Abstract:Nanosilica particles well dispersed in ethanol were modified by 3-(trimethoxysilyl) propyl methacrylate (MPS) and then re-dispersed into methyl methacrylate (MMA) and poly(methyl methacrylate) matrix via a media replacement process and an in situ bulk polymerization process, respectively. The MPS modified status of silica particles and its effects on the dispersion of silica particles in different media and polymer matrix were systematically investigated by FTIR, TG, DLS and TEM. It was found MPS oligomer was the main form for MPS coupling on silica particles surface. Excessive MPS dosage not only resulted in the formation of MPS homo-polymeric particles in media phase, but also the MPS oligomer thick layer on silica surface, which would inevitably induce the small-scale aggregation of silica particles. There existed an appropriate MPS coupling amount for excellent silica dispersity, which is mainly related with the apparent coupling density of MPS molecules on silica particles surface. When the apparent coupling density is 1. 3 similar to 5. 6 mu mol . (m(2) . SiO2)(-1), the MPS coupling efficiency is acceptable and the modification of silica particles is sufficient. Only on this state, silica particles can be dispersed in the monomer and polymer matrix at the primary particles size level, even in the case of 20% silica content. The silica/monomer dispersion prepared via the above processes exhibited high silica dispersity, high silica content, high storage stability and high grafting controllability on silica surface. All of them imply that this kind of dispersion is avail to prepare silica/PMMA composite microspheres via in situ heterogeneous polymerization, and these microspheres would possess controllable morphology and controllable graft interface.

Preparation And Characterization Of Uv-Curable Mps-Modified Silica Nanocomposite Coats

The Effect of Silane Coupling Agent Containing Methacryloxy Group on UV-Curable Acrylate-Modified Polyurethane/SiO2 Hybrid Coatings

Preparation and characterization of ultraviolet-curable nanocomposite coatings initiated by benzophenone/n-methyl diethanolamine

Effects of preparation method on microstructure and properties of UV-curable nanocomposite coatings containing silica

Synthesis of UV-Cured Silicone Resin/Silica Nanocomposites from UV-Curable Polysilisiquioxane and Methacrylate-Functionalized Silica

Preparation of acrylate polymer/silica nanocomposite particles with high silica encapsulation efficiency via miniemulsion polymerization

The Preparation and Characterization of Aqueous Nanosilica/Polyester Composite Resin and Coatings

Preparation and characterization of nanocomposite polyurethane.

Preparation and characterization of acrylic latex/nano-SiO2 composites

Preparation of Crosslinked Composite Nanoparticles

Preparation and Characterization of Scratch and Mar Resistant Waterborne Epoxy/Silica Nanocomposite Clearcoat

Preparation and Characterization of Silica/Pmma Composites with Highly Dispersed Silica Nanoparticles Dispersion of Nanosilica in Mma

Dispersion of γ-methacryloxypropyltrimethoxysilane-functionalized zirconia nanoparticles in UV-curable formulations and properties of their cured coatings

Preparation and Characterization of Polyester/Silica Nanocomposite Resins

Hydroxyl terminated silicone oil as co-stabilizer for miniemulsion copolymerization of acrylate and methacryloxy(propyl)-trimethoxysilane

Research of the Synthesis and Film Performance of Silica/poly(st-Ba-mps) Core-Shell Latexes Obtained by Miniemulsion Co-Polymerization

The Properties of High Solid Acrylic Based Polyurethane and Acrylic Latex Embedded with Nano-Silica

Mini-Emulsification and Mini-Emulsion Polymerization of Methyl Methacrylate/Nanosilica Dipsersion

Preparation of Solvent-borne Acrylic-based Polyurethane-Modified Silica Nanocomposites

Synthesis and characterization of UV and thermal curable polybenzoxazine/silica nanocomposites

Preparation of UV-curable Nano-composite Coating by the Sol-Gel Process