Study of PVC/CM Thermoplastic Elastomer

LIU Li,LI Rongxun,CHEN Yanlu,YANG Lei,HAN Feng

DOI: https://doi.org/10.3969/j.issn.1009-7937.2011.01.007

2011-01-01

Abstract:Brands and dosage of chlorinated polyethylene rubbers(CM) and dosages of plasticizers on properties of PVC/CM thermoplastic elastomers were studied.Experiments results show that:(1) when the mass ratio of PVC to CM5236 is 100∶10,and the dosage of DOP is 80 parts,PVC/CM thermoplastic elastomer can obtain the best mechanical property with tensile strength 12 MPa and elongation at break 400%-500%,while its hardness maintaining about 65(Shao A);(2) PVC with high polymerization degree can improve the tensile strength,elongation at break and low temperature resistance of PVC/CM thermoplastic elastomer,but excessive high polymerization degree can cause the increase of hardness of PVC/CM thermoplastic elastomer,so the polymerization degree of PVC should be controlled at 1 000-2 000;(3) with the increase of CM dosage,the low temperature resistance of PVC/CM thermoplastic elastomer becomes better;(4) the adding of small amount of powdered butadiene-acrylonitrile rubber(P83) can increase the tensile strength and elongation at break of PVC/CM thermoplastic elastomer,and improve its low temperature resistance.