Abstract:A newly developed method for the formation of nanowires by self-aggregation of nanoparticles is presented in this paper. Co3C, Co-rich, and Ni nanoparticles dispersed on holey carbon grids are inserted in a vacuum oven and are co-annealed with PolyChloroTriFluoroEthylene (PCTFE) at 375 degrees C. No external electric or magnetic fields were applied. High resolution electron microscopy (HREM) was extensively used to determine the shape, size distribution and crystallographic phase of the starting and produced materials. Interestingly, after an annealing circle of 72 hours, the nanoparticles seem to self-agglomerate into nanowires which have diameters in the 5-20 nm range and lengths exceeding at cases 1 micron. The diameter of the produced wires is in the same range as the diameter of the initial nanoparticles, further supporting the notion that the nanowires have formed out of nanoparticle agglomeration. Close inspection of nanowire HREM images shows that the core structure of nanowires wider than approximately 11 nm resembles linked nanoparticles. Phase identification performed using the HREM images reveals the core is of the same phase/material as the starting nanoparticles. Since nanowires appear to form over holes on the holey carbon grid, a base growth mechanism is proposed. The fluorocarbon vapour decomposes over the transitional metal nanoparticles and carbon tubules start growing. The nanoparticles appear to be trapped inside the tubules where their close proximity enhances their fusion into a continuous core. At the studied temperature, the nanoparticle fusion is seen to be limited by the size of the nanoparticles manifested by continuous cores only in the thin nanowires. The process presented here shows that nanoparticles can spontaneously self-align into nanowires in a way and to an extent never reported before. Therefore there is certainly scope for studying this method further to reveal more information about the catalytic action of transitional metals on hydrocarbons and the exact nanowire formation mechanism. Although it is currently a matter of speculation, this process might lead to the effortless growth of nanowires at particular places when building miniature circuits.

Growth of Single-Crystal Magnetite Nanowires from Fe3o4 Nanoparticles in A Surfactant-Free Hydrothermal Process

Ultrafast growth of single-crystalline Si nanowires

Synthesis and Magnetic Properties of Single-Crystalline Magnetite Nanowires

Hydrothermal growth and characterization of magnetite (Fe3O4) thin films

Morphology-controlled Synthesis and Characterization of MnWO4 Nanocrystals Via a Facile, Additive-Free Hydrothermal Process

Growth and process conditions of aligned and patternable films of iron(III) oxide nanowires by thermal oxidation of iron.

Hydrothermal Synthesis and Characterization of Uniform Α-Feooh Nanowires in High Yield

Hydrothermal-induced Oriented Growth of Fe–Co Alloy and Sm3+-substituted Magnetite Nanowire Composites

Spontaneous self-agglomeration of magnetic nanoparticles into nanowires

One-step wet chemistry for preparation of magnetite nanorods

Hydrothermal Preparation and Characterization of MnWO4Nanowires

Applied Stress-Assisted Growth of Single Crystal Γ-Fe2o3 Nanowires

Shape-Controlled Synthesis of Mnwo4 Nanocrystals by A Surfactant-Free Hydrothermal Method

Selective Synthesis of Fe 2 O 3 and Fe 3 O 4 Nanowires Via a Single Precursor: A General Method for Metal Oxide Nanowires

Simplified Synthesis of Single-Crystalline Magnetic CoFe2O4 Nanorods by a Surfactant-Assisted Hydrothermal Process

Hydrothermal synthesis of nanowires ZnS with surfactant

Growth and Properties of Single-Crystalline Γ-Fe2o3 Nanowires

Large Scale Growth and Magnetic Properties of Fe and Fe3o4 Nanowires

Synthesis of Single-Crystalline Fe Nanowires Using Catalyst-Assisted Chemical Vapor Deposition

Surfactant-assisted synthesis of alpha-Fe2O3 nanotubes and nanorods with shape-dependent magnetic properties.

Preparation of inorganic salts (CaCO3, BaCO3, CaSO4) nanowires in the Triton X-100/cyclohexane/water reverse micelles