Effect of Solute Concentration on Portevin-Le Chatelier Effect in Al-Cu Alloys

Sun Liang,Zhang Qingchuan,Jiang Huifeng

DOI: https://doi.org/10.1007/s11706-007-0031-z

2007-01-01

Frontiers of Materials Science in China

Abstract:The solute concentration and precipitated phase content in alloys were altered by solution treatment (ST) at different temperatures. A series of serrated load curves was obtained in tensile tests at a constant applied strain rate. The influences of solute concentration and precipitated phase content on dislocation movement were analyzed with tensile test results, and the micro-mechanism of the Portevin-Le Chatelier (PLC) effect is discussed in this paper. In the tests, when ST temperature was reduced from 500°C, the amplitude of serrated flow decreased. It reached the minimum when ST temperature was reduced to 300°C. On the other hand, the amplitude of serrated flow increased with ST temperature decreasing from 300 to 100°C. Experimental results show that when ST temperature is higher than 300°C, solute concentration is a governing factor to PLC effect; whereas when ST temperature is lower than 300°C, the precipitated phase content significantly affects the PLC effect.