Abstract:Pure molybdenum (PM) and La2O3 dispersion strengthened Mo alloy (ODS-Mo) were prepared by powder metallurgy through two different mixing method (solid-solid or SS mixing and solid-liquid or SL mixing). After annealed at 1050°C for 1h, the PM, SS-Mo and SL-Mo were compared in microstructure and mechanical properties. The microstructural examinations showed that the PM was mostly recrystallized with rather coarse grains, but the ODS-Mo alloys remained fine elongated grains. This discrepancy is due to a higher recrystallization temperature held in the ODS-Mo alloys. The uniaxial testing results showed that the ODS-Mo had higher tensile mechanical properties compared to the PM, which are attributed to the remarkable strengthening and ductilizing effect induced by the La2O3 particles. The low cycle fatigue (LCF) testing results revealed that the PM experienced cyclic hardening behaviors, while the ODS-Mo alloys exhibited cyclic softening behaviors. The Basquin-Manson-Coffin analyses results demonstrated that the ODS-Mo possessed a higher fatigue ductility and longer fatigue life than the PM. Two kinds of cracks, i.e., cleavage cracks and intergranular cracks, were experimentally observed to coexist on the fracture surface. In particular in the SL-Mo alloy, the two crack interacted and propagated forward until final fracture, leading to a step-like crack growth path and concomitantly enhanced fatigue ductility. In addition, different cycling dislocation structures were revealed between the PM and ODS-Mo alloys. Cycle fatigue mechanisms responsible for the fatigue behaviors and microstructure evolution during LCF testing were discussed. The best LCF resistance combined with superior uniaxial tensile mechanical properties found in the SL-Mo alloy were rationalized.

Tem in Situ Observation of Crack Propagation in Lanthanum Oxide Dispersion Strengthened Molybdenum Alloy

Microstructure, Compressive Performance and Wear Resistance of Pure Molybdenum Additively Manufactured Via Laser Powder Bed Fusion

Microstructure and Strengthening Mechanism of Oxide Lanthanum Dispersion Strengthened Molybdenum Alloy

New Insights of the Microcrack Initiation Induced by Mo Addition in Ni-based Single Crystal Superalloys During Creep at 900 °C

In Situ SEM Observation of Microscale Strain Fields Around a Crack Tip in Polycrystalline Molybdenum

INFLUENCE OF DOPING WAYS ON FRACTURE TOUGHNESS OF Mo-La2 O3 ALLOYS AND DOPED PARTICLES’ MICROSTRUCTURE

Coupling Effect of Intergranular and Intragranular Particles on Ductile Fracture of Mo–La2O3 Alloys

Microstructure and Tensile Properties of Oxide Dispersion Strengthened Molybdenum Alloys Prepared by Different Doping Process

In Situ TEM Observation of Crack Propagation in LiTaO3 Particle Toughened Al2O3 Ceramics

Influences of Doping Methods on Microstructure and Fracture Toughness of Mo-La Alloys

Low Cycle Fatigue Behaviors of Pure Mo and Mo-La2O3 Alloys

SEM in-situ observation on microfracture of pure Mo

In-Situ Straining Observation On Crack Initiation And Growth In An Intermetallic Al67mn8ti25 Alloy

In situ observation of intergranular fracture propagation in nanocrystalline freestanding ultrathin tungsten film

Uncovering the Weakening Mechanism of Electron Beam Welded Joints of La2O3 Dispersion Strengthened Molybdenum Alloy: Experiment and Simulation

Strengthening and Elongation Mechanism of Lanthanum-doped Titanium-Zirconium-Molybdenum Alloy

Microstructure and Mechanical Properties of Molybdenum Alloy Strengthened by Lanthanum Oxide and Silicon

Effects of doping methods on microstructure and mechanical properties of Mo-La2O3

INTERACTIONS BETWEEN La2O3 PARTICLES AND DISLOCATIONS IN Mo-La2O3 ALLOYS

Microstructure and Mechanical Properties of Multi-Components Rare Earth Oxide-Doped Molybdenum Alloys

Crack Initiation Mechanism in Lanthanum-Doped Titanium-Zirconium-molybdenum Alloy During Sintering and Rolling