Investigation on Spectroscopic Properties and Fabrication of Yb3+-Doped Silicate Glasses

Xu Bo,Li Peng,Zhou Guiyao,Hou Lantian
DOI: https://doi.org/10.3969/j.issn.1000-0755.2010.07.030
2010-01-01
Abstract:Yb3+-doped silicate glass is prepared by melting method. The differential thermal analysis of host glass 70SiO2-mLi2O-nNa2O-xCaO-yAl2O3 (mol%)(m+n+x+y=30) is conducted. The results show that the glass transition temperature is up to 593.2℃, crystallization temperature 783.4 ℃. The temperature difference is up to 190.2℃, and the glass is drawn into optical fiber. The absorption spectra and fluorescence spectra of the doped glass are measured. The results show that the main absorption peak is at 975 nm with a subpeak at 908 nm, and there is an relatively dispersive absorption peak from 920 nm to 965 nm, its central wavelength being at 942nm, the fluorescence peak being at 1036nm with a subpeak near 993 nm. Also some parameters such as absorption cross-section, integral-absorption cross-section, stimulated emission cross-section, and fluorescence lifetime are calculated using McCumber and Judd-Ofelt theory.
What problem does this paper attempt to address?