heat-treated Mg–Gd–Zn–Zr alloy at high temperature, DO 3 -type (Mg,Zn) 3 RE phase at grain boundaries transformed into 14H-LPSO phase. Our study further investigated the mechanism of this transformation and the orientation relationship between (Mg,Zn) 3 RE phase and 14H-LPSO phase. Both (Mg,Zn) 3 RE phase and 14H-LPSO phase are observed at grain boundaries in GWZ1032K alloys at the rates of 0.5 K/s and 0.1 K/s. The orientation relationship between (Mg,Zn) 3 RE phase and 14H-LPSO phase was revealed by SAED patterns as (1 1 0) (Mg,Zn)3RE //(0 0 1 4) 14H-LPSO phase , [ 3 ¯ 3 2 ] ( Mg , Zn ) 3 RE / / [ 1 1 0 ] 14 H-LPSO phase and [ 1 ¯ 1 2 ] ( Mg , Zn ) 3 RE / / [ 2 1 0 ] 14 H-LPSO phase . The finding of this orientation relationship is helpful to the researches on the transformation mechanism from (Mg,Zn) 3 RE phase to 14H-LPSO phase. We found that weak streaks are observed in SAED patterns obtained from the interface between (Mg,Zn) 3 RE phase and 14H-LPSO phase. Zhu pointed out that any disordered arrangement of RE and Zn atoms within the segregation layers would lead to the disappearance of streaks and intensity maxima in SAED patterns of LPSO structure in Mg–Y–Zn alloys [21] . It is considered that weak streaks maybe caused by the ordered arrangement of RE and Zn atoms and lattice distortion in the area near the interface. Our study demonstrates the morphology and volume fraction of 14H-LPSO structure in GWZ1032K alloy are adjusted by the cooling rate. This finding indicates slow solidification, as well as hot extrusion [26] and rapidly solidified powder metallurgy [5] , is one of methods to obtain Mg alloy with uniformly distributed LPSO structure. 5 Conclusion We investigated the morphologies of 14H-LPSO structure in GWZ1032K alloys solidified at different cooling rates. The obtained conclusions are summarized as follows. We investigated the morphologies of 14H-LPSO structure in GWZ1032K alloys solidified at different cooling rates. The obtained conclusions are summarized as follows. 1 14H-LPSO structure, including 14H-LPSO phase and lamellar 14H-LPSO structure, is present in Alloy B (5 K/s), Alloy C (0.5 K/s), Alloy D (0.1 K/s), Alloy E (0.01 K/s) and Alloy F (0.005 K/s), but not present in Alloy A (10 4 K/s). It suggests that 14H-LPSO structure in as-cast GWZ1032K alloy increases with the cooling rate slowing down. When the cooling rate is very slow (0.005 K/s), lamellar 14H-LPSO structure propagates through the matrix grain. 2 The second phase at grain boundaries is variable in the as-cast GWZ1032K alloys at different cooling rates. Alloy B (5 K/s) has only (Mg,Zn) 3 RE phase. Both (Mg,Zn) 3 RE phase and 14H-LPSO phase are found in Alloy C (0.5 K/s) and Alloy D (0.1 K/s). There is only 14H-LPSO phase in Alloy E (0.01 K/s) and Alloy F (0.005 K/s). 3 The orientation relationship between (Mg,Zn) 3 RE phase and 14H-LPSO phase is determined by the composite SAED patterns to be (1 1 0) (Mg,Zn)3RE //(0 0 1 4) 14H-LPSO phase , [ 3 ¯ 3 2 ] ( Mg , Zn ) 3 RE / / [ 1 1 0 ] 14 H - LPSO phase and [ 1 ¯ 1 2 ] ( Mg , Zn ) 3 RE / / [ 2 1 0 ] 14 H - LPSO phase . Weak streaks along the direction of g(0 0 1) 14H-LPSO phase were also observed in the composite SAED patterns. Acknowledgements The authors acknowledge the financial support of the National Nature Science Foundation of China (No.: 50771063 ), and Science and Technology Commission of Shanghai Municipality ( 08JC1412200 ), and New-century Training Program Foundation for the Talents by the State Education Commission of China ( WCET-07-0554 ). The authors want to express their gratitude to Prof. S.P. Chen and Prof. D.L. Lin for their valuable advice on the discussion of this paper. The authors thank the Instrumental Analysis Center of Shanghai Jiao Tong University for their technical support. References [1] L.L. Rokhin Magnesium Alloys Containing Rare Earth Metals 2003 Taylor and Francis London p. 1 [2] S. Kamado Y. Kojima R. Ninomiya K. Kubota G.W. Lorimer Proceedings of the Third International Magnesium Conference, 1996 1997 Institute of Materials Machester, UK 327 [3] S.M. He X.Q. Zeng L.M. Peng X. Gao J.F. Nie W.J. Ding J. Alloy Compd. 427 2007 316 [4] S.M. He X.Q. Zeng L.M. Peng X. Gao J.F. Nie W.J. Ding J. Alloy Compd. 421 2006 309 [5] Y. Kawamura K. Hayashi A. Inoue T. Masumoto Mater. Trans. 42 2001 1172 [6] T. Itoi T. Seimiya Y. Kawamura M. Hirohashi Mater. Sci. Forum. 419–422 2003 721 [7] Y. Chino M. Mabuchi S. Hagiwara H. Iwasaki A. Yamamoto H. Tsubakino Scripta Mater. 51 2004 711 [8] K. Liu J.H. Zhang G.H. Su D.X. Tang L.L. Rokhlin F.M. Elkin J. Meng J. Alloy Compd. 481 2009 811 [9] M. Yamasaki M. Sasaki M. Nishijima K. Hiraga Y. Kawamura Acta Mater. 55 2007 6798 [10] M. Yamasaki T. Anan S. Yoshimoto Y. Kawamura Scripta Mater. 53 2005 799 [11] Y.J. Wu X.Q. Zeng D.L. Lin L.M. Peng W.J. Ding J. Alloy Compd. 477 2009 193 [12] Y.J. Wu D.L. Lin X.Q. Zeng L.M. Peng W.J. Ding J. Mater. Sci. 44 2009 1607 [13] Y. Gao Q.D. Wang J.H. Gu Y. Zhao Y. Tong D.D. Yin J. Alloy Compd. 477 2009 374 [14] T. Honma T. Ohkubo S. Kamado K. Hono Acta Mater. 55 2007 4137 [15] D.J. Li X.Q. Zeng J. Dong C.Q. Zhai W.J. Ding J. Alloy Compd. 468 2009 164 [16] X.B. Liu R.S. Chen E.H. Han J. Alloy Compd. 465 2008 232 [17] K. Yamada Y. Okubo S. Kamado Y. Kojima Adv. Mater. Res. 11–12 2006 417 [18] X.H. Liu W.L. Johnson J. Appl. Phys. 78 1995 6514 [19] V.P. Perminov Powder Metall. Met. Ceram. 6 1967 409 [20] E. Padezhnova Russ. Metall. (Engl. Transl.) 1982 1982 185 [21] A. Datta U.V. Waghmare U. Ramamurty Acta Mater. 56 2008 2531 [22] Y.M. Zhu A.J. Morton J.F. Nie Acta Mater. 58 2010 2936 [23] T. Itoi T. Seimiya Y. Kawamura M. Hirohashi Scripta Mater. 51 2004 107 [24] Y.M. Zhu M. Weyland A.J. Morton K. Oh-ishi K. Honod J.F. Nie Scripta Mater. 60 2009 980 [25] W.J. Ding Y.J. Wu L.M. Peng X.Q. Zeng G.Y. Yuan D.L. Lin J. Mater. Res. 24 2009 1842 [26] K. Liu J. Zhang L.L. Rokhlin F.M. Elkin D. Tang J. Meng Mater. Sci. Eng. A 505 2009 13
What problem does this paper attempt to address?
-
The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys
Zhibing Ding,Ruopeng Lu,Yuhong Zhao,Hua Hou,Peng Cheng,Bu Zhiqiang,Peilin Zhang
DOI: https://doi.org/10.1590/1980-5373-mr-2017-0992
2018-01-01
Abstract:The microstructure, mechanical properties and fracture behavior of as-cast Mg-10Gd-3Y-xZn-0.6Zr (x = 0, 0.5, 1 and 2 wt%) alloys have been investigated by X-ray diffraction (XRD), optical microscopy (OM), scanning electron microscopy (SEM) and tensile tests. The experimental results reveal that the microstructure of the alloy without Zn contains α-Mg and Mg24(Gd,Y)5 phase, the microstructure of the alloy with 0.5% Zn contained of α-Mg, (Mg,Zn)3(Gd,Y) and Mg24(Gd,Y,Zn)5 phase, whereas when Zn content was 1% and 2%, the Mg12(Gd,Y)Zn phase and some needle-shaped stacking faults notably appear and the Mg24(Gd,Y,Zn)5 phases completely disappear. Moreover, a new 18R long period stacking ordered (LPSO) phase is observed in grain boundaries with increasing Zn content up to 2%. The tensile tests indicate that the alloy containing 0.5% Zn shows the optimal mechanical properties and the ultimate tensile strength (UTS), yield strength (YS) and elongation are 228MPa, 172MPa and 5.1%, respectively. As indicated by fracture analyses, the fracture modes of the alloys with 0%, 1% and 2% Zn are brittleness transcrystalline fracture, and the tensile fracture mode of 0.5% Zn alloy is typical tough transgranular fracture.
-
The Effect of Morphology of the Long-Period Stacking Ordered Phase on Mechanical Properties of the Mg-7Gd-3Y-1Nd-1Zn-0.5Zr (wt.%) Alloy
M. Li,X. Wang,Q. Y. Feng,J. Wang,Z. Xu,P. H. Zhang
DOI: https://doi.org/10.1016/j.matchar.2017.01.032
IF: 4.537
2017-01-01
Materials Characterization
Abstract:The effect of morphology of the long-period stacking ordered (LPSO) phase on mechanical properties of the Mg-7Gd-3Y-1Nd-1Zn-0.5Zr (wt.%) alloy have been studied. The results reveal that the block-like 14H-LPSO phases in and near grain boundaries can be formed during heat treatment at high temperature, but low temperatures is conducive to form the needle-like 14H-LPSO phases within α-Mg grains. During heat treatment at fixed temperature for different time, the preferential nucleation sites of the 14H-LPSO phases are located in grain boundaries, then the14H-LPSO phases grow into the α-Mg matrix in the form of needle-like, the needle-like 14H-LPSO phases gradually decrease its length after growing a certain stage, at last the needle-like 14H-LPSO phases disappear completely. The decomposition of the block-like 14H-LPSO phases is found during furnace cooling after homogenization. After decomposition of the block-like 14H-LPSO phases, the rapid diffusion of Zn atoms into α-Mg matrix leads to form the needle-like 14H-LPSO phases within α-Mg matrix, but the retention of RE atoms in grain boundaries results in forming the Mg-RE particles. After extrusion and subsequent ageing, it is found that the alloy with the needle-like 14H-LPSO phases exhibit superior elongation than the alloy without the needle-like 14H-LPSO phase. The precipitates of peak-aged alloys are studied by TEM. The <112−0>α demonstrates that the stacking faults can be observed, the serious lattice distortion appears near the stacking fault. The [0001] zone axis shows that the β′ and a new rod phase are found, and the enrichment of RE atoms are detected in the two phase by HADDF-STEM. It seems to be that the rod phase can be subdivided into a plurality of mutually parallel structure unit.
-
Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy
Cong Dang,Xiaoxu Dou,Jingfeng Wang,Di Yu,Jinxing Wang,Ruopeng Lu,Hua Hou,Yuhong Zhao
DOI: https://doi.org/10.1016/j.jmrt.2023.04.089
IF: 6.267
2023-01-01
Journal of Materials Research and Technology
Abstract:Different solution treatments were carried out on the semi-continuously cast Mg-9.55Gd-2.27Y-1.28Zn-0.55Zr-0.11Nd (wt.%) alloy at temperatures of 480 °C, 500 °C, and 520 °C. It was found that the different solution treatment temperatures led to different phase constitutions of the alloy. The Mg3RE-type eutectic phases transform into long period stacking order (LPSO) phases with various morphologies after solution treatment. Increasing the solution temperature resulted in larger grain size, greater number of lamellar LPSO phases, and segregation of Zr element. Block LPSO phases also shifted to rod LPSO phase. After ageing treatment, the special spatial structure consisting of prismatic β′ precipitates, basal γ′ precipitates, and lamellar LPSO phases hindered dislocation movement effectively, leading to high strength. However, the accumulation of massive dislocations promoted the premature formation of cracks at the grain boundary and LPSO/Mg matrix interface, resulting in a rapid decrease in ductility of the alloy. After solution treatment at 480 °C for 12 h and aged at 200 °C for 48 h, the Mg-9.55Gd-2.27Y-1.28Zn-0.55Zr-0.11Nd alloy exhibited favorable comprehensive mechanical properties at room temperature: ultimate tensile strength (UTS) of 383 MPa, tensile yield strength (TYS) of 269 MPa, and fracture elongation (EL) of 5.1%.
-
Microstructure Evolution and Mechanical Properties of Mg-7Gd-3Y-1Nd-2Zn-0.5Zr Alloy During Two-Step Homogenization Heat Treatment
Ting Li,Zhi Wei Du,Wei Liu,Jia Wei Yuan,Kui Zhang,Dong Jie Chen,Sheng Nan Zhou
DOI: https://doi.org/10.4028/www.scientific.net/msf.950.15
2019-01-01
Materials Science Forum
Abstract:This paper proposes a two-step homogenization heat treatment to dissolve the eutectic structure and long period stacking ordered phase (LPSO) formed during solidification into the α-Mg matrix. The microstructure evolution and mechanical properties of Mg–7Gd–3Y–1Nd–2Zn–0.5Zr alloy during the two-step homogenization heat treatment have been investigated systemically. The results reveal that as-cast alloy is composed mainly of α-Mg, (Mg,Zn)3RE, eutectic phase, stacking fault, block-like LPSO phase and square-shaped compounds rich in RE. The HRTEM results suggest that the block-like long period stacking ordered phase in as-cast alloy is 14H-type rather than 18R structure, and the stacking sequences of the 14H-LPSO phase are ABABACBCBCBCAB. After the first step homogenization of 520°C for 48 h, the eutectic structure has dissolved into the matrix, whereas the 14H-LPSO phase remains in the alloy. To further dissolve the LPSO phase into matrix, the second step homogenization of 540°C for 24h was adopted. After the second-step of homogenization, the residual 14H-LPSO phase has dissolved into the matrix totally. The as-homogenized alloy is composed mainly of α-Mg and square-shaped compounds rich in RE. The tensile tests at room temperature (RT) exhibit that the ultimate tensile strength (UTS), yield strength (YS) and elongation of as-cast alloy are 172 MPa, 128MPa and 2.8%, whereas the UTS, YS and elongation of as-homogenized alloy are 253 MPa, 185 MPa and 8.4, respectively.
-
Effect of Zn/(Gd+Y) ratio on the microstructure evolution and mechanical properties of Mg-Gd-Y-Zn-Zr alloy
Xiaoxiao Wei,Li Jin,Shuai Dong,Fenghua Wang,Jie Dong
DOI: https://doi.org/10.1016/j.matchar.2020.110670
IF: 4.537
2020-11-01
Materials Characterization
Abstract:<p>In Mg-Gd-Y-Zn-Zr alloy, the ratio of Zn/(Gd+Y) has a significant influence on the structure and distribution of second phases, which further affects the properties of the alloy. Here we regulated the feature of second phases through altering the Zn/(Gd+Y) ratio with 0.14, 0.21 and 0.25, and analyzed the effects of the Zn/(Gd+Y) ratio on microstructure evolution and mechanical properties of these alloys. The extruded alloys all present bimodal structure, which including the fine grain with diameters below 3 μm and coarse grain with diameters more than 3 μm, and the alloy with Zn/(Gd+Y) ratio of 0.21 shows highest area fraction of fine grain. The sample with Zn/(Gd+Y) ratio of 0.25 shows numerous large block-shaped LPSO phases, while the LPSO phases in the alloys with Zn/(Gd+Y) ratio of 0.14 and 0.21 are much finer. For the alloy with Zn/(Gd+Y) ratio of 0.21, lamellar LPSO phases/SFs exist in the matrix, and some atom clusters exist as well. Extruded alloy with Zn/(Gd+Y) ratio of 0.21 possesses excellent ductility as well as a clear yield drop compared with alloys with higher (0.25) or lower (0.14) Zn/(Gd+Y) ratio. The higher area fraction of fine grain and fine LPSO phases ensure excellent ductility, and the significant solute-dislocation interaction is responsible for a clear yield drop.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing
-
Dissolution and Reprecipitation of 14H-LPSO Structure Accompanied by Dynamic Recrystallization in Hot-Extruded Mg89Y4Zn2Li5 Alloy
Wei Liu,Yu Su,Yuntao Zhang,Liwen Chen,Hua Hou,Yuhong Zhao
DOI: https://doi.org/10.1016/j.jma.2022.03.018
IF: 11.813
2022-01-01
Journal of Magnesium and Alloys
Abstract:We investigate the variation induced in long-period stacking ordered（LPSO） structures, dynamic recrystallization（DRX）, and mechanical performance of hot-extruded Mg 89 Y 4 Zn 2 Li 5 alloys fabricated at different extrusion speeds（Ve= 0.4, 0.8, 1.0, 1.2 mm/s） and die angles（α = 30°, 60°, 90°） under 400 °C, the dissolution and reprecipitation of 14H LPSO structure accompanied by DRX process are then clarified in detail. Upon all extrusion conditions, the block 18R LPSO structures elongate in the extrusion direction, while the lamellar 14H LPSO structures dissolve under the deformation strain. In addition, due to discontinuous and continuous DRX mechanisms, all hot-extruded alloys have a full DRX microstructure consisting of equiaxed recrystallized grains, but the DRX grain size reduces when both extrusion speed and die angle decrease. Note that, in the interior of DRX grains, thin LPSO lamellae mixing 14H, 18R and 24R structures nucleate and dynamically precipitate due to the dissolution of the original lamellar 14H LPSO structures. Furthermore, the hot-extruded Mg 89 Y 4 Zn 2 Li 5 alloy becomes stronger as decreasing of the extrusion speed and die angle, whereas the ductility remains nearly constant. Finally, the hotextruded Mg 89 Y 4 Zn 2 Li 5 alloy achieves an excellent strength-ductility balance at a relatively low extrusion speed（0.4 mm/s） and small die angle（30°） mainly due to the elongated 18R LPSO structure, fine and full DRX microstructure, thin mixed LPSO precipitates in the DRX grains, twins and dislocations.
-
Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy
Zijian Yu,Linlin Liu,Adil Mansoor,Ke Liu,Shubo Li,Wenbo Du
DOI: https://doi.org/10.1016/j.jallcom.2021.158826
IF: 6.2
2021-05-01
Journal of Alloys and Compounds
Abstract:<p>In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg<sub>3</sub>RE phase variants, which are bulk Mg<sub>3</sub>RE phase with a size range of 10–30 µm, spot Mg<sub>3</sub>RE phase with a size range of 1–2 µm and spherical Mg<sub>3</sub>RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg<sub>3</sub>RE phase has a strong dispersion strengthening effect, while the bulk Mg<sub>3</sub>RE phase acts as crack resources and deteriorates the ductility. A novel island-like <span class="math"><math>β1R</math></span> phase (FCC, <em>a</em> = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <span class="math"><math>(1̅12)β1R</math></span>//<span class="math"><math>(101̅0)α</math></span> interface at the broad facet and a semi-coherent <span class="math"><math>(1̅11)β1R</math></span>//<span class="math"><math>(112̅0)α</math></span> interface at the end facet. The <span class="math"><math>β1R</math></span> phase transforms from <span class="math"><math>βH</math></span> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <span class="math"><math>β1R</math></span> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <span class="math"><math>β1R</math></span> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg<sub>3</sub>RE phase variants, and <span class="math"><math>β1R</math></span> phase.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
-
Study on phase constitutions, growth pattern and mechanical properties of Mg-1.4Gd-1.2Y-xZn-0.15Zr (at%) alloys
Dongjie Chen,Yongjun Li,Kui Zhang,Xinggang Li,Minglong Ma,Guoliang Shi,Jiawei Yuan,Ting Li
DOI: https://doi.org/10.1016/j.jre.2019.12.019
IF: 4.632
2020-01-01
Journal of Rare Earths
Abstract:The effects of minor Zn (0.2 at%, 0.4 at%, 0.6 at%) on the microstructures and mechanical properties of Mg-1.4Gd-1.2Y-0.15Zr (at%) alloys were systematically explored. Results reveal that increasing Zn content leads to the increase of the intergranular phases and the change of their composition from Mg24(Gd,Y)5 phase and (Mg,Zn)3(Gd,Y) phase to 18R-LPSO phase and (Mg,Zn)3(Gd,Y) phase. Mg24(Gd,Y)5 phase is body-centered cubic structure and shares the same lattice constant with Mg24Y5 while (Mg,Zn)3(Gd,Y) phase is face-centered cubic structure with lattice constant of 0.72 nm, slightly lower than Mg3Gd. 18R-LPSO structure is identified to be monoclinic with c-axis not strictly vertical to the bottom surface but 93.5°. The growth patterns of intergranular phases change from the divorced growth to coupled growth as compositions change. Moreover, the mechanical performance improves with Zn rising, ascribed to the decrease of brittle phases at grain boundaries and the increase of LPSO structure phases.
-
Effects of an LPSO Phase Induced by Zn Addition on the High-Temperature Properties of Mg-9Gd-2Nd-(1.5Zn)-0.5Zr Alloy
Ming Li,Mengling Yao,Liangzhi Liu,Xiaoxia Zhang,Zhihui Xing,Xiangsheng Xia,Peng Liu,Yuanyuan Wan,Qiang Chen,Hongxia Wang
DOI: https://doi.org/10.3390/ma17164075
2024-08-16
Abstract:In this study, we prepared Mg-9Gd-2Nd-0.5Zr, referred to as alloy I, and Mg-9Gd-2Nd-1.5Zn-0.5Zr, referred to as alloy II. The effects of a long-period stacking ordered (LPSO) phase induced by Zn addition on the high-temperature mechanical properties and fracture morphology of alloy I and alloy II at different temperatures (25 °C, 200 °C, 225 °C, and 250 °C) were studied using optical microscopy (OM), scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS), electron backscatter diffraction (EBSD), and transmission electron microscopy (TEM). The results indicate that Mg5RE at the crystal boundary of the as-cast alloy I transformed into (MgZn)3RE (as-cast alloy II) by the addition of Zn. After solid solution treatment, the secondary phase in alloy I completely disappeared, and there were still residual secondary phases in block-like and needle-like structures in alloy II, while layered LPSO phases precipitated in the matrix. During the high-temperature tensile test, the yield and tensile strength of alloy I decreased significantly with the increase in temperature, while the elongation increased. Compared to alloy I, the yield strength of alloy II with an LPSO phase showed an increasing trend at 25 °C~200 °C and then decreased when the temperature reached around 250 °C. The thermal stability was significantly enhanced, and the elongation was also higher than that of alloy I. As the temperature increased, the fracture surface of alloy I showed increased folding, bending of scratches, and crack enlargement. However, the fracture surface of alloy II remained largely unchanged, with only minor wrinkles and cracks appearing at temperatures reaching 250 °C.
-
Microstructure of as-cast Mg-4.2Zn-0.8Y (at.%) alloys containing Gd
J Wu,Y L Chiu,I P Jones
DOI: https://doi.org/10.1088/1742-6596/522/1/012033
2014-06-11
Journal of Physics: Conference Series
Abstract:Mg-Zn-Y is a high performance magnesium ternary alloy with high specific strength. A second rare earth element Gd with different content was added into Mg-4.2Zn-0.8Y (at.%) alloys to investigate the effect of Gd addition on the microstructure and mechanical properties. In the as cast alloys, the following phases have been identified: in the Gd-free alloy, an H phase (hcp, a=0.918nm, c=0.95nm), W phase (fcc, a=0.682nm) and icosahedral quasicrystalline phases (i-phase). With 0.5at.% Gd and 1 at.% Gd, W phase, long-period stacking ordered phase (LPSO phase) and i-phase were observed. The coexistence of i-phase and LPSO phase was observed after Gd addition. As the content of Gd increased, the grain size decreased, the volume fractions of second phases increased, and the hardness of the as-cast alloys increased.
-
Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys
Wang Jun,Zhu Xiurong,Wang Rong,Xu Yongdong,Nie Jingjiang,Ling Guoping
DOI: https://doi.org/10.1016/s1002-0721(10)60478-4
IF: 4.632
2011-01-01
Journal of Rare Earths
Abstract:Age hardening, microstructure and mechanical properties of Mg-xY-1.5MM-0.4Zr (x=0, 2, 4, 6 wt.%) alloys (MM represents Ce-based misch-metal) were investigated by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results showed that the formed precipitates being responsible for age hardening changed from fine hexagonal-shaped equilibrium Mg12MM phase to metastable β′ phase with bco crystal structure when Y was added into Mg-1.5MM-0.4Zr alloy, and the volume fraction of precipitate phases also increased. With the increase of Y content in Mg-Y-1.5MM- 0.4Zr alloys, it was found that the age hardening was enhanced, the grain sizes became finer and the tensile strength was improved. The cubic-shaped β-Mg24Y5 precipitate phases were observed at grain boundaries in Mg-6Y-1.5MM-0.4Zr alloy. It was suggested that the distribution of prismatic shaped β′ phases and cubic shaped β-Mg24Y5 precipitate phases in Mg matrix might account for the remarkable enhancement of tensile strength of Mg-Y-MM-Zr alloy. It was shown that the Mg-6Y-1.5MM-0.4Zr alloy was with maximum tensile strength at aged-peak hardness, UTS of 280 MPa at room temperature and 223 MPa at 250°C, respectively.
-
Microstructure and mechanical properties of the Mg98.5Zn0.5RE1 (RE=Gd and/or Y) alloys processed by equal channel angular pressing
Xiaojie Zhou,Zihang Guo,Yu Tu,Yi Wang,Jian Zhang,Gang Zeng,Xianzheng Lu,Xiaomin Chen,Yaru Liu
DOI: https://doi.org/10.1016/j.jmrt.2023.08.294
IF: 6.267
2023-09-01
Journal of Materials Research and Technology
Abstract:In this work, Mg98.5Zn0.5RE1 (RE = Gd and/or Y) and Mg97Zn1Y2 (at%) alloys were subjected to homogenization and equal channel angular pressing (ECAP) to systematically compare the microstructure evolution and mechanical properties. The results indicate that, instead of the lamellar LPSO phases in the as-cast Mg-Zn-Y series alloys, the β-Mg5(Gd, Zn) phases appear in the as-cast Mg98.5Zn0.5Gd1 alloy which tend to be dissolved during homogenization. The furnace cooling after homogenization promotes the precipitation of numerous lamellar LPSO phases in all the studied alloys which inhibit the DRX behavior but facilitate the operation of kinking deformation during ECAP for the Mg98.5Zn0.5RE1 alloys, especially the Mg98.5Zn0.5Gd1 one. After the 5p-ECAP process at 350 °C, the larger density of kink bands, more LAGBs (low-angle grain boundaries) and lower SF B (Schmid factor for basal slip) combine to endow the Mg98.5Zn0.5Gd1 alloy with the higher strength-ductility synergy, exhibiting the tensile yield strength (TYS) of 214 MPa and elongation of 9.6%. The Mg97Zn1Y2 alloy with the larger volume fraction of interdendritic LPSO phases and dynamically recrystallized (DRXed) regions exhibits the superior ultimate tensile strength (UTS) of 277 MPa and moderate elongation of 7.2%.
materials science, multidisciplinary,metallurgy & metallurgical engineering
-
Deformation-induced Dynamic Precipitation of 14H-LPSO Structure and Its Effect on Dynamic Recrystallization in Hot-Extruded Mg-Y-Zn Alloys
Wei Liu,Yuhong Zhao,Yuntao Zhang,Chuan Shuai,Liwen Chen,Zhiquan Huang,Hua Hou
DOI: https://doi.org/10.1016/j.ijplas.2023.103573
IF: 8.5
2023-01-01
International Journal of Plasticity
Abstract:Understanding dynamic precipitation in thermo-mechanical processing can shed light on the manufacturing of high-performance Mg-based alloys. This study investigates the dynamic pre-cipitation of long-period stacking order (LPSO) phase with 14H structure and its effect on dy-namic recrystallization (DRX) in the hot-extruded Mg98.5Y1Zn0.5, Mg97Y2Zn1 and Mg94Y4Zn2 (at. %) alloys. First, the simultaneous increase of Y and Zn atoms not only promotes the formation of interdendritic block 18R-LPSO phases during solidification but also facilitates the dynamic pre-cipitation of intragranular lamellar and thin 14H-LPSO phases in coarse non-DRX and fine DRX grains, respectively, during hot extrusion. Second, the increased block 18R volume fraction and lamellar 14H number density significantly delays DRX. However, as the deformation strain in-creases, broken 18R fragments accelerate the DRX particle-stimulated nucleation (PSN) mecha-nism and fluctuant alpha-Mg/18R interfaces initiate the discontinuous DRX mechanism. In particular, the deformation kinking and dissolving of lamellar 14H activate the continuous DRX mechanism. Finally, the mechanical strength increases but ductility decreases with increasing the content of Y and Zn atoms for the hot-extruded Mg-Y-Zn alloys. The high strength of the hot-extruded Mg94Y4Zn2 alloy is attributed to fine DRX grain size, strong un-DRX grains, major block 18R and lamellar/thin 14H phases, and deformation kinking, while the high ductility of the hot -extruded Mg98.5Y1Zn0.5 alloy is responsible for large DRX volume fraction, high activity of deformation twins, and easy mobility of basal slip.
-
Evolution of precipitates in Mg?7Gd?3Y?1Nd?1Zn?0.5Zr alloy with fine plate -like 14H-LPSO structures aged at 240?C
Yong-gang Peng,Zhi-wei Du,Wei Liu,Yong-jun Li,Ting Li,Xiao-lei Han,Ming-long Ma,Zheng Pang,Jia-wei Yuan,Guo-liang Shi
DOI: https://doi.org/10.1016/S1003-6326(20)65314-6
IF: 3.752
2020-01-01
Transactions of Nonferrous Metals Society of China
Abstract:Abstract The morphology and crystal structure of the precipitates in Mg−7Gd−3Y−1Nd−1Zn−0.5Zr (wt.%) alloy with fine plate-like 14H-LPSO structures aged at 240 °C were investigated using transmission electron microscopy (TEM) and high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM). Fine plate-like 14H-LPSO structures precipitate after heat treatment at 500 °C for 2 h, and β-type phases precipitate after the alloy is aged at 240 °C. The long-period atomic stacking sequence of 14H-LPSO structures along the [0001]α direction is ABABCACACACBABA. After being aged at 240 °C for 2 h, the β-type phases are the ordered solution clusters, zig-zag GP zones, and a small number of β′ phases. The peak hardness is obtained at 240 °C for 18 h with a Brinell hardness of 112, the β-type phases are β’ phases and local RE-rich structures. After being aged at 240 °C for 100 h, the β-type phases are β’, β1 and β’F phases. β′ phases nucleate from the zig-zag GP zones directly without β″ phases, and then transform into β1 phase by β’→β’F→β1 transformations. The Zn not only can form LPSO structure, but also is the constituent element of β1 phases. LPSO structures have a certain hindrance to the coarsening of β’ and β1 along 〈0001〉α.
-
Microstructure Evolution and Mechanical Properties of Mg-7Gd-3Y-1Nd-1Zn-0.5Zr Alloy
Meng Li,Kui Zhang,Zhi-wei Du,Xing-gang Li,Ming-long Ma
DOI: https://doi.org/10.1016/s1003-6326(16)64230-9
IF: 3.752
2016-01-01
Transactions of Nonferrous Metals Society of China
Abstract:X-ray diffraction (XRD), optical microscopy (OM), scanning electronic microscopy (SEM), transmission electron microscopy (TEM) and tensile tests at room temperature (RT) were performed to investigate the effect of homogenization on microstructure evolution and mechanical properties of Mg-7Gd-3Y-1Nd-1Zn-0.5Zr (mass fraction, %) alloy. The results indicate that the microstructure of the as-cast alloy is composed of α-Mg, (Mg, Zn)3RE phase and stacking fault (SF), the homogenization results in the disappearance of (Mg, Zn)3RE phase and stacking fault (SF) as well as the emergence of 14H-type long-period stacking ordered (LPSO) phase. The ultimate tensile strength (UTS), yield strength (YS) and elongation of the as-cast alloy are 187 MPa, 143 MPa and 3.1%, and the UTS, YS and elongation of the as-homogenized alloy are 229 MPa, 132 MPa and 7.2%, respectively.
-
Microstructures and Mechanical Properties of the Mg–4.5Zn–xGd (x = 0, 2, 3 and 5) Alloys
Jie Yang,Lidong Wang,Limin Wang,Hongjie Zhang
DOI: https://doi.org/10.1016/j.jallcom.2007.05.044
IF: 6.2
2008-01-01
Journal of Alloys and Compounds
Abstract:Microstructures and mechanical properties of the peak-aged Mg–4.5Zn–xGd (x=0, 2, 3 and 5wt.%) alloys have been investigated. The results showed that grain size increased with increasing Gd. Phase analysis showed that MgZn2 phase was observed in the Mg–4.5Zn alloy. While with Gd additions, Mg3Gd and Mg3Gd2Zn3 phases formed, and the volume fraction of the Mg3Gd2Zn3 phase increased with increasing Gd. Tensile test results indicated that the optimal mechanical properties were obtained in the Mg–4.5Zn–2Gd alloy, and the ultimate tensile strength and yield strength were 215MPa and 121MPa, respectively. However, the strength decreased with increasing Gd, which was mainly due to the increasing volume fraction of the Mg3Gd2Zn3 phase.
-
Hot Compression Behavior of Mg–Gd–Y–Zn–Zr Alloy Containing LPSO with Different Morphologies
Rui Guo,Xi Zhao,Bo-Wen Hu,Xue-Dong Tian,Qiang Wang,Zhi-Min Zhang,Zhao, Xi
DOI: https://doi.org/10.1007/s40195-023-01587-8
2023-07-25
Acta Metallurgica Sinica (English Letters)
Abstract:In this study, hot compression behavior of as-homogenized Mg-9Gd-4Y-2Zn-0.5Zr alloys containing long period ordered (LPSO) phases with different initial morphologies was investigated under a strain rate of 0.01 s −1 at 450 °C. The microstructure, texture evolution and dynamic recrystallization (DRX) mechanism under different strains (0.1, 0.3, 0.5, 0.7, and 1.4) were studied. Under compression conditions, the block-shape phase and deformed α -Mg matrix were regularly arranged vertically in the compression direction (CD). The particle phase (Mg 5 RE) and amount of kink bands were produced. The degree of kink increased initially and decreased significantly when the deformation strain reached 1.4. Three DRX mechanisms were produced during the compression process: (i) The block LPSO, Mg5RE and Zr–Zn phase activated DRX through the particle stimulated nucleation (PSN) mechanism. (ii) Several DRX activated on the serrated grain boundary between the two parent grains through discontinuous DRX (DDRX) mechanism. (iii) A large number of kink bands and larger spacing of lamellar LPSO increased the nucleation of DRX through continuous DRX (CDRX) mechanism. The combination of different recrystallization mechanisms has evident effects on grain refinement. DRX increased as compression proceeds, and the texture was gradually weakened.
metallurgy & metallurgical engineering
-
Evolution of Deformation Substructure and MgxZnyCaz Metastable Phase in Fine-Grained Mg Alloys
Zhen-Liang Li,Xin-Lei Zhang
DOI: https://doi.org/10.1007/s40195-024-01775-0
2024-10-06
Acta Metallurgica Sinica (English Letters)
Abstract:The spray-deposition was used to produce billets of Mg-4Al-1.5Zn-3Ca-1Nd (A alloy) and Mg-13Al-3Zn-3Ca-1Nd (B alloy), and evolution of deformation substructure and Mg x Zn y Ca z metastable phase in fine-grained (3 μm) Mg alloys was investigated by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), and electron backscattered diffraction (EBSD). It was found that different dislocation configurations were formed in A and B alloys. Redundant free dislocations (RFDs) and dislocation tangles were the ways to form deformation substructure in A alloy, no RFDs except dislocation tangles were found in B alloy. The interaction between nano-scale second phase particles (nano-scale C15 and β-Mg 17 (Al, Zn) 12 phase) and different dislocation configurations had a significant effect on the deformation substructures formation. The mass transfer of Mg x Zn y Ca z metastable phases and the stacking order of stacking faults were conducive to the Mg-Nd-Zn typed long period stacking ordered (LPSO) phases formation. Nano-scale C15 phases, Mg-Nd-Zn typed LPSO phases, c / a ratio, β-Mg 17 (Al, Zn) 12 phases were the key factors influencing the formation of textures. Different textures and grain boundary features (GB features) had a significant effect on k -value. The non-basal textures were the main factor affecting k -value in A alloy, while the high-angle grain boundary (HAGB) was the main factor affecting k -value in B alloy.
metallurgy & metallurgical engineering
-
Evolutions of Microstructure and Mechanical Properties in Mg–5Li–1Zn–0.5Ag–0.5Zr–xGd Alloy
Bing-Yu Qian,Rui-Zhi Wu,Jian-Feng Sun,Jing-Huai Zhang,Le-Gan Hou,Xiao-Chun Ma,Jia-Hao Wang,Hai-Ting Hu
DOI: https://doi.org/10.1007/s40195-022-01509-0
2023-01-07
Acta Metallurgica Sinica (English Letters)
Abstract:The evolution of the microstructure and mechanical properties of alloy system with nominally composition Mg–5Li–1Zn–0.5Ag–0.5Zr– x Gd ( x = 0, 1.2, 2.4, 3.6, 4.8, 6) is evaluated based on computational phase diagram and corresponding experimental studies. The results show that grains are significantly refined with the increase of Gd content. The main phases of as-cast alloys are α -Mg, β -Li, AgLi 2 Mg, and Mg 3 Gd. With the increase of Gd content, the amounts of Mg 3 Gd phase and β -Li phase have been increased. When the Gd content exceeds 3.6 wt%, Mg 3 Gd phase precipitates in a form of the network at the grain boundaries. The precipitation of β -Li can be attributed to the competitive dissolution of Zn, Gd, and Li in Mg. Meanwhile, γ ′′ is formed after the addition of Gd, which grows and transforms into γ ′ with the increase of Gd content. In solidification process, stacking faults are formed by solid transformation of partial α -Mg and Mg 3 Gd. Eventually, with the synergistic effect of Mg 3 Gd, β -Li, and γ ′′ (or γ ′), as the Gd content increasing, the tensile strength of the alloy first increases, then decreases, and the elongation decreases. When the content of Gd is 4.8 wt%, the ultimate tensile strength and yield strength reach the maximum values of 227 MPa and 139 MPa, and the elongation is 18.1%, respectively.
-
High-strength Mg‐10Gd‐3Y‐1Zn‐0.5Zr alloy fabricated by wire-arc directed energy deposition: Phase transformation behavior and mechanical properties
Qianhui Cao,Caiyou Zeng,Xinyi Cai,Ruize Zhang,Fude Wang,Haibo Wang,Yu Zhang,Bojin Qi,Baoqiang Cong
DOI: https://doi.org/10.1016/j.addma.2023.103789
IF: 11
2023-09-19
Additive Manufacturing
Abstract:Magnesium rare-earth (Mg-RE) alloys have great potential in lightweight applications because of the high specific strength. Wire-arc directed energy deposition (WA-DED) exhibits great prospects for the fabrication of large-scale monolithic structural components with high manufacturing flexibility. In this work, a single-pass multilayer Mg‐10Gd‐3Y‐1Zn‐0.5Zr (wt%, GWZ1031K) deposit was prepared via WA-DED. Electron backscatter diffraction (EBSD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM) are conducted to systematically explore the microstructural evolution during the WA-DED process and the subsequent heat treatment . The GWZ1031K alloy deposit fabricated by WA-DED exhibits uniform equiaxed grain structure whose average grain size is 22.3 ± 5.6 μm. The (Mg,Zn) 3 (Gd,Y) phase and RE segregation can be observed along the α-Mg grain boundaries (GBs). A number of needle-like γ ́ /γ ́ ́ phases embedded in the α-Mg grain interior (GI). In addition, there is a small number of fine RE-rich cubic phase and (Gd,Y) 2 O 3 particles. The deposit shows significantly enhanced ductility and slightly improved strength after solution treated at 500 °C for 12 h. After the solution treatment, the intergranular (Mg,Zn) 3 (Gd,Y) eutectics dissolve into the matrix and long period stacking ordered (LPSO) phases precipitate from the GBs into the GI, contributing to the enhancement in ductility. Besides, the LPSO phase along with the existing RE-rich cubic phase, (Gd,Y) 2 O 3 and Zr particles at GBs also play a role in hindering grain growth. The high-density nanoscale β ́ phases appear in the GI after aging treated at 200 °C for 24 h, resulting in the remarkable precipitation strengthening. In comparison with the solution-treated GWZ1031K deposit, the aging-treated exhibits a prominently improved ultimate tensile strength of 337 ± 7 MPa in the building direction (BD) and 331 ± 5 MPa in the travelling direction (TD). It is envisaged that the WA-DED manufacturing method will provide a simple and effective route to fabricate large-scale Mg-RE alloy components for various applications.
engineering, manufacturing,materials science, multidisciplinary