The role of lithium in hydrogen trapping and embrittlement of Al-Cu-Li alloys: Experimental study and DFT calculations
Heng-shi Li,Si Luo,Hui Xiang,Zhen-zhen Liu,Yong Yao,Jin-feng Li,Hui-jin Tao,Rui-feng Zhang,Dan-yang Liu
DOI: https://doi.org/10.1016/j.jallcom.2024.174289
IF: 6.2
2024-06-01
Journal of Alloys and Compounds
Abstract:The role of lithium in hydrogen embrittlement (HE) and trapping of Al-Cu-Li alloys were investigated in experimental and density functional theory (DFT) calculations. The tensile curves and fracture morphology show that the Li-contained samples are more sensitive to HE than the Li-free samples and the HE sensitivity increases with the aging time expansion. The Transmission Electron Microscope (TEM) analyses reveal that the number density of T1 (Al2CuLi) precipitates increases about 66.8% with aging process, suggesting that HE sensitivity is exacerbated by T1 precipitates. In addition, the lithium in T1 precipitates, solid solution matrix and solute segregation grain boundaries (GBs) always has a high affinity to hydrogen according to DFT calculations, where T1 precipitates have the highest hydrogen trapping energy with 0.736 eV/H atom. Moreover, the influence of hydrogen on Al-Cu-Li alloys was investigated using X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), and electrochemical corrosion analysis. These analyses indicate that hydrogen exists in the form of hydrogen atoms, which results in a reduction in corrosion potential (E corr ) from −676.3 mV to −699.3 mV by approximately 20 mV and an increase in corrosion current density (i corr ) from 2.1×10−6 A/cm2 to 10.8×10−6 A/cm2 by an order of magnitude. The accumulated hydrogen atoms eventually lead to corrosion pits and blisters on the surface of alloys.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering