Effect of lanthanum ions on magnetic properties of Y 3 Fe 5 O 12 nanoparticles

Zhongjun Cheng,Yuming Cui,Hua Yang,Yan Chen
DOI: https://doi.org/10.1007/s11051-008-9501-1
IF: 2.533
2008-01-01
Journal of Nanoparticle Research
Abstract:Lanthanum ion (La 3+ )-substituted garnet nanoparticles Y 3− x La x Fe 5 O 12 ( x = 0.0, 0.2, 0.4, 0.6, 0.8, and 1.0) were fabricated by a sol–gel method. Their crystalline structures and magnetic properties were investigated by using X-ray diffraction (XRD), vibrating sample magnetometer (VSM), and Mössbauer spectrum. The XRD results show that samples of Y 3− x La x Fe 5 O 12 (0.0 ≤ x ≤ 0.8) are all single phase and the sizes of particles range from 32 to 65 nm. Those of Y 2 LaFe 5 O 12 consisted of peaks from garnet and LaFeO 3 structures. Compared to pure YIG, the saturation magnetization is larger when the La concentration x = 0.2. However, with increasing La concentration ( x ), it decreases obviously. Meanwhile, may be due to the enhancement of the surface spin effects, the saturation magnetization rises as the particle size is increased. Different from the pure YIG, the Mössbauer spectra of Y 2.8 La 0.2 Fe 5 O 12 and Y 2.2 La 0.8 Fe 5 O 12 are composed of four sets of six-line hyperfine patterns. The results tell us that the substitution of La 3+ ions with large ionic radius (1.061 Å) will give rise to a microscopic structure distortion of the a- and d-sites to different degrees, and the Zeeman sextets from a- and d-sites begin to split into two sub-sextets, which is helpful to explain the phenomenon observed in the study of the magnetic property.
What problem does this paper attempt to address?