Abstract:Titania-based nanocomposites have recently attracted much attention due to their unique structure and properties. Titania has been known to have three crystal phases: brookite, anatase and rutile. The anatase titania has the highest photoactivity than the other two phases. Meanwhile Ohtani et al. [1] reported that amorphous titania has a negligible photoactivity compared to the crystalline titania. Much work has been conducted on the optimization of catalytic properties of titania used in the photodegradation of organic pollutants in water by either using modified titania or thin titania films. Many researches indicated that dopants, such as many oxides, can effectively suppress the transformation of anatase into rutile by improving the onset transformation temperature [2]. Silica-titania mixed oxide is considered a potential candidate because it is used as not only a good photocatalyst itself but also a support material for other chemical reaction catalysts [3, 4]. 30SiO2/TiO2 powders (30 denotes the weight percent of silica) were prepared by sol-gel process. Ti(OBu n )4 and TEOS were used as precursors of titania and silica respectively. After TEOS was stirred in a mixture solution of pure ethanol, distilled water and hydrochloric acid for 1 h, Ti(OBu n )4 was added slowly into the mixture. The sol of SiO2/TiO2 was obtained after another two hours’ vigorous stirring and cooled to room temperature. The gel was calcined at different temperatures and then ground into fine powders. The distilled water solution of methyl orange (with a concentration of 25 mg/L) was chosen for photodegradation. 0.2 g powders were added into 40 ml of the above solution with vigorous agitation under the mercury light. A 756MC UV-VIS spectrometer was used to record the change of concentration of the methyl orange. FT-IR spectra was obtained by a Bruker EQUINOX55 spectrometer. TEM and HREM observations were carried out using a Jeol-2010 electron microscope. The XRD patterns were made in a D/max3A diffractometer with Cu Kα radiation. The crystallite size of powders was determined by Scherrer equation. Electron spin resonance measurements were made with a Bruker paramagnetic spectrometer. X-ray photoelectron spectroscopy (XPS) spectra of the sample were obtained with an NP-1 using the Mg Kα excitation source and the binding energies referenced to the C1s hydrocarbon line at 284.6 eV. The atomic ratios were obtained by intergrating the areas under the peak. Photodegradation for methyl orange with 30SiO2/ TiO2 samples calcinated at different temperature under UV irradiation is illustrated in Fig. 1. The results of other samples heated at temperatures higher than 850 ◦ C were not shown in this figure because further increase of the calcination temperature decreased the decomposition rate. It can be seen that decomposition rate of the samples fired at 400 ◦ C and 500 ◦ Ci s low. When the calcination temperature was further increased to 600 ◦ C, the higher photoactivity than Degussa P25’s was obtained. The sample heated at 800 ◦ C has the best photoactivity about 2 times higher than the Degussa P25.

Sol–gel immobilization of SiO 2 /TiO 2 on hydrophobic clay and its removal of methyl orange from water

A high-stability silica-clay composite: synthesis, characterization and combination with TiO2 as a novel photocatalyst for Azo dye.

Enhanced photoactivity of silica-titania binary oxides prepared by sol-gel method

Fabrication of hydroxyl group modified monodispersed hybrid silica particles and the h-SiO2/TiO2 core/shell microspheres as high performance photocatalyst for dye degradation

Facile Fabrication of Mesoporous SiO2@(cTiO2/BiOI) Heterojunctions with Enhanced Photocatalytic Properties Due to Large Surface Area for Contact with Pollutants

Composites of TiO2 pillared sericite: Synthesis, characterization and photocatalytic degradation of methyl orange

Preparation of silicon-doped TiO2 fiber and supported TiO2 and comparison study of their photocatalytic activity

Template-free synthesis of polymer-derived mesoporous SiOC/TiO 2 and SiOC/N-doped TiO 2 ceramic composites for application in the removal of organic dyes from contaminated water

Facile Fabrication of Mesoporous SiO2@(cTiO2/BiOI) 2 @(ctio 2 /bioi) Heterojunctions with Enhanced Photocatalytic Properties Due to Large Surface Area for Contact with Pollutants

Novel kaolin/polysiloxane based organic-inorganic hybrid materials: Sol-gel synthesis, characterization and photocatalytic properties

A Novel Vermiculite/TiO2 Composite: Synergistic Mechanism of Enhanced Photocatalysis towards Organic Pollutant Removal

Immobilized chitosan-montmorillonite composite adsorbent and its photocatalytic regeneration for the removal of methyl orange

Hollow TiO2–SiO2 Nanospheres for Photocatalytic Degradation of Organic Dyes

Development and Upscaling of SiO2@TiO2 Core-Shell Nanoparticles for Methylene Blue Removal

Synergistic Promotion of Photocatalytic Degradation of Methyl Orange by Fluorine- and Silicon-Doped TiO2/AC Composite Material

Hydrolytic Modification of SiO2 Microspheres with Na2SiO3 and the Performance of Supported Nano-TiO2 Composite Photocatalyst

Development of a TiO2/Sepiolite Photocatalyst for the Degradation of a Persistent Organic Pollutant in Aqueous Solution

Facile Synthesis of SiO 2 @tio 2 Hybrid NPs with Improved Photocatalytic Performance

Hydrothermal Synthesis and Morphological Evolution of Mesoporous Titania−Silica

Layered Double Hydroxide-Bismuth Molybdate Hybrids toward Water Remediation via Selective Adsorption of Anionic Species

Analysis of the Surface Adsorbed Organics of Nanosized TiO2 Photocatalyst with High Visible-Light Photocatalysis Activity by Ultrasonic Treatment under Water and Ethanol Solution