Ti3C2Tx‐UHMWPE Nanocomposites—Towards an Enhanced Wear‐Resistance of Biomedical Implants
Benedict Rothammer,Klara Feile,Siegfried Werner,Rainer Frank,Marcel Bartz,Sandro Wartzack,Dirk W. Schubert,Dietmar Drummer,Rainer Detsch,Bo Wang,Andreas Rosenkranz,Max Marian
DOI: https://doi.org/10.1002/jbm.a.37819
2024-10-26
Journal of Biomedical Materials Research Part A
Abstract:Polymeric biomedical materials, notably UHMWPE in load‐bearing joints, lack optimal mechanical and biotribological properties. This study aims to enhance Ti3C2Tx‐UHMWPE nanocomposites, improving mechanical strength, biocompatibility, and biotribological performance. Tests reveal no adverse effects on hardness, elasticity, or cytotoxicity. Ti3C2Tx reinforcement reduces friction and wear by 19% and 44%, respectively, with a 2 wt.% addition, attributed to a shear transfer film. There is an urgent need to enhance the mechanical and biotribological performance of polymeric materials utilized in biomedical devices such as load‐bearing artificial joints, notably ultrahigh molecular weight polyethylene (UHMWPE). While two‐dimensional (2D) materials like graphene, graphene oxide (GO), reduced GO, or hexagonal boron nitride (h‐BN) have shown promise as reinforcement phases in polymer matrix composites (PMCs), the potential of MXenes, known for their chemical inertness, mechanical robustness, and wear‐resistance, remains largely unexplored in biotribology. This study aims to address this gap by fabricating Ti3C2Tx‐UHMWPE nanocomposites using compression molding. Primary objectives include enhancements in mechanical properties, biocompatibility, and biotribological performance, particularly in terms of friction and wear resistance in cobalt chromium alloy pin‐on‐UHMWPE disk experiments lubricated by artificial synovial fluid. Thereby, no substantial changes in the indentation hardness or the elastic modulus are observed, while the analysis of the resulting wettability and surface tension as well as indirect and direct in vitro evaluation do not point towards cytotoxicity. Most importantly, Ti3C2Tx‐reinforced PMCs substantially reduce friction and wear by up to 19% and 44%, respectively, which was attributed to the formation of an easy‐to‐shear transfer film.
engineering, biomedical,materials science, biomaterials