Abstract:The nature of magnetism in the doubly-diluted spinel ZnTiCoO4= (Zn2+)A[Ti4+Co2+]BO4is reported here employing the temperature and magnetic field (H) dependence of dc susceptibility (χ), ac susceptibilities (χ' andχ″), and heat capacity (Cp) measurements. Whereas antiferromagnetic (AFM) Néel temperatureTN= 13.9 K is determined from the peak in the ∂(χT)/∂TvsTplot, the fit of the relaxation timeτ(determined from the peak in theχ″ vsTdata at different frequencies) to the Power law:τ=τ0[(T-TSG)/TSG]-zνyields the spin glass freezing temperatureTSG= 12.9 K,zν∼ 11.75, andτ0∼ 10-12s. Since the magnitudes ofτ0andzνdepend on the magnitude ofTSG, a procedure is developed to find the optimum value ofTSG= 12.9 K. A similar procedure is used to determine the optimumT0= 10.9 K in the Vogel-Fulcher law:τ=τ0 exp[Ea/kB(T-T0)] yieldingEa/kB= 95 K, andτ0= 1.6 × 10-13s. It is argued that the comparatively large magnitude of the Mydosh parameter Ω = 0.026 andkBT0/Ea= 0.115 (≪1) suggests cluster spin-glass state in ZnTiCoO4below TSG. In theCpvsTdata from 1.9 K to 50 K, only a broad peak near 20 K is observed. This and absence ofλ-type anomaly nearTNorTSGcombined with the reduced value of change in magnetic entropy from 50 K to 1.9 K suggests only short-range AFM ordering in the system, consistent with spin-glass state. The field dependence ofTSGshows slight departure (ϕ∼ 4.0) from the non-mean-field Almeida-Thouless lineTSG(H) =TSG(0) (1 -AH2/ϕ). Strong temperature dependence of magnetic viscositySand coercivityHCwithout exchange bias, both tending to zero on approach toTSGfrom below, further support the spin-glass state which results from magnetic dilution driven by diamagnetic Zn2+and Ti4+ions leading to magnetic frustration. Magnetic phase diagram in theH-Tplane is established using the high-field magnetization dataM(H,T) forT<TNwhich reveals rapid decrease ofTSGwith increase inHwhereas decrease inTNwith increase inHis weaker, typical of AFM systems. ForT>TN, the data ofχvsTare fit to the modified Curie-Weiss law,χ=χ0+C/(T+θ), withχ0= 3.2 × 10-4emu mol-1Oe-1yieldingθ= 4 K andC= 2.70 emu K mol-1Oe-1. This magnitude ofCyields effective magnetic moment = 4.65μBfor Co2+, characteristic of Co2+ions with some contribution from spin-orbit coupling. Molecular field theory with effective spinS= 3/2 of Co2+is used to determine the nearest-neighbor exchange constantJ1/kB= 2.39 K AFM and next-nearest-neighbor exchange constantJ2/kB= -0.66 K (ferromagnetic).

Spin-Glass Behavior in Hexagonal Na0.70mno2

Spin-glass Behavior and Valence States of Transition-Metal Ions of SrMn0.5Fe0.5O3

Re-entrant spin-glass behavior induced by co-doping in hexagonal Y0.3Lu0.7MnO3 single crystal

Enhanced Room Temperature Magnetoresistance and Cluster Spin Glass Behavior in Mo Doping La0.67Sr0.33MnO3

Spin glass state in Co doped NdMnO3

Spin-cluster Glass State in U(Ga 0.95 Mn 0.05 ) 3

Superspin glass behavior and giant exchange bias effect in hexagonal (Mn0.7Cu0.3)66Ga34 ferrimagnet

Spin-glass-like Behavior in Rhombohedral Li(Mn,Cr)O2

Singular Behavior Observed in the Low Temperature Electronic Transport and Thermodynamic Properties of Mn Doped Na0.68coo2

Cluster Spin-Glass State and Kondo Behavior in Sm-based Bulk Metallic Glasses

Spin correlations in Na<sub><i>x</i></sub>CoO<sub>2</sub>with<i>x</i>= 0.8 and 0.5

Spin glass like ground state and observation of exchange bias in Mn_{0.8}Fe_{0.2}NiGe alloy

Eu0.5Sr1.5MnO4: A Three-Dimensional…

Spin-glass Ground State in a Triangular-Lattice Compound YbZnGaO_4

Spin Correlations In Naxcoo2 With X=0.8 And 0.5

Ferrimagnetic hexagonal Mn$_2$CuGe Heusler alloy with a low-temperature spin-glass state

Interplay of lattice-spin-orbital coupling and Jahn-Teller effect in -noncollinear spinel Ti x Mn 1-x (FeyCo 1-y ) 2 O 4 : A neutron diffraction study

Antiferromagnetic short-range order and cluster spin-glass state in diluted spinel ZnTiCoO4

High-field NMR study of the spin correlations in the spin-cluster mineral Na$_2$Cu$_3$O(SO$_4$)$_3$

Immersions of Surfaces into Aspherical 3-Manifolds

Cluster Spin Glass Behavior in Bi(Fe0.95co0.05)O-3