Crystal Structure, Thermal Expansion and Electrical Conductivity of Perovskite Oxides BaxSr1−xCo0.8Fe0.2O3−δ (0.3≤X≤0.7)

Bo Wei,Zhe Lu,Xiqiang Huang,Jipeng Miao,Xueqing Sha,Xianshuang Xin,Wenhui Su

DOI: https://doi.org/10.1016/j.jeurceramsoc.2005.06.047

IF: 5.7

2005-01-01

Journal of the European Ceramic Society

Abstract:BaxSr1−xCo0.8Fe0.2O3−δ (0.3≤x≤0.7) composite oxides were prepared and characterized. The crystal structure, thermal expansion and electrical conductivity were studied by X-ray diffraction, dilatometer and four-point DC, respectively. For x≤0.6 compositions, cubic perovskite structure was obtained and the lattice constant increased with increasing Ba content. Large amount of lattice oxygen was lost below 550°C, which had significant effects on thermal and electrical properties. All the dilatometric curves had an inflection at about 350–500°C, and thermal expansion coefficients were very high between 50 and 1000°C with the value larger than 20×10−6°C−1. The conductivity were larger than 30Scm−1 above 500°C except for x>0.5 compositions. Furthermore, conductivity relaxation behaviors were also investigated at temperature 400–550°C. Generally, Ba0.4Sr0.6Co0.8Fe0‘2O3−δ and Ba0.5Sr0.5Co0.8Fe0.2O3−δ are potential cathode materials.