Abstract:The carbonation behavior of calcium-containing sorbents, CaO and Ca(OH)2, was investigated under pressurized CO2 at nominal room temperature. The carbonation reaction was mechanically driven via reactive ball milling. The carbonation rate was determined by monitoring the CO2 pressure inside the sealed milling jar. Two different versions of CaO were fabricated as starting materials. The addition of citric acid in CaO synthesis resulted in a significant increase in sorbent surface area, bringing up the conversion of CO2 from 18% to 41% after 3 h of reactive milling. The hydroxide formation from these two oxides closed the surface area gap. Nevertheless, we found that hydroxides had a higher initial carbonation rate and greater final CO2 uptake than their oxide counterparts. However, the formation of byproduct water limited the further carbonation of Ca(OH)2. When we added a controlled amount of water to the CaO-containing milling jar, the highest carbonation rate and most extensive CO2 uptake were attained due to the in situ formation of reactive Ca(OH)2 nanoparticles. We saw CaCO3 X-ray diffraction peaks only when Ca(OH)2 was involved in this low-temperature carbonation, indicating that the grain growth of CaCO3 is easier on the Ca(OH)2 surface than on the CaO surface. We used the Friedman isoconversional method to calculate the effective activation energy of decarbonation for the high surface area CaO sorbent milled with water. The average effective activation energy was found to be about 72 kJ mol−1, and its magnitude started to decrease significantly from 50% sorbent regeneration. The drastic change of the effective activation energy during decarbonation suggests that CaCO3, formed at nominal room temperature by reactive milling under pressurized CO2, should undergo a more drastic morphology change than the typical thermally carbonated CaCO3.

Effects of CO2 flow rate on morphology and adsorption capacity of CaCO3

Modulation of nano CaCO3pore size and effect on properties of carbonation reaction

Modified Kinetics Model of Nano CaO Reactions with CO2 in a CaO-Based Adsorbent

Preparation of Nano-CaCO3 from Phosphogypsum by Gas–Liquid–Solid Reaction for CO2 Sorption

Study on the kinetics of Ca-based CO2 sorbent of carbonation and calcination for adsorption enhanced reforming process

Performance of Nano-Caco3 Coated with SiO2 on CO2 Adsorption at High Temperature

Preparation of cage-like nano-CaCO3 hollow spheres for enhanced CO2 sorption

Adsorption Properties of Coating Modified Nano CaO-Based CO2 Adsorbents

Particle Carbonation Kinetics Models and Activation Methods under Mild Environment: the Case of Calcium Silicate

The Effect of CaO Content on Sorption Performance of Nano CaO Based CO2 Adsorbent

Effects of Temperature on Morphology and Adsorption Capacity of CaCO_3

Calcium-Based Sorbent Carbonation at Low Temperature via Reactive Milling under CO2

Effect of Temperature on the Carbonation Reaction of Cao with Co2

The effects of impurities in carbide slag on the morphological evolution of CaCO3 during carbonation

Morphological Changes of Pure Micro‐ and Nano‐Sized CaCO3 during a Calcium Looping Cycle for CO2 Capture

Slag Blended Cement Paste Carbonation under Different CO2 Concentrations: Controls on Mineralogy and Morphology of Products

Effects of temperature and CO2 concentration on the early stage nucleation of calcium carbonate by reactive molecular dynamics simulations

Modeling of the Carbonation Kinetics of A Synthetic Cao-Based Sorbent

XRD and 29Si MAS NMR study on carbonated cement paste under accelerated carbonation using different concentration of CO2

Carbonation Kinetics of CO2 with CaO-Ca9Al6O18 Sorbent

The Precipitation of Calcium Carbonate Via a Bubbling Method in the Presence of Mg2+and Glucose