Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Low Cycle Fatigue Behaviors of Pure Mo and Mo-La2O3 Alloys

Microstructure, Compressive Performance and Wear Resistance of Pure Molybdenum Additively Manufactured Via Laser Powder Bed Fusion

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Strain Ratio Effects on Low-Cycle Fatigue Behavior and Deformation Microstructure of 2124-T851 Aluminum Alloy

Evaluating low cycle fatigue property of nanoscale ZrO2 particles strengthening molybdenum alloy

Effect of zirconia on low cycle fatigue and energy absorption of molybdenum alloy

Low cycle fatigue response and fracture mechanism in a novel Al-3.5Si-0.5Mg-0.4Cu casting alloy

Deformation Mechanisms of Selective Laser Melted 316l Austenitic Stainless Steel in High Temperature Low Cycle Fatigue

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Preparation of nanostructural oxide dispersion strengthened (ODS) Mo alloy by mechanical alloying and spark plasma sintering, and its characterization

Microstructure and compression properties of fine Al2O3 particles dispersion strengthened molybdenum alloy

Anisotropic Low Cycle Behavior of the Extruded 7075 Al Alloy

Effect of Post-Heat Treatment Cooling Conditions on Microstructures and Fatigue Properties of Cobalt Chromium Molybdenum Alloy Fabricated through Selective Laser Melting

Unveiling the Mo effect on the microstructural stability of L1 2 -strengthened chemically complex alloys

Low-cycle fatigue of MCrAlY-coated superalloys: a fracture mechanics-based analysis

Nano Mo–La–O particles strengthened Mo alloys fabricated via freeze-drying technology and low temperature sintering

High Temperature Low-Cycle Fatigue, Deformation Microstructure and Final Fracture Behavior of a Nickel-Base Superalloy

The Origin of Exceptionally Large Ductility in Molybdenum Alloys Dispersed with Irregular-Shaped La2O3 Nano-Particles

Influence of Al and Mo on microstructure and tribological behaviors of Co-based superalloy

Low‐cycle fatigue behavior of rolled WE43‐T5 magnesium alloy