Abstract:Rutile TiO2 nanorods with lengths greater than 600 nm and aspect ratios greater than ca. 16 were synthesized through a one-pot hydrothermal method using lactic acid (LA) as a structure-directing agent. Under the hydrothermal treatment at 200 °C, the LA concentration higher than 1.6 mol dm-3 and the hydrothermal time of 72 h were needed to obtain 100% rutile nanorods. The length and the width of the nanorods increased with the increasing LA concentration. The photocatalytic activity of the synthesized nanorods was evaluated for the oxygen evolution in aqueous AgNO3 solutions under ultraviolet irradiation. Calcination of the synthesized nanorods at 400 °C was required to decompose residual organic compounds on the surface and improve the oxygen evolution. The highest oxygen evolution rate was obtained with the nanorods after being calcined at 800 °C. It is worth noting that the nanorods retained their shape (aspect ratio of 8.8) at 800 °C. Selected area electron diffraction patterns indicated that the side or the end surface of the nanorods was attributable to the {110} or {111} facet, respectively. Deposition of Pt or PbO2 on the nanorods revealed that the {110} or {111} facet acted as reductive or oxidative sites. For comparison, near-spherical TiO2 nanoparticles were synthesized by a sol-gel method. Furthermore, using glycolic acid as the structure-directing agent, we synthesized small rutile TiO2 nanorods (aspect ratio of 9) and changed the shape to near-spherical (aspect ratio of 1.3) by calcining at 800 °C. Time-resolved diffuse reflectance spectra were measured to determine the lifetime of the photogenerated electrons. The photocatalytic activity of the nanorods was much lower than that of the near-spherical TiO2 nanoparticles. However, the nanorods synthesized with LA are useful as catalyst support or platforms for various applications because of their unique morphology and high heat resistance.

Self-assembly of Rutile (Α-Tio2) Nanoclusters into Nanorods in Microemulsions at Low Temperature and Their Photocatalytic Performance

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

Effects of Hydrothermal Time on the Morphologies of Rutile TiO2 Hierarchical Nanoarrays and Their Optical and Photocatalytic Properties

Preparation and Photocatalytic Activities of TiO2 Nanotubes with Mixed Crystal Structure

Hollow TiO 2 microspheres assembled with rutile mesocrystals: Low-temperature one-pot synthesis and the photocatalytic performance

Low Temperature Synthesis and Photocatalytic Activity of Rutile TiO2 Nanorod Superstructures

Solvothermal Growth of Three-Dimensional TiO2 Nanostructures and Their Optical and Photocatalytic Properties

Synthesis, Characterization and Photocatalytic Activity of Hierarchical Spherical TiO2 Nanostructures

Photoelectrocatalytic Efficiency of Low-Temperature Precipitated Monolayer Rutile TiO 2 Nanoflower Film

EG-solvothermal Synthesis of Self-Assembly SrTiO3 Nano Sheets and Photocatalytic Property

Nonaqueous sol–gel synthesis and growth mechanism of single crystalline TiO2 nanorods with high photocatalytic activity

Low Temperature Synthesis of Few-Layer Titanate Nanobelts on Ti Mesh and the Hot-Water Induced Transformations to Highly Photocatalytic Active Titania Nanorods

Preparation of Controllable Crystalline Titania and Study on the Photocatalytic Properties.

Large-scale Synthesis and Characterization of Fan-Shaped Rutile TiO2 Nanostructures

Low‐Temperature Growth of Rutile Nanorod Thin Films and Their Photon‐Induced Property

A facile synthesis of hierarchical TiO2 for dye adsorption and photocatalysis

Ordered Mesoporous Thin Films Of Rutile Tio2 Nanocrystals Mixed With Amorphous Ta2o5

A Simple Solvothermal Process to Synthesize CaTiO3 Microspheres and Its Photocatalytic Properties

Self-Assembly Tio2 Hierarchical Hollow Microspheres with Rutile Nanorods by Template-Free Hydrothermal Method

One-Pot Synthesis of Long Rutile TiO2 Nanorods and Their Photocatalytic Activity for O2 Evolution: Comparison with Near-Spherical Nanoparticles

A Facile Approach for Fabrication of TiO2 Hierarchical Nanostructures and Their Photocatalytic Properties