Abstract:Magnesium (Mg) alloys containing rare earths (RE) gained special attention as promising candidates for degradable implant applications. Cerium (Ce) is one of the RE elements which can be tolerated by the human physiological system when used as an alloying element in Mg alloys. In this current research work, Mg-Ce binary alloys (0%, 0.5%, 1%, 1.5%, and 2% Ce by weight) were prepared by the stir-casting method. The developed alloys were characterised, and corrosion performance was assessed by immersion experiments in normal saline solution and by electrochemical experiments. The degradation rate of the developed alloys was measured as decreased with the increased Ce content up to 1.5%. From the polarisation studies, lower corrosion current density values 3.5 × 10 −5 A/cm 2 and 4.1 × 10 −5 A/cm 2 were observed for Mg-1.5%Ce and Mg-2%Ce alloys, respectively compared with the other samples. The surface morphologies after removing the corrosion products revealed more degraded regions for Mg and alloys with lower Ce content (0.5% and 1%) compared with 1.5% and 2% Ce. From the results, it is concluded that developing an Mg-Ce alloy with an optimum fraction of Ce (1.5%) is promising to produce degradable Mg-based medical implants with controlled degradation. Récemment, les alliages de magnésium (Mg) contenant des terres rares (TR) ont retenu une attention particulière en tant que candidats prometteurs pour les applications d'implants dégradables. Le cérium (Ce) est l'un des éléments de TR qui peuvent être tolérés par le système physiologique humain lorsqu'il est utilisé comme élément d'alliage dans les alliages de Mg. Dans ces travaux de recherche en cours, on a préparé des alliages binaires Mg-Ce (0%, 0.5%, 1%, 1.5% et 2% Ce en poids) par la méthode de coulée avec agitation. On a caractérisé les alliages développés et l'on a évalué leurs performances à la corrosion par des expériences d'immersion dans une solution saline normale et par des expériences électrochimiques. On a mesuré la vitesse de dégradation des alliages développés comme diminuant avec l'augmentation de la teneur en Ce jusqu'à 1.5%. À partir des études de polarisation, on a observé des valeurs de densité de courant de corrosion plus faibles de 3.5 × 10 −5 A/cm 2 et de 4.1 × 10 −5 A/cm 2 pour les alliages Mg-1.5%Ce et Mg-2%Ce, respectivement, par rapport aux autres échantillons. Les morphologies de surface après l'élimination des produits de corrosion ont révélé des régions plus dégradées pour le Mg et pour les alliages à plus petite teneur en Ce (0.5% et 1%) contre 1.5% et 2% de Ce. À partir de ces résultats, il est conclu que le développement de l'alliage Mg-Ce avec une fraction optimale de Ce (1.5%) promet de produire des implants médicaux dégradables à base de Mg avec une dégradation contrôlée.

The Corrosion Behavior of Ce-implanted Magnesium Alloys

Retardation of Surface Corrosion of Biodegradable Magnesium-Based Materials by Aluminum Ion Implantation

Corrosion resistance and electrical conductivity of V/Ce conversion coating on magnesium alloy AZ31B

Ce-doped MgO films on AZ31 alloy substrate for biomedical applications: preparation, characterization and testing

Investigating the Concurrent Effect of Cerium/Hydroxyapatite Coatings on Mg-Based Implant for Enhancing Corrosion Performance and In-Vitro Activity

Improvement in corrosion resistance and biocompatibility of AZ31 magnesium alloy by NH<sub>2</sub><SUP>+</SUP> ions

Corrosion resistance and biocompatibility of carbon ion implanted AZ31B magnesium alloy

The Effects of ECAP, Mn and Ca Elements on the Microstructure and Corrosion Properties of Magnesium Alloys Were Investigated

EFFECT OF CERIUM AND LANTHANUM ALLOYING ON MICROSTRUCTURE AND CORROSION BEHAVIOR OF AZ91 MAGNESIUM ALLOY

Influence of Biocompatible Metal Ions (ag, Fe, Y) on the Surface Chemistry, Corrosion Behavior and Cytocompatibility of Mg-1ca Alloy Treated with Mevva

Preparation and corrosion resistance studies of nanometric sol–gel-based CeO2 film with a chromium-free pretreatment on AZ91D magnesium alloy

Corrosion behaviour of the magnesium-cerium binary alloy designed for degradable medical implants

Microstructures, Mechanical Properties and Corrosion Resistances of Extruded Mg-Zn-Ca-Xce/La Alloys

A Comparison Study of Ce/La and Ca Microalloying on the Bio-Corrosion Behaviors of Extruded Mg-Zn Alloys

PREPARATION AND CORROSION ELECTROCHEMISTRY BEHAVIOR OF CERIUM-BASED CHEMICAL CONVERSION COATING ON AZ91 MAGNESIUM ALLOY

Development of potentiostatically deposited cerium conversion coating for Mg alloys

Microstructure and corrosion properties of Mg–0.5Zn–0.2Ca–0.2Ce alloy with different processing conditions

Tailoring the microstructure and enhancing the corrosion resistance of extruded dilute Mg-0.6Al-0.5Mn-0.25Ca alloy by adding trace Ce

Effect of Ce Addition on Modifying the Microstructure and Achieving a High Elongation with a Relatively High Strength of As-Extruded AZ80 Magnesium Alloy

Ion Implantation of Calcium and Zinc in Magnesium for Biodegradable Implant Applications

Enhanced Mechanical Properties and Corrosion Resistance of Rolled Mg-1.5Sn-0.5Ca Alloy by Ce Microalloying