Long Ag-Clad Bi-Based Superconducting Tapes And Coils

H.K. Liu,J. Yau,Y.C. Guo,Q.Y. Hu,J.X. Jin,N. Savvides,S.X. Dou

DOI: https://doi.org/10.1016/0921-4526(94)91606-3

1994-01-01

Abstract:Ag-sheathed Bi-based superconducting single and multifilament tapes have been fabricated using a powder-in-tube technique. A J(c) of 6,000 A/cm2 at 77 K over 12 meters of a single core tape is compared with 18,500 A/cm2 for the tape processed by pressing. A J(c) of 11,000 A/cm2 at 77 K and 137,000 A/cm2 at 4.2 K over 8 meters of a 49 multifilament tape has been achieved. Multiprobe measurements for a tape show that there is no indication of accumulative grain boundary resistance over the entire length at high temperatures. The J(c) remained unchanged when the tapes were rewound into a pancake coil and a solenoid with an internal diameter of 5 cm for single core tapes and of 1.4 cm for a 49 multifilament tape. Multifilament tapes exhibit robust mechanical properties and feasible for practical applications.