Abstract:Starch-g-poly(sodium allyl sulfonate-co-ethyl acrylate) (S-g-P(SAS-co-EA)) containing amphiphilic P(SAS-co-EA) branches, were synthesized via the graft polymerization of acid-converted starch (ACS) with sodium allyl sulfonate (SAS) and ethyl acrylate (EA) monomers in an aqueous phase, for providing a new biological starch sizing agent for warp sizing. The adhesion to cotton and polyester fibers was determined by testing the bonding forces of sized roving according to the method of FZ/T 15001-2008. The film properties were measured in terms of breaking elongation, tensile strength, and bending endurance. In the grafting ratio range of 2.82–10.62%, S-g-P(SAS-co-EA) samples with a range of 4.76–10.62% were significantly superior to ACS (grafting ratio = 0) in the bonding forces to cotton fibers, and film elongation and endurance (p < 0.05). As the ratios increased from 7.91% to 10.62%, the S-g-P(SAS-co-EA) samples were obviously higher than ACS in the forces to polyester fibers (p < 0.05). These results concluded that incorporating amphiphilic P(SAS-co-EA) branches could significantly promote the adhesion of starch to both fibers and reduce its film brittleness to provide higher extensibility and flexibility. With the rises in the grafting ratios from 2.82% to 10.62%, bonding forces as well as film elongation and endurance were gradually increased, whereas the tensile strength of S-g-P(SAS-co-EA) film was consistently reduced. Based on the results, the S-g-P(SAS-co-EA) possessed superior adhesion and film properties and could be used as a potential sizing agent for sizing cotton and polyester warps.

Grafting Modification of Sesbania Gum and Its Application to Textile Sizing

Modification and Sizing Effect of Sesbania Gum

Preparation and Sizing Effect of Modified Sesbania Gum Grafting Polyacrylic Acid Sizing Material

Modified Methods of Sesbania Gum Ploymer Chemical Structure

Effects of graft modification on the properties of chitosan for warp sizing

Effect of particle size of sesbania gum on its modification, structure and performances

Effects of Graft Modification on the Water Solubility, Apparent Viscosity, and Adhesion of Feather Keratin for Warp Sizing

Characterization of Dialdehyde Carboxymethyl Cross-Linked Sesbania Gum and its Application in Solid Electrolyte Membranes

Preparation and Anti‐leakage Properties of Sesbania Gum‐grafted Copolymers

Synthesis and Characterization of Hydroxypropyl Sesbania Galactamannan Seed Gum for Pharmaceutical Application

Modification of Acrylic Fabric by Grafting Silkworm Chrysalis Protein on It

Technological Evaluation of Methacrylic Acid/Fenugreek Gum Grafted Products as Thickener in Textile Printing

Oxidation of Sesbania Gum Using an Octenyl Succinate-Esterified Composite

Study on Modification of Acrylic Fabrics Grafted Sericin Protein with SFEGE

Effect of Surface Grafting-Modified on Structure and Property of Cellulose Fibers

The Effects of Extrusion Processing on Rheological and Physicochemical Properties of Sesbania Gum

Introducing the grafted poly(acrylic acid- co -butyl acrylate) branches onto biological corn starch macromolecule for imparting it with superior sizing properties

Incorporation of poly(sodium allyl sulfonate) branches on corn starch chains for enhancing its sizing properties: Viscosity stability, adhesion, film properties and desizability

Adhesion to cotton and polyester fibers and film properties of starch-g-poly(sodium allyl sulfonate-co-ethyl acrylate) for warp sizing

Cellulose Fibers Modified By Pva-Based Polymers Via Grafting And Adsorption

Preparation of Graft Copolymer Onto Starch and Its Performance in Surface Sizing