Hydrothermal-hydrolysis Synthesis and Photocatalytic Properties of Nano-Tio2 with an Adjustable Crystalline Structure.

Jinghuan Zhang,Xin Xiao,Junmin Nan
DOI: https://doi.org/10.1016/j.jhazmat.2009.11.074
IF: 13.6
2009-01-01
Journal of Hazardous Materials
Abstract:Tri-phase (anatase, rutile, and brookite), bi-phase (anatase and rutile), and mono-phase (rutile) TiO(2) nanomaterials with different morphologies were successively synthesized using a hydrothermal-hydrolysis method and adjusting the Ti(4+)/Ti(3+) molar ratio in a precursor solution. The properties of the fabricated nanomaterials were characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), photocatalytic reaction, and other techniques. It has been shown that TiO(2) nanorods can be obtained by increasing the Ti(4+)/Ti(3+) molar ratio in a precursor solution from 1:0 to 0.3:0.7. TiO(2) nanoparticles are formed if the Ti(3+) fraction in the solution is further increased. The selective synthesis of TiO(2) nanomaterials is explained by a decrease in the reaction rate and by changes in acidity with increasing Ti(3+) content. The tri-phase nanorods and bi-phase nanoparticles synthesized with Ti(4+)/Ti(3+) molar ratios from 1:0 to 0.8:0.2 and 0.2:0.8 to 0:1, respectively, have a higher degradation ability with respect to methylene blue aqueous solutions under UV irradiation at ambient temperature compared to purely rutile TiO(2) nanorods synthesized with Ti(4+)/Ti(3+) molar ratios from 0.7:0.3 to 0.3:0.7. The high photocatalytic activity of the multi-phase TiO(2) samples is primarily attributed to their larger band gap and suppressed recombination of photo-generated electron-hole pairs.
What problem does this paper attempt to address?