Modeling of In-Situ Indentation Tests in the Framework of Material Point Method
L. Hu,R. Bhide,W. Nguyen,D. Butt,J. McLennan,G. Gadikota
DOI: https://doi.org/10.56952/arma-2022-0330
2022-01-01
Abstract:ABSTRACT: This work presents numerical simulations of a series of In-situ TEM (Transmission Electron Microscopy) indentation tests using the framework of the Material Point Method (MPM). The selection of MPM is based on its robust capacity for handling large deformation problems which could otherwise be an arduous challenge for mesh-based numerical methods such as the finite element method due to issues with mesh tangling. In this work, the nanoparticles were represented with a collection of material points which carry all the information relevant to the material. The mechanical bonds between particles were simulated with cohesive elements. For simplicity, our current model is a 2D simulation and 3D modeling is pending. Furthermore, up-scaling was necessary to avoid excessively small-time steps. Comparison between the experimental data and the numerical results shows that the numerical modeling with MPM successfully simulates the failure processes manifested by the test specimens including both tensile and shear failure. Our simulation experience also suggests that using an implicit scheme in MPM could be a suitable and beneficial way for extending the application of this powerful numerical technique. 1. INTRODUCTION Nanoindentation is a common and convenient experimental protocol to investigate near-surface mechanical properties, to depths of a few micrometers (Schuh, 2006; Oyen and Cook, 2009; Wheeler, 2015; Ma et al., 2020). The complementary application of in-situ transmission electron microscopy (TEM) enables the observation of deformation and creation of cracks at a micro scale (Minor et al., 2002; Sun et al., 2009; Wang et al., 2017). Unlike the considerable progress and extended applications of indentation tests for revealing the material behavior at nano/micro scale, numerical modeling of this technique in particulate agglomerates - at a micron scale - is relatively rare (Sajjad et al., 2020;). The biggest challenge arises from the large deformation relative to the particle size and the complicated interaction/movement between the particles. Commonly used mesh-based numerical methods such as the finite element method will fail due to mesh tangling if sophisticated and time-consuming mesh treatments are not employed. In this work, we simulated experimental in-situ TEM nanoindentation tests using the framework of the Material Point Method (MPM).