Abstract:Rotationally symmetric workpieces of Ti2AlNb-based alloys have great potential for high-temperature service condition in aviation industry, while the poor workability limits their application until now. In this study, shear spinning and heat treatment were first conducted to investigate the corresponding microstructure evolution and mechanical properties of Ti2AlNb conical workpieces. The microstructure of the 1st and 2nd pass spun workpieces (SP1 and SP2) mainly consisted of B2 + retained alpha(2) phases. After two passes spinning, the B2 phase texture changed from <111>//ND of as-received alloy to be <001>//ND. The ultimate tensile stress (UTS) of SP1 and SP2 was increased to 1163 MPa and 932 MPa, respectively, compared with 782 MPa of as-received alloy at 650 degrees C. Also, the yield stress anomaly (YSA) occurred in SP1 and SP2 because {110}<111> and {112}<111> cross slip systems of B2 phase were difficult to slip at or below room temperature (RT), but they became active at 650 degrees C and above. As an essential step for increasing the spinnability of multi-pass spinning process of the Ti2AlNb alloy, the H3 heat treatment scheme, i.e. 960 degrees C/2 h+ 850 degrees C/12 h, was carried out between two successive passes to increase the hot workability, by which the ductility of the heat treated as-spun workpieces with the microstructure of B2 + primary O + acicular secondary O + high amount spheroidized alpha(2) phases reached 72.1% at 900 degrees C. After being subject to the H1 heat treatment scheme, i.e. 960 degrees C-2 h, the spun workpieces with the microstructure of B2 + primary O + intergranular primary alpha(2) phases achieved an optimized comprehensive mechanical properties both at room temperature and 650 degrees C, which should be chosen as the post-spinning heat treatment process for the service requirement. (C) 2022 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.

Tube-spinning Microstructure and Preferential Orientation of BT20 Alloy

Texture Evolution Of Bt20 Alloy In Backward Tube Spinning

Quality analysis and control of tubular wordpiece hot spinning of BT20 titanium alloy

Deformation history and the resultant microstructure and texture in backward tube spinning of Ti–6Al–2Zr–1Mo–1V

Microstructure Evolution of Ta15 Titanium Alloy During Hot Power Spinning

Hot Spinning of Cylindrical Workpieces of Ta15 Titanium Alloy

Process Design and Microstructure-Property Evolution During Shear Spinning of Ti2AlNb-based Alloy

Enhancing Hoop Strength of Titanium Alloy Tube by Cross Spinning

Effect of Multi-Pass Power Spinning on Microstructure Homogenization and Mechanical-Property Strengthening of Ti2AlNb-Based Alloy Using Welded Tube Blank

Research on the Characteristics of Hot Deformation in BT20 Titanium Alloy and Its Optimum Spinning Temperature Range

Study on Strong Spinning Preparation Method and Mechanism of the Industrial Pure Titanium Ultrafine Crystallization

Effect of power spinning and heat treatment on microstructure evolution and mechanical properties of duplex low-cost titanium alloy

Microstructure Evolution of TB18 Alloy after Thermal Treatment and the Effect of Recrystallization Texture on Mechanical Properties

Study on the Spinning Process of Cylinder-Conical Composite Curved Generatrix Workpiece of TA15 Titanium Alloy

Study on Microstructure Evolution of Ultrafine Crystallization of TA2 Industrial Pure Titanium

Spinning Process of 2219 Aluminum Alloy Tubes for Used in Hydroforming

Evolution of microstructure and texture of a near α titanium alloy during forging bar into disk

Study on High-Temperature Flow Behavior and Substructure and Texture Evolution of TA15 Titanium Alloy

Microstructure and Texture Characterstics of a Near-Alpha Titanium Alloy Tube

Strain-dependent Heterogeneity of Microstructure and Mechanical Properties of 2195 Al-Li Alloy During Power Spinning and Heat Treatment

Preparation and forming mechanism of ultrathin-walled Ni-Cu alloy tubes with submicrometer structures by ball spinning