Hydroxyapatite synthesized by a simplified hydrothermal method

H.S. Liu,T.S. Chin,L.S. Lai,S.Y. Chiu,K.H. Chung,C.S. Chang,M.T. Lui

DOI: https://doi.org/10.1016/0272-8842(95)00135-2

IF: 5.532

1997-01-01

Ceramics International

Abstract:A simplified hydrothermal method of synthesizing hydroxyapatite powder is described. Heating powders of Ca(OH)(2), Ca(H2PO4)(2) . H2O and distilled water in a pressurized pot at 109 degrees C for 1-3 h results in powders consisting of crystallized hydroxyapatite in a needle shape, 130-170 nm in length and 15-25 nm in width. The specific surface area is 31-43 m(2)/g and the Ca/P ratio is 1.640-1.643. The obtained HA powder can be sintered to a high density at 1200-1300 degrees C. No decomposition was identified by X-ray diffraction. The optimally sintered ceramic has a pore-free surface structure with a flexural strength of 120 MPa, a micro-Vickers hardness of 5.1 GPa and fracture toughness of 1.2 MPa . m(1/2). The biocompatibility of the pulverized sintered-ceramic is excellent and comparable to that of a commercial grade hydroxyapatite by evaluating the implantation in a dog. The synthesis method is simple, economic, and results in a high quality powder which is useful in hard tissue reconstruction applications. (C) 1996 Elsevier Science Limited and Techna S.r.l.